Wetting response of KrF laser ablated polyimide surfaces

The wettability of polyimide surfaces microstructured using KrF laser radiation at fluences above the material ablation threshold was studied by static contact angle measurements. The laser-treated surfaces present a morphology consisting of conical features whose dimensions and areal density depend on the fluence. The effect of these parameters on the surface apparent contact angle depends on the wetting regime. When wetting occurs in the homogeneous regime, the apparent contact angle of the treated surfaces increases with the radiation fluence because the cone dimensions increase. In contrast, when wetting occurs in the heterogeneous regime, the apparent contact angle increases with the radiation fluence because the average distance between cones increases. The apparent water contact angle of the laser-treated surfaces can reach values as high as 162 degrees, as compared to 75 degrees for virgin polyimide.

Cellular uptake of BCG-loaded chitosan microparticles and in vivo evaluation of immune response following intranasal immunisation

Attenuated Mycobacterium bovis bacillus Calmette-Guérin (BCG) is the only currently available vaccine against tuberculosis. It is highly effective in pre-exposure immunisation against TB in children when administered by subcutaneous route to newborns. However, it does not provide permanent protection in adults. In this work, polymeric chitosan-alginate microparticles have been evaluated as potential nasal delivery systems and mucosal adjuvants for live attenuated BCG. Chitosan (CS) has been employed as adjuvant and mucosal permeation-enhancer, and, together with alginate (ALG), as additive to enhance BCG-loaded microparticles (MPs) cellular uptake in a human monocyte cell line, by particle surface modification. The most suitable particles were used for vaccine formulation and evaluation of immune response following intranasal immunisation of BALB/c mice.

Electrochemical response of 70Co-30Ni highly branched 3D-dendritic structures for charge storage electrodes

A 70Co-30Ni dendritic alloy was produced on stainless steel by pulse electrodeposition in the cathodic domain, and oxidized by potential cycling. X-ray diffraction (XRD) identified the presence of two phases and scanning electron microscopy (SEM) evidenced an open 3D highly branched dendritic morphology. After potential cycling in 1 M KOH, SEM and X-ray photoelectron spectroscopy (XPS) revealed, respectively, the presence of thin nanoplates, composed of Co and Ni oxi-hydroxides and hydroxides over the original dendritic film. Cyclic voltammetry tests showd the presence of redox peaks assigned to the oxidation and reduction of Ni and Co centres in the surface film. Charge/discharge measurements revealed capacity values of 121 mAh g(1) at 1 mA cm(2). The capacity retention under 8000 cycles was above 70%, stating the good reversibility of these redox materials and its suitability to be used as charge storage electrodes. Electrochemical impedance spectroscopy (EIS) spectra, taken under different applied bias, showed that the capacitance increased when the electrode was fully oxidized and decreased when the electrode was reduced, reflecting different states-of-charge of the electrode. (C) 2015 Elsevier Ltd. All rights reserved.