Hydrogen evolution on nanostructured Ni-Cu foams

Three-dimensional (3D) nickel-copper (Ni-Cu) nanostructured foams were prepared by galvanostatic electrodeposition, on stainless steel substrates, using the dynamic hydrogen bubble template. These foams were tested as electrodes for the hydrogen evolution reaction (HER) in 8 M KOH solutions. Polarisation curves were obtained for the Ni-Cu foams and for a solid Ni electrode, in the 25-85 degrees C temperature range, and the main kinetic parameters were determined. It was observed that the 3D foams have higher catalytic activity than pure Ni. HER activation energies for the Ni-Cu foams were lower (34-36 kJ mol(-1)) than those calculated for the Ni electrode (62 kJ mol(-1)). The foams also presented high stability for HER, which makes them potentially attractive cathode materials for application in industrial alkaline electrolysers.

Phototransistor with nanocrystalline Si/amorphous Si bilayer channel

We report a field-effect phototransistor with a channel comprising a thin nanocrystalline silicon transport layer and a thicker hydrogenated amorphous silicon absorption layer. The semiconductor and dielectric layers were deposited by radio-frequency plasma enhanced chemical vapor deposition. The phototransistor with channel length of 24 microns and photosensitive area of 1.4 mm(2) shows an off-current of about 1 pA, and high photoconductive gain in the subthreshold region. Measurements of the quantum efficiency at different incident light intensities and biasing conditions, along with spectral-response characteristics, and threshold voltage stability characterization demonstrate the feasibility of the phototransistor for low light level detection.

Síntese e fotosensibilização de nanotubos de titanatos

Nesta tese é descrita a preparação de nanotubos de titanatos (TNT) via síntese hidrotérmica alcalina, usando uma nova metodologia que evita a utilização de TiO2 cristalino como precursor. Foi estudada a influência da substituição sódio/protão na estrutura, morfologia e propriedades ópticas dos materiais preparados. Os resultados mostraram que a substituição Na+ → H+ resulta numa redução na distância intercamadas dos TNTs, tendo sido medidos valores entre 1.13±0.03 nm e 0.70±0.02 nm para aquele parâmetro. O comportamento óptico dos TNTs foi estudado na região UV-vis, estimando-se um hiato óptico de energia 3.27±0.03 eV para a amostra com maior teor de sódio enquanto que para a amostra protonada foi determinado um valor de 2.81±0.02 eV. Estes valores mostram que a troca iónica Na+ → H+ teve influência no desvio da banda de absorção dos TNTs para a região do visível próximo. A actividade fotocatalítica dos TNTs na degradação do corante rodamina 6G (R6G) foi posteriormente estudada. Verificou-se que, apesar de a amostra com maior teor de sódio ter sido a que exibiu maior capacidade para adsorver o R6G, foi a amostra protonada que apresentou a actividade catalítica mais elevada na fotodegradação deste corante. Numa segunda fase, e com o objectivo de preparar novos materiais nanoestruturados fotosensíveis, procedeu-se à decoração dos TNTs protonados com semicondutores (SC) nanocristalinos usando um método novo. Para o efeito os TNTs foram decorados com nanocristalites de ZnS, CdS e Bi2S3. Foi estudada a influência do tipo de semicondutor na estrutura, morfologia e propriedades ópticas dos SC/TNTs obtidos. Verificou-se que, para qualquer dos semicondutores usados no processo de decoração, a estrutura dos TNTs é preservada e não ocorre segregação do SC. Verificou-se ainda que a morfologia dos nanocompósitos preparados depende fortemente da natureza do semicondutor. No que respeita ao comportamento óptico destes materiais, foram determinados hiatos ópticos de energia 3.67±0.03 eV, 2.47±0.03 eV e 1.35±0.01 eV para as amostras ZnS/TNT, CdS/TNT e Bi2S3/TNT, respectivamente. Estes resultados mostram que através do processo de decoração de TNTs com semicondutores podem ser preparados materiais nanocompósitos inovadores, com propriedades ópticas novas e/ou pré-definidas numa gama alargada do espectro electromagnético.

Electrodeposition and characterization of nickel–copper metallic foams for application as electrodes for supercapacitors

Nickel-copper metallic foams were electrodeposited from an acidic electrolyte, using hydrogen bubble evolution as a dynamic template. Their morphology and chemical composition was studied by scanning electron microscopy and related to the deposition parameters (applied current density and deposition time). For high currents densities (above 1 A cm(-2)) the nickel-copper deposits have a three-dimensional foam-like morphology with randomly distributed nearly-circular pores whose walls present an open dendritic structure. The nickel-copper foams are crystalline and composed of pure nickel and a copper-rich phase containing nickel in solid solution. The electrochemical behaviour of the material was studied by cyclic voltammetry and chronopotentiometry (charge-discharge curves) aiming at its application as a positive electrode for supercapacitors. Cyclic voltammograms showed that the Ni-Cu foams have a pseudocapacitive behaviour. The specific capacitance was calculated from charge-discharge data and the best value (105 F g(-1) at 1 mA cm(-2)) was obtained for nickel-copper foams deposited at 1.8 A cm(-2) for 180 s. Cycling stability of these foams was also assessed and they present a 90 % capacitance retention after 10,000 cycles at 10 mA cm(-2).

