Low-Carbon Cement with Waste Oil-Cracking Catalyst Incorporation

The present paper shows preliminary results of an ongoing project which one of the goals is to investigate the viability of using waste FCC catalyst (wFCC), originated from Portuguese oil refinery, to produce low carbon blended cements. For this purpose, four blended cements were produced by substituting cement CEM I 42.5R up to 20% (w/w) by waste FCC catalyst. Initial and final setting times, consistency of standard paste, soundness and compressive strengths after 2, 7 and 28 days were measured. It was observed that the wFCC blended cements developed similar strength, at 28 days, compared to the reference cement, CEM I 42.5R. Moreover, cements with waste FCC catalyst incorporation up to 15% w/w meet European Standard EN 197-1 specifications for CEM II/A type cement, in the 42.5R strength class.

Solubility of red 153 and blue 1 in supercritical carbon dioxide

Solubilities of red 153, (3-[[4-[[5,6(or 6,7)-dichloro-2-benzothiazolyl]azo]phenyl]ethylamino]propanenitrile), an azo compound, and disperse blue1 (1,4,5,8-tetraaminoantraquinone) in supercritical carbon dioxide (SC CO(2)) were measured at T = (333.2 to 393.2) K over the pressure range (12.0 to 40.0) MPa by a flow type apparatus. The solubility of red 153 (0.985. 10(-6) to 37.2. 10(-6)) in the overall region of measurements is found to be significantly higher than that of disperse blue 1 (1.12.10(-7) to 4.89.10(-7)). The solubility behavior of disperse red 153 follows the general solubility trend displayed by disperse dyes with a crossover pressure at about 20 MPa. On the other hand, blue 1, which is a disperse anthraquinone dye, exhibits unexpected behavior not recorded previously there is no crossover pressure at the temperature and pressure ranges studied, and the dye's solubility at T = 333.2 K practically does not increase with pressure. To the best of our knowledge, there are no previous measurements of blue 1 solubility in SC CO(2) reported in the literature. The experimental data were correlated by using the Soave Redlich Kwong equation of state (EoS) with the one-fluid van der Waals mixing rule, and an acceptable correlation of the solubility data for both dyes was obtained.

Effects of oxidante acid treatments on carbon-templated hierarchical SAPO-11 materials: synthesis, characterization and catalytic evaluation in n-decane hydroiosomerization

Hierarchical SAPO-11 was synthesized using a commercial Merck carbon as template. Oxidant acid treatments were performed on the carbon matrix in order to investigate its influence on the properties of SAPO-11. Structural, textural and acidic properties of the different materials were evaluated by XRD, SEM, N-2 adsorption, pyridine adsorption followed by IR spectroscopy and thermal analyses. The catalytic behavior of the materials (with 0.5 wt.% Pt, introduced by mechanic mixture with Pt/Al2O3), were studied in the hydroisomerization of n-decane. The hierarchical samples showed higher yields in monobranched isomers than typical microporous SAPO-11, as a direct consequence of the modification on both porosity and acidity, the later one being the most predominant. (C) 2014 Elsevier B.V. All rights reserved.

Low-carbon cement with waste oil-craking catalyst incorporation

The present paper shows preliminary results of an ongoing project which one of the goals is to investigate the viability of using waste FCC catalyst (wFCC), originated from Portuguese oil refinery, to produce low carbon blended cements. For this purpose, four blended cements were produced by substituting cement CEM I 42.5R up to 20% (w/w) by waste FCC catalyst. Initial and final setting times, consistency of standard paste, soundness and compressive strengths after 2, 7 and 28 days were measured. It was observed that the wFCC blended cements developed similar strength, at 28 days, compared to the reference cement, CEM I 42.5R. Moreover, cements with waste FCC catalyst incorporation up to 15% w/w meet European Standard EN 197-1 specifications for CEM II/A type cement, in the 42.5R strength class.