Study of Annealed Indium Tin Oxide-Films prepared by RF Reactive Magnetron Sputtering

Tin doped indium oxide (ITO) films were deposited on glass substrates by rf reactive magnetron sputtering using a metallic alloy target (In-Sn, 90-10). The post-deposition annealing has been done for ITO films in air and the effect of annealing temperature on the electrical, optical and structural properties of ITO films was studied. It has been found that the increase of the annealing temperature will improve the film electrical properties. The resistivity of as deposited film is about 1.3 x 10(-1) Omega*cm and decreases down to 6.9 x 10(-3) Omega*cm as the annealing temperature is increased up to 500 degrees C. In addition, the annealing will also increase the film surface roughness which can improve the efficiency of amorphous silicon solar cells by increasing the amount of light trapping.

Revestimentos descontínuos de coberturas: análise da normalização europeia aplicável

Esta dissertação tem como principais objectivos analisar a conformidade das características de revestimentos descontínuos de coberturas produzidos ou comercializados em Portugal com as exigências preconizadas nas normas europeias aplicáveis. Contudo, e tendo em conta a diversidade do tema, o presente estudo centralizou-se em três tipos de revestimentos descontínuos: fibrocimento, metais e plásticos. Optou-se por uma abordagem teórica complementada por uma campanha experimental. No caso da primeira, serão descritas as características de uma cobertura inclinada e alguns dos principais tipos de revestimentos descontínuos existentes. No que concerne à campanha experimental, para além da pesquisa efectuada ao nível do mercado nacional e dos contactos desenvolvidos para a recolha de amostras, realizaram-se ensaios de natureza geométrica de todas as amostras recolhidas. Em suma, a presente dissertação foi validada através de uma campanha experimental simples, que consistiu na análise do cumprimento das exigências das normas europeias aplicáveis aos produtos ensaiados, resultando numa avaliação crítica aos valores obtidos.

ITO/SiOx/Si optical sensor with internal gain

A visible/near-infrared optical sensor based on an ITO/SiOx/n-Si structure with internal gain is presented. This surface-barrier structure was fabricated by a low-temperature processing technique. The interface properties and carder transport were investigated from dark current-voltage and capacitance-voltage characteristics. Examination of the multiplication properties was performed under different light excitation and reverse bias conditions. The spectral and pulse response characteristics are analysed. The current amplification mechanism is interpreted by the control of electron current by the space charge of photogenerated holes near the SiOx/Si interface. The optical sensor output characteristics and some possible device applications are presented.

Structural, electrical and magnetic studies of Co:SnO2 and (Co,Mo):SnO2 films prepared by pulsed laser deposition

Here we report on the structural, optical, electrical and magnetic properties of Co-doped and (Co,Mo)-codoped SnO2 thin films deposited on r-cut sapphire substrates by pulsed laser deposition. Substrate temperature during deposition was kept at 500 degrees C. X-ray diffraction analysis showed that the undoped and doped films are crystalline with predominant orientation along the [1 0 1] direction regardless of the doping concentration and doping element. Optical studies revealed that the presence of Mo reverts the blue shift trend observed for the Co-doped films. For the Co and Mo doping concentrations studied, the incorporation of Mo did not contribute to increase the conductivity of the films or to enhance the ferromagnetic order of the Co-doped films. (C) 2012 Elsevier B.V. All rights reserved.