Electrodeposition and characterization of nikel-copper metallic foams for application as electrodes for supercapacitors

Nickel-copper metallic foams were electrodeposited from an acidic electrolyte, using hydrogen bubble evolution as a dynamic template. Their morphology and chemical composition was studied by scanning electron microscopy and related to the deposition parameters (applied current density and deposition time). For high currents densities (above 1 A cm(-2)) the nickel-copper deposits have a three-dimensional foam-like morphology with randomly distributed nearly-circular pores whose walls present an open dendritic structure. The nickel-copper foams are crystalline and composed of pure nickel and a copper-rich phase containing nickel in solid solution. The electrochemical behaviour of the material was studied by cyclic voltammetry and chronopotentiometry (charge-discharge curves) aiming at its application as a positive electrode for supercapacitors. Cyclic voltammograms showed that the Ni-Cu foams have a pseudocapacitive behaviour. The specific capacitance was calculated from charge-discharge data and the best value (105 F g(-1) at 1 mA cm(-2)) was obtained for nickel-copper foams deposited at 1.8 A cm(-2) for 180 s. Cycling stability of these foams was also assessed and they present a 90 % capacitance retention after 10,000 cycles at 10 mA cm(-2).

Is it possible to remove polymeric nanoparticles from aqueous paints during the activated sludge treatment?

The market for emulsion polymers (latexes) is large and growing at the expense of other manufacturing processes that emit higher amounts of volatile organic solvents. The paint industry is not an exception and solvent-borne paints have been gradually substituted by aqueous paints. In their life-cycle, much of the aqueous paint used for architectural or decorative purposes will eventually be discharged into wastewater treatment facilities, where its polymeric nanoparticles (mainly acrylic and styrene-acrylic) can work as xenobiotics to the microbial communities present in activated sludge. It is well established that these materials are biocompatible at macroscopic scale. But is their behaviour the same at nanoscale? What happens to the polymeric nanoparticles during the activated sludge process? Do nanoparticles agregate and are discharged together with the sludge or remain in emulsion? How do microorganisms interact with these nanoparticles? Are nanoparticles degradated by them? Are they adsorbed? Are these nanoparticles toxic to the microbial community? To study the influence of these xenobiotics in the activated sludge process, an emulsion of cross-linked poly(butyl methacrylate) nanoparticles of ca. 50 nm diameter was produced and used as model compound. Activated sludge from a wastewater treatment plant was tested by the OCDE’s respiration inhibition test using several concentrations of PBMA nanoparticles. Particle aggregation was followed by Dynamic Light Scattering and microorganism surfaces were observed by Atomic Force Microscopy. Using sequential batch reactors (SBRs) and continuous reactors, both inoculated with activated sludge, the consumption of carbon, ammonia, nitrite and nitrate was monitored and compared, in the presence and absence of nanoparticles. No particles were detected in all treated waters by Dynamic Light Scattering. This can either mean that microorganisms can efficiently remove all polymer nanoparticles or that nanoparticles tend to aggregate and be naturally removed by precipitation. Nevertheless respiration inhibition tests demonstrated that microorganisms consume more oxygen in the presence of nanoparticles, which suggests a stress situation. It was also observed a slight decrease in the efficiency of nitrification in the presence of nanoparticles. AFM images showed that while the morphology of some organisms remained the same both in the presence and absence of nanoparticles, others assumed a rough surface with hilly like shapes of ca. 50 nm when exposed to nanoparticles. Nanoparticles are thus likely to be either incorporated or adsorbed at the surface of some organisms, increasing the overall respiration rate and decreasing nitrification efficiency. Thus, despite its biocompatibility at macroscopic scale, PBMA is likely to be no longer innocuous at nanoscale.

Hierarchical wrinkling on elastometric Janus spheres

Hierarchical wrinkling on elastomeric Janus spheres is permanently imprinted by swelling, for different lengths of time, followed by drying the particles in an appropriate solvent. First-order buckling with a spatial periodicity (lambda(11)) of the order of a few microns and hierarchical structures comprising of 2nd order buckling with a spatial periodicity (lambda(12)) of the order of hundreds of nanometers have been obtained. The 2nd order buckling features result from a Grinfeld surface instability due to the diffusion of the solvent and the presence of sol molecules.

Characterisation and electrochemical behaviour of electrodeposited Cu-Fe foams applied as pseudocapacitor electrodes

Copper iron (Cu-Fe) 3D porous foams for supercapacitor electrodes were electrodeposited in the cathodic regime, on stainless steel current collectors, using hydrogen bubbling dynamic template. The foams were prepared at different current densities and deposition times. The foams were submitted to thermal conditioning at temperatures of 150 and 250 degrees C. The morphology, composition and structure of the formed films were studied by SEM, EDS and XRD, respectively. The electrochemical behaviour was studied by cyclic voltammetry, electrochemical impedance spectroscopy and chronopotentiometry. The morphology of the 3D Cu-Fe foams is sensitive to the electrodeposition current and time. The increase of the current density produces a denser, larger and more ramified dendritic structure. Thermal conditioning at high temperature induces a coarser grain structure and the formation of copper oxides, which affect the electrochemical behaviour. The electrochemical response reveals the presence of various redox peaks assigned to the oxidation and reduction of Cu and Fe oxides and hydroxides in the foams. The specific capacitance of the 3D Cu Fe foams was significantly enhanced by thermal conditioning at 150 degrees C. The highest specific capacitance values attained 297 Fg(-1) which are much above the ones typically observed for single Cu or Fe Oxides and hydroxides. These values highlight a synergistic behaviour resulting from the combination of Cu and Fe in the form of nanostructured metallic foams. Moreover, the capacitance retention observed in an 8000 charge/discharge cycling test was above 66%, stating the good performance of these materials and its enhanced electrochemical response as supercapacitor negative electrodes. (C) 2014 Elsevier B.V. All rights reserved.