Inter- and intra-tester reliability of clinical measurement to determine medio-lateral patellar position using a pachymeter or visual assessment

The aim was to investigate inter-tester and intra-tester reliability and parallel reliability between a visual assessment method and a method using a pachymeter for locating the mid-point of the patella in determining the medial/lateral patella orientation. Fifteen asymptomatic subjects were assessed and the mid-point of the patella was determined by both methods on two separate occasions two weeks apart. Inter-tester reliability was obtained by ANOVA and by intraclass correlation coefficient (ICC); intra-tester reliability was obtained by a paired t-test and ICC; and parallel reliability was obtained by Pearson`s Correlation and ICC, for the measurement on the first and second evaluations. There was acceptable inter-tester agreement (p = 0.490) and reliability for the visual inspection (ICC = 0.747) and for the pachymeter (ICC = 0.716) at the second evaluation. The inter-tester reliability in the first evaluation was unacceptable (visual ICC = 0.604; pachymeter ICC = 0.612). Although there was statistical similarity between measurements for the first and second evaluations for all testers, intra-tester reliability was not acceptable for both methods: visual (examiner 1 ICC = 0.175; examiner 2 ICC = 0.189; examiner 3 ICC = 0.155) and pachymeter (examiner 1 ICC = 0.214; examiner 2 ICC = 0.246; examiner 3 ICC = 0.069). Parallel reliability gave a perfect correlation at the first evaluation (r=0.828; p<0.001) and at the second (r=0.756; p<0.001) and reliability was between acceptable and very good (ICC = [0.748-0.813]). Both visual and pachymeter methods provide reliable and similar medial/lateral patella orientation and are reliable between different examiners, but the results between the two assessments at 2 weeks` interval demonstrated an unacceptable reliability. (C) 2009 Elsevier B.V. All rights reserved.

Evaluation of superficial microhardness in dental enamel with different eruptive ages

This study evaluated the superficial microhardness of enamel in teeth at different posteruptive ages (before eruption in the oral cavity, 2-3 years after eruption, 4-10 years after eruption and more than 10 years after eruption). The study sample was composed of 134 specimens of human enamel. One fragment of each tooth was obtained from the flattest central portion of the crown to produce specimens with 3 x 3 mm. The enamel blocks were minimally flattened out and polished in order to obtain a flat surface parallel to the base, which is fundamental for microhardness testing. Microhardness was measured with a microhardness tester and a Knoop diamond indenter, under a static load of 25 g applied for 5 seconds. Comparison between the superficial microhardness obtained for the different groups was performed by analysis of Student's t test. The results demonstrated that superficial microhardness values have a tendency to increase over the years, with statistically significant difference only between unerupted enamel and that with more than 10 years after eruption. According to the present conditions and methodology, it was concluded that there were differences between the superficial micro-hardness of specimens at different eruptive ages, revealing an increasing mineralization. However, this difference was significant only between unerupted specimens and those with more than 10 years after eruption.

Impact and fracture resistance of an experimental acrylic polymer with elastomer in different proportions

The purpose of this study was to evaluate the impact and fracture resistance of acrylic resins: a heat-polymerized resin, a high-impact resin and an experimental polymethyl methacrylate with elastomer in different proportions (10, 20, 40 and 60%). 120 specimens were fabricated and submitted to conventional heat-polymerization. For impact test, a Charpy-type impact tester was used. Fracture resistance was assessed with a 3-point bending test by using a mechanical testing machine. Ten specimens were used for each test. Fracture (MPa) and impact resistance values (J.m-1) were submitted to ANOVA - Bonferroni's test - 5% significance level. Materials with higher amount of elastomer had statistically significant differences regarding to impact resistance (p < 0.05). Fracture resistance was superior (p < 0.01) for high-resistance acrylic resin. The increase in elastomer concentration added to polymethyl methacrylate raised the impact resistance and decreased the fracture resistance. Processing the material by injection decreased its resistance to impact and fracture.

