Modifying fish gelatin electrospun membranes for biomedical applications: cross- linking and swelling behavior

Development of suitable membranes is a fundamental requisite for tissue and biomedical engineering applications. This work presents fish gelatin random and aligned electrospun membranes cross-linked with glutaraldehyde (GA). It was observed that the fiber average diameter and the morphology is not influenced by the GA exposure time and presents fibers with an average diameter around 250 nm. Moreover, when the gelatin mats are immersed in a phosphate buffered saline solution (PBS), they can retain as much as 12 times its initial weight of solution almost instantaneously, but the material microstructure of the fiber mats changes from the characteristic fibrous to an almost spherical porous structure. Cross-linked gelatin electrospun fiber mats and films showed a water vapor permeability of 1.37 ± 0.02 and 0.13 ± 0.10 (g.mm)/(m2.h.kPa), respectively. Finally, the processing technique and cross-linking process does not inhibit MC-3T3-E1 cell adhesion. Preliminary cell culture results showed good cell adhesion and proliferation in the cross-linked random and aligned gelatin fiber mats.

Bioactive albumin functionalized polylactic acid membranes for improved biocompatibility

Biocompatibility is a major challenge for successful application of many biomaterials. In this study the ability to coat chemically and enzymatically activated poly(L-lactic acid) (PLA) membranes with heat denatured human serum albumin to improve biocompatibility was investigated. PLA membranes hydrolyzed with NaOH or cutinase and then treated with 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide, hydrochloride (EDAC) as a heterobifunctional cross-linker promoted the coupling single bondCOOH groups on PLA membranes and single bondNH2 groups of heat denatured human serum albumin. This resulted in increased hydrophilicity (lowest water contact angles of 43° and 35°) and highest antioxidant activity (quenching of 79 μM and 115 μM tetramethylazobisquinone (TMAMQ) for NaOH and cutinase pretreated membranes, respectively). FTIR analysis of modified PLA membranes showed new peaks attributed to human serum albumin (amide bond, NH2 and side chain stretching) appearing within 3600–3000 cm−1 and 1700–1500 cm−1 (Fig. 3). MTT studies also showed that osteoblasts-like and MC-3T3-E1 cells viability increased 2.4 times as compared to untreated PLA membranes. The study therefore shows that this strategy of modifying the surfaces of PLA polymers could significantly improve biocompatibility.