Thermal and hydrolytic degradation of electrospun fish gelatin membranes

The thermal and hydrolytic degradation of electrospun gelatin membranes cross-linked with glutaraldehyde in vapor phase has been studied. In vitro degradation of gelatin membranes was evaluated in phosphate buffer saline solution at 37 ºC. After 15 days under these conditions, a weight loss of 68 % was observed, attributed to solvation and depolymerization of the main polymeric chains. Thermal degradation kinetics of the gelatin raw material and as-spun electrospun membranes showed that the electrospinning processing conditions do not influence polymer degradation. However, for cross-linked samples a decrease in the activation energy was observed, associated with the effect of glutaraldehyde cross-linking reaction in the inter- and intra-molecular hydrogen bonds of the protein. It is also shown that the electrospinning process does not affect the formation of the helical structure of gelatin chains.

Processing and characterization of alpha-elastin electrospun membranes

Elastin isolated from fresh bovine ligaments was dissolved in a mixture of 1,1,1,3,3,3-Hexafluoro-2-propanol and water and electrospun into fiber membranes under different processing conditions. Fiber mats of randomly and aligned fibers were obtained with fixed and rotating ground collectors and fibrils were composed by thin ribbons whose width depends on electrospinning conditions; fibrils with 721 nm up to 2.12 m width were achieved. After cross-linking with glutaraldehyde, -elastin can uptake as much as 1700 % of PBS solution and a slight increase on fiber thickness was observed. The glass transition temperature of electrospun fiber mats was found to occur at ~ 80 ºC. Moreover, -Elastin showed to be a perfect elastomeric material, and no mechanical hysteresis was found in cycle mechanical measurements. The elastic modulus obtained for oriented and random fibers mats in a PBS solution was 330 ± 10 kPa and 732 ± 165 kPa, respectively. Finally, the electrospinning and cross-linking process does not inhibit MC-3T3-E1 cell adhesion. Cell culture results showed good cell adhesion and proliferation in the cross-linked elastin fiber mats.

PHB-PEO electrospun fiber membranes containing chlorhexidine for drug delivery applications

Fiber meshes of poly(hydroxybutyrate) (PHB) and poly(hydroxybutyrate)/ poly(ethylene oxide) (PHB/PEO) with different concentrations of chlorhexidine (CHX) were prepared by electrospinning, for assessment as a polymer based drug delivery system. The electrospun fibers were characterized at morphological, molecular and mechanical levels. The bactericidal potential of PHB and PHB/PEO electrospun fibers with and without CHX was investigated against Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus) by disk diffusion susceptibility tests. Electrospun fibers containing CHX exhibited bactericidal activity. PHB/PEO-1%CHX displayed higher CHX release levels and equivalent antibacterial activity when compared to PHB/PEO with 5 and 10 wt% CHX. Bactericidal performance of samples with 1 wt% CHX was assessed by Colony Forming Units (CFU), where a reduction of 100 % and 99.69 % against E. coli and S. aureus were achieved, respectively.

Modifying fish gelatin electrospun membranes for biomedical applications: cross- linking and swelling behavior

Development of suitable membranes is a fundamental requisite for tissue and biomedical engineering applications. This work presents fish gelatin random and aligned electrospun membranes cross-linked with glutaraldehyde (GA). It was observed that the fiber average diameter and the morphology is not influenced by the GA exposure time and presents fibers with an average diameter around 250 nm. Moreover, when the gelatin mats are immersed in a phosphate buffered saline solution (PBS), they can retain as much as 12 times its initial weight of solution almost instantaneously, but the material microstructure of the fiber mats changes from the characteristic fibrous to an almost spherical porous structure. Cross-linked gelatin electrospun fiber mats and films showed a water vapor permeability of 1.37 ± 0.02 and 0.13 ± 0.10 (g.mm)/(m2.h.kPa), respectively. Finally, the processing technique and cross-linking process does not inhibit MC-3T3-E1 cell adhesion. Preliminary cell culture results showed good cell adhesion and proliferation in the cross-linked random and aligned gelatin fiber mats.

Uma abordagem na ótica do consumidor: regiões turísticas transfronteiriças

O turismo é um dos mais importantes e atuais motores de crescimento de uma economia, marcado pelo dinamismo, diversidade da oferta e crescimento constante, nele se incidindo o objeto de estudo proposto. É nosso intuito estudar o comportamento e perfil do consumidor de turismo, numa perspetiva de marketing, de modo a melhor conhecer o padrão de consumo turístico em contextos específicos de turismo, em mercados cada vez mais dinâmicos e com interesses individuais distintos. Em particular, discutimos tendências, motivações e determinantes na procura de turismo de nichos em regiões transfronteiriças. Espera-se conhecer o padrão de consumo turístico de zonas transfronteiriças, procurando sistematizar os aspetos principais e encontrar tendências/hábitos específicos na procura de nichos. O trabalho a desenvolver será composto por duas partes distintas: numa primeira parte será feita uma revisão da literatura existente no âmbito desta temática, numa segunda parte será desenvolvido um estudo empírico, que procurará dar um contributo acrescido à sua compreensão, tendo em vista os objetivos de pesquisa previamente definidos

Sistema eletromecânico para controlo intuitivo dos movimentos de uma sonda transesofágica

O ser humano realiza uma alimentação pouco variada, com grandes teores de açúcar e gorduras saturadas, ao mesmo tempo, está sujeito a profissões cada vez mais competitivas aonde passa longos períodos sentados sem qualquer esforço físico. Estes aspetos levam à acumulação de gorduras em redor de todos os órgãos, que promovem o aparecimento de problemas cardiovascular, que são atualmente, a principal causa de morte no mundo. O tratamento das doenças cardiovasculares é em muitas situações realizado por procedimentos minimamente-invasivos, que são guiados através de imagem médica. Contudo, a utilização de radiação durante a navegação é normalmente requerida o que tem consequências para o paciente e para a equipa médica. Nesta dissertação, focamo-nos nos recentes sistemas de aquisição de imagem sem radiação e no desenvolvimento de sistemas mais inteligentes para facilitar o controlo destes equipamentos durante o procedimento. Assim, pretendemos desenvolver um robô que apoie na aquisição de imagens de ultrassons através de uma sonda transesofágica. O robô desenvolvido possui um conjunto de engrenagens que fazem a transferência de movimento para as rodas dos manípulos da sonda e um encoder magnético que proporciona uma leitura rápida e de alta precisão dos movimentos da sonda. De forma a automaticamente adaptar a posição da sonda na direção do alvo anatómico, um sistema de motion tracking foi acoplado ao robô e ao instrumento cirúrgico utilizado durante o procedimento. Assim, todos os movimentos realizados pelo intervencionista são repetidos pela sonda, permitindo assim adquirir uma imagem de ultrassom sempre centrada no instrumento cirúrgico. Para avaliar a performance do robô foram realizados testes em laboratório. mais concretamente: 1) controlo do robô sem sonda acoplada e 2) controlo do robô com sonda acoplada. Os testes foram realizados com diferentes posições angulares, em todas as gamas de funcionamento do robô, avaliando o erro da posição final em relação posição desejada e o tempo de resposta. Os resultados demonstraram que um erro médio de 2º foi observado para as diferentes situações com um tempo médio de resposta de 300 ms. Os resultados alcançados demonstraram uma boa resposta do sistema, pelo que se espera que sistema desenvolvido venha ser capaz de reduzir o tempo de intervenção, aumentando a qualidade da intervenção e minimizando possíveis erros.