Effect of different polishing systems on the surface roughness of microhybrid composites

The use of composite resins in dentistry is well accepted for restoring anterior and posterior teeth. Many polishing protocols have been evaluated for their effect on the surface roughness of restorative materials. This study compared the effect of different polishing systems on the surface roughness of microhybrid composites. Thirty-six specimens were prepared for each composite $#91;Charisma® (Heraeus Kulzer), Fill Magic® (Vigodent), TPH Spectrum® (Dentsply), Z100® (3M/ESPE) and Z250® (3M/ESPE)] and submitted to surface treatment with Enhance® and PoGo® (Dentsply) points, sequential Sof-Lex XT® aluminum oxide disks (3M/ESPE), and felt disks (TDV) combined with Excel® diamond polishing paste (TDV). Average surface roughness (Ra) was measured with a mechanical roughness tester. The data were analyzed by two-way ANOVA with repetition of the factorial design and the Tukey-Kramer test (p<0.01). The F-test result for treatments and resins was high (p<0.0001 for both), indicating that the effect of the treatment applied to the specimen surface and the effect of the type of resin on surface roughness was highly significant. Regarding the interaction between polishing system and type of resin used, a p value of 0.0002 was obtained, indicating a statistically significant difference. A Ra of 1.3663 was obtained for the Sof-Lex/TPH Spectrum interaction. In contrast, the Ra for the felt disk+paste/Z250 interactions was 0.1846. In conclusion, Sof-Lex polishing system produced a higher surface roughness on TPH Spectrum resin when compared to the other interactions.

Características agronômicas do Panicum maximum cv. "Mombaça" submetido a níveis crescentes de fósforo

O objetivo deste experimento foi avaliar o efeito da adição de doses crescentes de P2O5 sobre a altura do dossel, o número de perfilhos e a produção de matéria seca de folhas e de colmos do capim-Mombaça, em diferentes idades. Foi conduzido um experimento implantado em um Nitossolo Vermelho Eutrófico. O delineamento experimental usado foi o de blocos completos casualizados, com quatro repetições, cinco doses de P2O5 (30, 60, 90, 120 e 150kg ha-1) e uma testemunha. Para a primeira e segunda coletas, observou-se o efeito linear do fósforo sobre o perfilhamento. Para a terceira e quarta coletas, os dados ajustaram-se ao modelo quadrático. A participação das lâminas foliares na matéria seca da parte aérea diminuiu com as doses de P2O5. Por outro lado, a participação de colmos aumentou com as doses de P2O5. A produção de matéria seca (MS) da parte aérea para primeira, segunda e terceira coletas respondeu de forma linear à aplicação de P2O5 observando-se um aumento estimado de 7, 15 e 19kg ha-1 de MS por kg ha-1 de P2O5, respectivamente. Para a quarta coleta, os dados ajustaram-se ao modelo quadrático de regressão, sendo a máxima produção, 8,3Mg ha-1 de MS, obtida com a aplicação de 103kg ha-1 de P2O5.

TiAlN coatings deposited by triode magnetron sputtering varying the bias voltage

TiAlN films were deposited on AISI O1 tool steel using a triode magnetron sputtering system. The bias voltage effect on the composition, thickness, crystallography, microstructure, hardness and adhesion strength was investigated. The coatings thickness and elemental composition analyses were carried out using scanning electron microscopy (SEM) together with energy dispersive X-ray (EDS). The re-sputtering effect due to the high-energy ions bombardment on the film surface influenced the coatings thickness. The films crystallography was investigated using X-ray diffraction characterization. The X-ray diffraction (XRD) data show that TiAlN coatings were crystallized in the cubic NaCl B1 structure, with orientations in the {111}, {200} {220} and {311} crystallographic planes. The surface morphology (roughness and grain size) of TiAlN coatings was investigated by atomic force microscopy (AFM). By increasing the substrate bias voltage from -40 to -150 V, hardness decreased from 32 GPa to 19 GPa. Scratch tester was used for measuring the critical loads and for measuring the adhesion. (C) 2011 Elsevier B. V. All rights reserved.

