Influence of electrospinning parameters on Poly(hydroxybutyrate) electrospun membranes fiber size and distribution

Poly(hydroxybutyrate) (PHB) obtained from sugar cane was dissolved in a blend of chloroform and dimethylformamide (DMF) and electrospun at 40 ºC. By adding DMF to the solution, the electrospinning process for the PHB polymer becomes more stable, allowing complete polymer crystallization during the jet travelling between the tip and the grounded collector. The influence of processing parameters on fiber size and distribution was systematically studied. It was observed that an increase of tip inner diameter promotes a decrease of the fiber average size and a broader distribution. On the other hand, an increase of the electric field and flow rate produces an increase of fiber diameter until a maximum of ~2.0 m, but for electric fields higher than 1.5 kV.cm-1, a decrease of the fiber diameter was observed. Polymer crystalline phase seems to be independent of the processing conditions and a crystallinity degree of 53 % was found. Moreover, thermal degradation of the as-spun membrane occurs in single step degradation with activation energy of 91 kJ/mol. Furthermore, MC-3T3-E1 cell adhesion was not inhibited by the fiber mats preparation, indicating their potential use for biomedical applications.

Processing and characterization of alpha-elastin electrospun membranes

Elastin isolated from fresh bovine ligaments was dissolved in a mixture of 1,1,1,3,3,3-Hexafluoro-2-propanol and water and electrospun into fiber membranes under different processing conditions. Fiber mats of randomly and aligned fibers were obtained with fixed and rotating ground collectors and fibrils were composed by thin ribbons whose width depends on electrospinning conditions; fibrils with 721 nm up to 2.12 m width were achieved. After cross-linking with glutaraldehyde, -elastin can uptake as much as 1700 % of PBS solution and a slight increase on fiber thickness was observed. The glass transition temperature of electrospun fiber mats was found to occur at ~ 80 ºC. Moreover, -Elastin showed to be a perfect elastomeric material, and no mechanical hysteresis was found in cycle mechanical measurements. The elastic modulus obtained for oriented and random fibers mats in a PBS solution was 330 ± 10 kPa and 732 ± 165 kPa, respectively. Finally, the electrospinning and cross-linking process does not inhibit MC-3T3-E1 cell adhesion. Cell culture results showed good cell adhesion and proliferation in the cross-linked elastin fiber mats.

Fatigue Prediction on Fibrin Poly-ε-caprolactone Macroporous Scaffolds

Tissue engineering applications rely on scaffolds that during its service life, either for in-vivo or in vitro applications, are under mechanical solicitations. The variation of the mechanical condition of the scaffold is strongly relevant for cell culture and has been scarcely addressed. Fatigue life cycle of poly-ε-caprolactone, PCL, scaffolds with and without fibrin as filler of the pore structure were characterized both dry and immersed in liquid water. It is observed that the there is a strong increase from 100 to 500 in the number of loading cycles before collapse in the samples tested in immersed conditions due to the more uniform stress distributions within the samples, the fibrin loading playing a minor role in the mechanical performance of the scaffolds

Applying complex network theory to the understanding of high-aspect-ratio carbon-filled composites

This work demonstrates that the theoretical framework of complex networks typically used to study systems such as social networks or the World Wide Web can be also applied to material science, allowing deeper understanding of fundamental physical relationships. In particular, through the application of the network theory to carbon nanotubes or vapour-grown carbon nanofiber composites, by mapping fillers to vertices and edges to the gap between fillers, the percolation threshold has been predicted and a formula that relates the composite conductance to the network disorder has been obtained. The theoretical arguments are validated by experimental results from the literature.

The perceived potential of business social networking sites

Business social networking is a facilitator of several business activities, such as market studies, communication with clients, and identification of business partners. This paper traduces the results of a study undertaken with the purpose of getting to know how the potential of networking is perceived in the promotion of business by participants of the LinkedIn network, and presents two main contributions: (1) to disseminate within the business community which is the relevance given to social networking; and (2) which are the social networks best suitable to the promotion of business, to support the definition of strategies and approaches accordingly. The results confirm that LinkedIn is the most suitable network to answer the needs of those that look for professional contacts and for the promotion of business, while innovation is the most recognized factor in the promotion of business through social networking. This study contributes to a better understanding of the potential of different business social networking sites, to support organizations and professionals to align their strategies with the perceived potential of each network.

