Influence of electrospinning parameters on Poly(hydroxybutyrate) electrospun membranes fiber size and distribution

Poly(hydroxybutyrate) (PHB) obtained from sugar cane was dissolved in a blend of chloroform and dimethylformamide (DMF) and electrospun at 40 ��C. By adding DMF to the solution, the electrospinning process for the PHB polymer becomes more stable, allowing complete polymer crystallization during the jet travelling between the tip and the grounded collector. The influence of processing parameters on fiber size and distribution was systematically studied. It was observed that an increase of tip inner diameter promotes a decrease of the fiber average size and a broader distribution. On the other hand, an increase of the electric field and flow rate produces an increase of fiber diameter until a maximum of ~2.0 ���m, but for electric fields higher than 1.5 kV.cm-1, a decrease of the fiber diameter was observed. Polymer crystalline phase seems to be independent of the processing conditions and a crystallinity degree of 53 % was found. Moreover, thermal degradation of the as-spun membrane occurs in single step degradation with activation energy of 91 kJ/mol. Furthermore, MC-3T3-E1 cell adhesion was not inhibited by the fiber mats preparation, indicating their potential use for biomedical applications.

Bioactive albumin functionalized polylactic acid membranes for improved biocompatibility

Biocompatibility is a major challenge for successful application of many biomaterials. In this study the ability to coat chemically and enzymatically activated poly(L-lactic acid) (PLA) membranes with heat denatured human serum albumin to improve biocompatibility was investigated. PLA membranes hydrolyzed with NaOH or cutinase and then treated with 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide, hydrochloride (EDAC) as a heterobifunctional cross-linker promoted the coupling single bondCOOH groups on PLA membranes and single bondNH2 groups of heat denatured human serum albumin. This resulted in increased hydrophilicity (lowest water contact angles of 43�� and 35��) and highest antioxidant activity (quenching of 79 ��M and 115 ��M tetramethylazobisquinone (TMAMQ) for NaOH and cutinase pretreated membranes, respectively). FTIR analysis of modified PLA membranes showed new peaks attributed to human serum albumin (amide bond, NH2 and side chain stretching) appearing within 3600���3000 cm���1 and 1700���1500 cm���1 (Fig. 3). MTT studies also showed that osteoblasts-like and MC-3T3-E1 cells viability increased 2.4 times as compared to untreated PLA membranes. The study therefore shows that this strategy of modifying the surfaces of PLA polymers could significantly improve biocompatibility.