Investigation of the Performance of the Disintegration Test for Dietary Supplements

The aim of this study was to investigate how beaker size, basket assembly, use of disk, and immersion medium impact the disintegration time of dietary supplements. The disintegration times were determined for five tablet and two capsule products. A two-station disintegration tester was used with Apparatus A or Apparatus B as described in the United States Pharmacopeia (USP) chapters, < 701 > and < 2040 >. Two beakers complying with the harmonized specifications were used, one with a volume of 1,000 mL and one with a 1,500-mL volume. The disintegration data were analyzed using ANOVA for the following factors: beaker size, equipment (App A and B) and condition (with/without disk). Two tablet products were not sensitive to any changes in the test conditions or equipment configurations. One product was only partially sensitive to the test conditions. The other products showed impact on the disintegration time for all test conditions. The results revealed that these tablet products might pass or fail current USP disintegration requirements depending on the equipment configuration. Similar results were obtained for the two investigated capsule formulations. One product might fail current USP disintegration requirements if the large beaker was used, but might pass the disintegration requirements when the small beaker was used. Hydroxy propyl methyl cellulose capsules were mostly influenced if sodium instead of a potassium buffer was used as the immersion medium. The results demonstrate that the current harmonized ICH specifications for the disintegration test are insufficient to make the disintegration test into reliable test for dietary supplements.

Effects of Ethanol on the Surface and Bulk Properties of a Microwave-Processed PMMA Denture Base Resin

Purpose: This study evaluated the effect of different concentrations of ethanol on hardness, roughness, flexural strength, and color stability of a denture base material using a microwave-processed acrylic resin as a model system. Materials and Methods: Sixty circular (14 x 4 mm) and 60 rectangular microwave-polymerized acrylic resin specimens (65 x 10 x 3 mm(3)) were employed in this study. The sample was divided into six groups according to the ethanol concentrations used in the immersion solution, as follows: 0% (water), 4.5%, 10%, 19%, 42%, and 100%. The specimens remained immersed for 30 days at 37 degrees C. The hardness test was performed by a hardness tester equipped with a Vickers diamond penetrator, and a surface roughness tester was used to measure the surface roughness of the specimens. Flexural strength testing was carried out on a universal testing machine. Color alterations (Delta E) were measured by a portable spectrophotometer after 12 and 30 days. Variables were analyzed by ANOVA/Tukey`s test (alpha = 0.05). Results: For the range of ethanol-water solutions for immersion (water only, 4.5%, 10%, 19.5%, 42%, and 100%), the following results were obtained for hardness (13.9 +/- 2.0, 12.1 +/- 0.7, 12.9 +/- 0.9, 11.2 +/- 1.5, 5.7 +/- 0.3, 2.7 +/- 0.5 VHN), roughness (0.13 +/- 0.01, 0.15 +/- 0.07, 0.13 +/- 0.05, 0.13 +/- 0.02, 0.23 +/- 0.05, 0.41 +/- 0.19 mu m), flexural strength (90 +/- 12, 103 +/- 18, 107 +/- 16, 90 +/- 25, 86 +/- 22, 8 +/- 2 MPa), and color (0.8 +/- 0.6, 0.8 +/- 0.3, 0.7 +/- 0.4, 0.9 +/- 0.3, 1.3 +/- 0.3, 3.9 +/- 1.5 Delta E) after 30 days. Conclusions: The findings of this study showed that the ethanol concentrations of tested drinks affect the physical properties of the investigated acrylic resin. An obvious plasticizing effect was found, which could lead to a lower in vivo durability associated with alcohol consumption.

Physical Properties of an Acrylic Resin after Incorporation of an Antimicrobial Monomer

