8 resultados para thermal treatments
em Biblioteca Digital da Produção Intelectual da Universidade de São Paulo (BDPI/USP)
Resumo:
Pure Er:YAB (Er:YAl(3)(BO(3))(4)) nanometer-sized crystalline powder was produced from low cost chemical route, the polymeric precursor method. The initial homogeneous solutions were heat treated from 200 to 700A degrees C under oxygen atmosphere and the unique crystalline phase was synthesized at around 1150A degrees C. The thermal treatments and the initial stoichiometry play a very important role on the Er:YAB preparation. The thermal events of amorphous precursor resins and the crystallization process up to phase formation were investigated.
Resumo:
The thermoluminescence (TL) peak in natural sodalite near 230 degrees C which appears only after submitted to thermal treatments and to gamma irradiation has been studied in parallel with electron paramagnetic resonance (EPR) spectrum appearing under the same procedure This study revealed a full correlation between the 230 degrees C TL peak and the eleven hyperfine lines from EPR spectrum In both case the centers disappear at the same temperature and are restored after gamma irradiation A complete model for the 230 C TL peak is presented and discussed In addition to the correlation and TL model specific characteristics of the TL peaks are described (C) 2010 Elsevier B V All rights reserved
Resumo:
Samples of natural andalusite (Al(2)SiO(5)) crystal have been investigated in terms of thermoluminescence (TL) and electron paramagnetic resonance (EPR) measurements. The TL glow curves of samples previously annealed at 600 degrees C for 30 min and subsequently gamma-irradiated gave rise to four glow peaks at 150, 210, 280 and 350 degrees C. The EPR spectra of natural samples heat-treated at 600 degrees C for 30 min show signals at g = 5.94 and 2.014 that do not change after gamma irradiation and thermal treatments. However, it was observed that the appearance of a paramagnetic center at g=1.882 for the samples annealed at 600 degrees C for 30 min followed gamma irradiation. This line was attributed to Ti(3+) centers. The EPR signals observed at g=5.94 and 2.014 are due to Fe(3+). Correlations between EPR and TL results of these crystals show that the EPR line at g=1.882 and the TL peak at 280 degrees C can be attributed to the same defect center. (C) 2011 Elsevier B.V. All rights reserved.
Resumo:
Samples of natural sodalite, Na(8)Al(6)Si(6)O(24)Cl(2), submitted to gamma irradiation and to thermal treatments, have been investigated using the thermoluminescence (TL) and electron paramagnetic resonance (EPR) techniques. Both, natural and heat-treated samples at 500A degrees C in air for 30 min, present an EPR signal around g = 2.01132 attributed to oxygen hole centers. The EPR spectra of irradiated samples show an intense line at g = 2.0008 superimposed by a hyperfine multiplet of 11 lines due to an O(-) ion in an intermediate position with respect to two adjacent Al nuclei. In the TL measurements, the samples were annealed at 500A degrees C for 30 min and then irradiated with gamma doses varying from 0.001 to 20 kGy. All the samples have shown TL peaks at 110, 230, 270, 365, and 445A degrees C. A correlation between the EPR g = 2.01132 line and the 365A degrees C TL peak was observed. A TL model is proposed in which a Na(+) ion acts as a charge compensator when an Al(3+) ion replaces a Si(4+) lattice ion. The gamma ray destruction of the Al-Na complex provides an electron trapped at the Na and a hole trapped at a non-bridging oxygen ion adjacent to the Al(3+) ion.
Resumo:
Silicate mineral hemimorphite has been investigated concerning its TL, IR and EPR properties. A broad TL peak around 180 degrees C and a weaker and narrower peak around 360 degrees C were found in a sample annealed at 600 degrees C for I h and then irradiated. The deconvolution using the CGCD method revealed peaks around 132, 169, 222 and 367 degrees C. The reflectivity measurements showed several bands in the NIR region due to H(2)O, OH and Al-OH complexes. No band was observed in the visible region. The thermal treatments were carried out from similar to 110 to 940 degrees C and dehydration was observed, first causing a diminishing optical absorption in general and the disappearance of water and hydroxyl absorption bands. The EPR spectrum of natural hemimorphite, presented Cu(2+) signals at g = 2.4 and g = 2.1 plus E(1)` signal superposed to Fe(3+) signal around g = 2.0. (C) 2008 Elsevier Ltd. All rights reserved.
Resumo:
The phase change of a natural hemimorphite sample from Minas Gerais (Brazil) was investigated by two X-ray diffraction (XRD) methods and by near-infrared reflectance spectroscopy. Applying successive thermal treatments, the crystal structure undergoes two orientation conversions. The first one occurs at about 550 degrees C, and it was revealed by the Laue method. Below 500 degrees C, the water molecules were partially expelled without changing the crystal structure. A fact that supports this statement is the sequential disappearance of the water bands at 1400 and 1900 nm by thermal treatment. The second conversion takes place below 939 degrees C. Moreover, at 972 degrees C a phase change to the willemite mineral (alpha-Zn(2)SiO(4)) has been observed. This last conversion was confirmed by the power XRD. In addition, natural hemimorphite displayed a high pyroelectricity, which is related both to the absence of inverse centre and to the presence of molecular water and hydroxyl groups in the crystal structure.
Resumo:
Films of amorphous aluminium nitride (AlN) were prepared by conventional radio frequency sputtering of an Al + Cr target in a plasma of pure nitrogen. The Cr-to-Al relative area determines the Cr content, which remained in the similar to 0-3.5 at% concentration range in this study. Film deposition was followed by thermal annealing of the samples up to 1050 degrees C in an atmosphere of oxygen and by spectroscopic characterization through energy dispersive x-ray spectrometry, photoluminescence and optical transmission measurements. According to the experimental results, the optical-electronic properties of the Cr-containing AlN films are highly influenced by both the Cr concentration and the temperature of the thermal treatments. In fact, thermal annealing at 1050 degrees C induces the development of structures that, because of their typical size and distinctive spectral characteristics, were designated by ruby microstructures (RbMSs). These RbMSs are surrounded by a N-rich environment in which Cr(3+) ions exhibit luminescent features not present in other Cr(3+)-containing systems such as ruby, emerald or alexandrite. The light emissions shown by the RbMSs and surroundings were investigated according to the Cr concentration and temperature of measurement, allowing the identification of several Cr(3+)-related luminescent lines. The main characteristics of these luminescent lines and corresponding excitation-recombination processes are presented and discussed in view of a detailed spectroscopic analysis.
Resumo:
Polycrystalline Eu(2+) and Dy(3+) doped barium aluminate materials, BaAl(2)O(4):Eu(2+),Dy(3+), were prepared with solid state reactions at temperatures between 700 and 1500 degrees C. The influence of the thermal treatments on the stability, homogeneity and structure as well as to the UV-excited and persistent luminescence of the materials was investigated by X-ray powder diffraction, SEM imaging and infrared spectroscopies as well as by steady state luminescence spectroscopy and persistent luminescence decay curves, respectively. The IR spectra of the materials prepared at 250, 700, and 1500 degrees C follow the formation of BaAl(2)O(4) composition whereas the X-ray powder diffraction of compounds revealed how the hexagonal structure was obtained. The morphology of the materials at high temperatures indicated important aggregation due to sintering. The luminescence decay of the quite narrow Eu(2+) band at ca. 500 nm shows the presence of persistent luminescence after UV irradiation. The dopant (Eu(2+)) and co-clopant (Dy(3+)) concentrations affect the crystallinity and luminescence properties of the materials. (C) 2009 Elsevier B.V. All rights reserved.