Durability performance of self-compacting concrete (SCC) with binary and ternary mixes of fly ash and limestone filler

The basic objective of this work is to evaluate the durability of self-compacting concrete (SCC) produced in binary and ternary mixes using fly ash (FA) and limestone filler (LF) as partial replacement of cement. The main characteristics that set SCC apart from conventional concrete (fundamentally its fresh state behaviour) essentially depend on the greater or lesser content of various constituents, namely: greater mortar volume (more ultrafine material in the form of cement and mineral additions); proper control of the maximum size of the coarse aggregate; use of admixtures such as superplasticizers. Significant amounts of mineral additions are thus incorporated to partially replace cement, in order to improve the workability of the concrete. These mineral additions necessarily affect the concrete's microstructure and its durability. Therefore, notwithstanding the many well-documented and acknowledged advantages of SCC, a better understanding its behaviour is still required, in particular when its composition includes significant amounts of mineral additions. An ambitious working plan was devised: first, the SCC's microstructure was studied and characterized and afterwards the main transport and degradation mechanisms of the SCC produced were studied and characterized by means of SEM image analysis, chloride migration, electrical resistivity, and carbonation tests. It was then possible to draw conclusions about the SCC's durability. The properties studied are strongly affected by the type and content of the additions. Also, the use of ternary mixes proved to be extremely favourable, confirming the expected beneficial effect of the synergy between LF and FA.

Effect of explosive mixture on quality of explosive welds of copper to aluminium

The aim of this research is to investigate the influence of explosive ratio and type of sensitizer on the quality of explosive welds between copper and aluminium alloy plates. The welds were performed on a partially overlapping joint configuration using an emulsion explosive (EE) with two different sensitizers, hollow glass microspheres (HGMS) and expanded polystyrene spheres (EPS). Welds with an improved surface were achieved by using the HGMS sensitizer. A higher wave amplitude was registered in welds produced with the EPS sensitizer. In turn, the dimension of the molten pockets was influenced by the explosive ratio, increasing in size with increases in the values of this parameter. The intermetallic content of these zones varied according to the sensitizer type. Unlike the CuAl2 phase, the Cu-richer phases CuAl and Cu9Al4 were only identified in welds performed using the EPS sensitizer. An increase in hardness was observed at the interface of all welds, which resulted from both the presence of intermetallic phases and the plastic deformation of the materials promoted by the impact. This effect was most evident on the aluminium alloy side. All the welds had a greater strength than copper, i.e. the weakest material of the joint. (C) 2016 Elsevier Ltd. All rights reserved.