PHB-PEO electrospun fiber membranes containing chlorhexidine for drug delivery applications

Fiber meshes of poly(hydroxybutyrate) (PHB) and poly(hydroxybutyrate)/ poly(ethylene oxide) (PHB/PEO) with different concentrations of chlorhexidine (CHX) were prepared by electrospinning, for assessment as a polymer based drug delivery system. The electrospun fibers were characterized at morphological, molecular and mechanical levels. The bactericidal potential of PHB and PHB/PEO electrospun fibers with and without CHX was investigated against Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus) by disk diffusion susceptibility tests. Electrospun fibers containing CHX exhibited bactericidal activity. PHB/PEO-1%CHX displayed higher CHX release levels and equivalent antibacterial activity when compared to PHB/PEO with 5 and 10 wt% CHX. Bactericidal performance of samples with 1 wt% CHX was assessed by Colony Forming Units (CFU), where a reduction of 100 % and 99.69 % against E. coli and S. aureus were achieved, respectively.

Success factors of regional airports: the case of Oporto airport

Oporto Airport (OPO) is a success story among European regional airports. This success is expressed, among other ways, in the rapid expansion of routes and the strong growth in demand, as well as in the recognition of the airport’s quality by its users. Over the past decade, the volume of traffic increased by almost 3.4 million passengers, from the 2.6 million recorded in 2002 to over 6 million in 2012. In this paper, we analyse some of the factors that influenced the success of Oporto Airport, namely the expansion of capacity and improvements to infrastructure, the increase in the number of routes and the increased demand in response to the new capacities of this airport-airlines set. Particular emphasis is given to the role of low cost carriers (LCC) in the growth of Oporto Airport and to strategies of attracting more traffic. Some of the main opportunities and challenges that this airport will face in the coming years are also discussed.

Modifying fish gelatin electrospun membranes for biomedical applications: cross- linking and swelling behavior

Development of suitable membranes is a fundamental requisite for tissue and biomedical engineering applications. This work presents fish gelatin random and aligned electrospun membranes cross-linked with glutaraldehyde (GA). It was observed that the fiber average diameter and the morphology is not influenced by the GA exposure time and presents fibers with an average diameter around 250 nm. Moreover, when the gelatin mats are immersed in a phosphate buffered saline solution (PBS), they can retain as much as 12 times its initial weight of solution almost instantaneously, but the material microstructure of the fiber mats changes from the characteristic fibrous to an almost spherical porous structure. Cross-linked gelatin electrospun fiber mats and films showed a water vapor permeability of 1.37 ± 0.02 and 0.13 ± 0.10 (g.mm)/(m2.h.kPa), respectively. Finally, the processing technique and cross-linking process does not inhibit MC-3T3-E1 cell adhesion. Preliminary cell culture results showed good cell adhesion and proliferation in the cross-linked random and aligned gelatin fiber mats.

Effect of neutralization and cross-linking on the thermal degradation of chitosan electrospun membranes

Thermal degradation of as electrospun chitosan membranes and samples subsequently treated with ethanol and cross-linked with glutaraldehyde (GA) have been studied by thermogravimetry (TG) coupled with an infrared spectrometer (FTIR). The influence of the electrospinning process and cross-linking in the electrospun chitosan thermal stability was evaluated. Up to three degradation steps were observed in the TG data, corresponding to water dehydration reaction at temperatures below 100 ºC, loss of side groups formed between the amine groups of chitosan and trifluoroacetic acid between 150 – 270 ºC and chitosan thermal degradation that starts around 250 ºC and goes up to 400 ºC. The Kissinger model was employed to evaluate the activation energies of the electrospun membranes during isothermal experiments and revealed that thermal degradation activation energy increases for the samples processed by electrospinning and subsequent neutralization and cross-linking treatments with respect to the neat chitosan powder.

Organisational and professional commitments: the influence in nurses´organizational citizenship behaviours

The way an employee behaves in his work can be influenced by the organisational and professional commitment. Nurses are professionals who are guided by organisational and professional goals and values. Among nurses, professional commitment may be an important antecedent of organisational citizenship behaviours. The study shows how organisational and professional commitment is related with nurses’ organisational citizenship behaviours. Data from a sample of 420 nurses working in two hospitals --- the Hospital of St. Marcos, Braga and the Hospital Centre of Alto Ave, Guimarães and Fafe units were collected. The main findings are as follows: (a) organisational commitment and professional commitment contribute to the explanation of nurses’ organisational citizenship behaviours, (b) affective organisational commitment, continuance organisational commitment --- personal sacrifice, affective professional commitment and continuance professional commitment explain 28.6% of variance of organisational citizenship behaviours. © 2013 Instituto Politécnico do Cávado e do Ave (IPCA). Published by Elsevier España, S.L.U. All rights reserved.