Purpose: This study evaluated the effect of the incorporation of the antimicrobial monomer methacryloyloxyundecylpyridinium bromide (MUPB) on the hardness, roughness, flexural strength, and color stability of a denture base material. Materials and Methods: Ninety-six disk-shaped (14-mm diameter x 4-mm thick) and 30 rectangular (65 x 10 x 3.3 mm(3)) heat-polymerized acrylic resin specimens were divided into three groups according to the concentration of MUPB (w/w): (A) 0%, (B) 0.3%, (C) 0.6%. Hardness was assessed by a hardness tester equipped with a Vickers diamond penetrator. Flexural strength and surface roughness were tested on a universal testing machine and a surface roughness tester, respectively. Color alterations (Delta E) were measured by a portable spectrophotometer after 12 and 36 days of immersion in water, coffee, or wine. Variables were analyzed by ANOVA/Tukey HSD test (alpha = 0.05). Results: The following mean results (+/-SD) were obtained for hardness (A: 15.6 +/- 0.6, B: 14.6 +/- 1.7, C: 14.8 +/- 0.8 VHN; ANOVA: p = 0.061), flexural strength (A: 111 +/- 17, B: 105 +/- 12, C: 88 +/- 12 MPa; ANOVA: p = 0.008), and roughness (A: 0.20 +/- 0.11, B: 0.20 +/- 0.11, C: 0.24 +/- 0.08 mu m; ANOVA: p = 0.829). Color changes of immersed specimens were significantly influenced by solutions and time (A: 9.1 +/- 3.1, B: 14.8 +/- 7.5, C: 13.3 +/- 6.1 Delta E; ANOVA: p < 0.05). Conclusions: The incorporation of MUPB affects the mechanical properties of a denture base acrylic resin; however, the only significant change was observed for flexural strength and may not be critical. Color changes were slightly higher when resin containing MUPB was immersed in wine for a prolonged time; however, the difference has debatable clinical relevance.

Mycoflora and fumonisin contamination in Brazilian sorghum from sowing to harvest

BACKGROUND: The aim of this study was to characterise the mycoflora and the presence of fumonisin in sorghum grains, correlating the results with the environment and abiotic factors. RESULTS: Fifty samples (five collections of ten samples each) of sorghum were analysed. All samples were found to be contaminated with fungi, with higher frequencies of Cladosporium spp. (61.8%) and Helminthosporium spp. (33.4%). Fusarium verticillioides was isolated from 15.1% of the samples, with 38% of them being contaminated with fumonisin B(1) (FB(1)) at levels ranging from 50 to 368.78 ng g(-1). Regarding abiotic factors, temperature, water activity and rainfall showed a positive correlation with the frequency of F. verticillioides and FB(1) production. There was a significant positive correlation between relative air humidity and FB(1) production. The results obtained from sexual crosses between standard F mating tester strains and the isolated strains confirmed that the strains isolated were F. verticillioides. CONCLUSION: It can be concluded that the decrease in F. verticillioides and fumonisin contamination occurred owing to atypical climatic factors during the period of sorghum cultivation, when there was any occurrence of rain and the level of water activity of grains did not reach 0.58. (C) 2010 Society of Chemical Industry

Influence of light guide tip used in the photo-activation on degree of conversion and hardness of one nanofilled dental composite

The aim of this study was to evaluate the degree of conversion and hardness of a dental composite resin Filtek (TM) Z-350 (3M ESPE, Dental Products St. Paul, MN) photo-activated for 20 s of irradiation time with two different light guide tips, metal and polymer, coupled on blue LED Ultraled LCU (Dabi Atlante, SP, Brazil). With the metal light tip, power density was of 352 and with the polymer was of 456 mW/cm(2), respectively. Five samples (4 mm in diameter and 2mm in thickness-ISO 4049), were made for each Group evaluated. The measurements for DC (%) were made in a Nexus-470 FT-IR, Thermo Nicolet, E.U.A. Spectroscopy (FTIR). Spectra for both uncured and cured samples were analyzed using an accessory of reflectance diffuse. The measurements were recorded in absorbance operating under the following conditions: 32 scans, 4 cm(-1) resolution, 300-4000 cm(-1) wavelength. The percentage of unreacted carbon double bonds (% C=C) was determined from the ratio of absorbance intensities of aliphatic C=C (peak at 1637 cm(-1)) against internal standard before and after curing of the sample: aromatic C-C (peak at 1610 cm(-1)). The Vickers hardness measurements (top and bottom surfaces) were performed in a universal testing machine (Buehler MMT-3 digital microhardness tester Lake Bluff, Illinois USA). A 50 gf load was used and the indenter with a dwell time of 30 s. The data were submitted to the test t Student at significance level of 5%. The mean values of degree of conversion for the polymer and metal light guide tip no were statistically different (p = 0.8389). The hardness mean values were no statistically significant different among the light guide tips (p = 0.6244), however, there was difference between top and bottom surfaces (p < 0.001). The results show that so much the polymer light tip as the metal light tip can be used for the photo-activation, probably for the low quality of the light guide tip metal.