Ash deposition during the co-firing of bituminous coal with pine sawdust and olive stones in a laboratory furnace

This article describes an experimental study on ash deposition during the co-firing of bituminous coal with pine sawdust and olive stones in a laboratory furnace. The main objective of this study was to relate the ash deposit rates with the type of biomass burned and its thermal percentage in the blend. The thermal percentage of biomass in the blend was varied between 10% and 50% for both sawdust and olive stones. For comparison purposes, tests have also been performed using only coal or only biomass. During the tests, deposits were collected with the aid of an air-cooled deposition probe placed far from the flame region, where the mean gas temperature was around 640 degrees C. A number of deposit samples were subsequently analyzed on a scanning electron microscope equipped with an energy dispersive X-ray detector. Results indicate that blending sawdust with coal decreases the deposition rate as compared with the firing of unblended coal due to both the sawdust low ash content and its low alkalis content. The co-firing of coal and sawdust yields deposits with high levels of silicon and aluminium which indicates the presence of ashes with high fusion temperature and, thus, with less capacity to adhere to the surfaces. In contrast, in the co-firing of coal with olive stones the deposition rate increases as compared with the firing of unblended coal and the deposits produced present high levels of potassium, which tend to increase their stickiness.

An SEM investigation of the pozzolanic activity of a waste catalyst oil refinery

The most active phase of the fluid catalytic cracking (FCC) catalyst, used in oil refinery, is zeolite-Y which is an aluminosilicate with a high internal and external surface area responsible for its high reactivity. Waste FCC catalyst is potentially able to be reused in cement-based materials - as an additive - undergoing a pozzolanic reaction with calcium hydroxide (Ca(OH)2) formed during cement hydration [1-3]. This reaction produces additional strength-providing reaction products i.e., calcium silicate hydrate (C-S-H) and hydrous calcium aluminates (C-A-H) which exact chemical formula and structure are still unknown. Partial replacement of cement by waste FCC catalyst has two key advantages: (1) lowering of cement production with the associated pollution reduction as this industry represents one of the largest sources of man-made CO2 emissions, and (2) improving the mechanical properties and durability of cement-based materials. Despite these advantages, there is a lack of fundamental knowledge on pozzolanic reaction mechanisms as well as spatial distribution of porosity and solid phases interactions at the microstructural level and consequently their relationship with macroscopical engineering properties of catalyst/cement blends. Within this scope, backscattered electron (BSE) images acquired in a scanning electron microscope (SEM) equipped with Energy-Dispersive Spectroscopy (EDS) and by X-ray diffraction were used to investigate chemical composition of hydration products and to analyse spatial information of the microstructure of waste FCC catalyst blended cement mortars. For this purpose mortars with different levels of cement substitution by waste catalyst as well as with different hydration ages, were prepared. The waste FCC catalyst used is produced by the Portuguese refinery company Petrogal S.A.

Pozzolanic activity of oil-refining catalyst: evaluation by electron and atomic microscopy

The reuse of waste fluid catalytic cracking (FCC) catalyst as partial surrogate for cement can reduce the environmental impact of both the oil-refinery and cement production industries [1,2]. FCC catalysts can be considered as pozzolanic materials since in the presence of water they tend to chemically react with calcium hydroxide to produce compounds possessing cementitious properties [3,4]. In addition, partial replacement of cement with FCC catalysts can enhance the performance of pastes and mortars, namely by improving their compressive strength [5,6]. In the present work the reaction of waste FCC catalyst with Ca(OH)2 has been investigated after a curing time of 28 days by scanning electron microscopy (SEM) with electron backscattered signal (BSE) combined with X-ray energy dispersive spectroscopy (EDS) carried out with a JEOL JSM 7001F instrument operated at 15 kV coupled to an INCA pentaFetx3 Oxford spectrometer. The polished cross-sections of FCC particles embedded in resin have also been evaluated by atomic force microscopy (AFM) in contact mode (CM) using a NanoSurf EasyScan 2 instrument. The SEM/EDS results revealed that an inward migration of Ca occurred during the reaction. A weaker outward migration of Si and Al was also apparent (Fig. 1). The migration of Ca was not homogeneous and tended to follow high-diffusivity paths within the porous waste FCC catalyst particles. The present study suggests that the porosity of waste FCC catalysts is key for the migration/reaction of Ca from the surrounding matrix, playing an important role in the pozzolanic activity of the system. The topography images and surface roughness parameters obtained by atomic force microscopy can be used to infer the local porosity in waste FCC catalyst particles (Fig. 2).