Study of electrochemical behavior of azoles for AISI 430 stainless steel in H(2)SO(4) 1 mol L(-1)

Corrosion is an undesirable process that occurs in metallic materials. Studied was the effect of inhibiting Benzotriazole (BTAH), Benzimidazole (BZM) and Indole in different concentrations-for the stainless steel (SS) AISI 430 in H(2)SO(4) mol The techniques employed this research were: anodic potenciostatic polarisation, electrochemical impedance spectroscopy, optical microscopy and scanning electron microscopy The curves of anodic polarisation showed that BTAH, BZM and Indol act as corrosion inhibitors for 430 SS, at concentrations of 1x10(-3) and 5x10(-4) mol L(-1) but do not inhibit corrosion for concentrations equal to or less than 1x10(-4) mol L(-1). The in-crease of the efficiency in relation to the inhibitory substances studied followed this order: Indol larization curve results were supported by electrochemical impedance spectroscopy, and microscopic analysis.

Electrochemical behavior of the cistein and diphosfonate for stainless steel in media of HCl 1 mol L(-1)

Amino acids and self assembled monolayers (SAM`s) have been studied as to their inhibiting action on the corrosion of metallic materials. The objective of work is to study the electrochemical behavior of the cisteincisteine, the diphosfonate and the mixture of both in inhibiting the action of corrosion on stainless steel 304 in HCl 1 molL(-1). As the following techniques were used: open circuit potential (OCP), potenciostatic anodic polarization (A P), chronoamperomeny (CA), electrochemical impedance spectroscopy (EIS) and optical microscopy (OM). The results of CA showed that cisteine has a double effect, catalytic and inhibiting, in function of the immersion time of the metallic part in the electrolytic solution. AP curves have shown lesser current density for the system containing cisteine diphosfonate suggesting an inhibiting synergic action. These results have been confirmed by EIS and OM.

Morphological analysis of pitting corrosion in AISI 310S austenitic stainless steel after salt spray exposition

This paper aims to study evolution of increase, distribution and classification of pits in 310S austenitic stainless steels obtained in the state as-received and heat-treated under different exposure times in saline. This work applicability has been based on a technique development for morphologic characterization of localized corrosion associated with description aspects of shapes, size and population-specific parameters. Methodology has been consisted in the following steps: specimens preparation, corrosion tests via salt spray in different conditions, microstructural analysis, pits profiles analysis and images analysis, digital processing and image analysis in order to characterize the pits distribution, morphology and size. Results obtained in digital processing and profiles image analysis have been subjected to statistical analysis using median as parameter in the alloy as received and treated. The alloy as received displays the following morphology: hemispheric pits> transition region A> transition region B> irregular> conic. The pits amount in the treated alloy at each exposure time is: transition region B> hemispherical> transition region A> conic> irregular.

Ion nitriding of a superaustenitic stainless steel: Wear and corrosion characterization

The superiority of superaustenitic stainless steel (SASS) lies in its good weldability and great resistance to stress corrosion and pitting, because of its higher chromium, molybdenum, and nitrogen contents, when compared to general stainless steels. However, some of its applications are limited by very poor wear behavior. Plasma-nitriding is a very effective treatment for producing wear resistant and hard surface layers on stainless steels without compromising the corrosion resistance. In this work, UNS S31254 SASS samples were plasma-nitrided at three different temperatures (400, 450, and 500 degrees C), under a pressure of 500 Pa, for 5 h, in order to verify the influence of the temperature on the morphology, wear, and corrosion behavior of the modified surface layers. The plasma-nitrided samples were analyzed by means of optical microscopy, micro-hardness. X-ray diffraction, wear, and corrosion tests. Wear tests were conducted in a fixed ball micro-wear machine and corrosion behavior was carried out in natural sea water by means of potentiodynamic polarization curves. For the sample which was plasma-nitrided at 400 degrees C, only the expanded austenite phase was observed, and for the treatments performed at 450 and 500 degrees C, chromium nitrides (CrN and Cr(2)N) were formed in addition to the expanded austenite. Wear volume and Knoop surface hardness increased as the plasma-nitriding temperature increased. Higher wear rates were observed at high temperatures, probably due to the increment on layer fragility. The sample modified at 400 degrees C exhibited the best corrosion behavior among all the plasma-nitriding conditions. (C) 2010 Elsevier B.V. All rights reserved.

Evaluation of austenitic-ferritic stainless steel wires for orthodontic applications

Several studies have shown that austenitic stainless steels are suitable for use in the final phases of orthodontic treatments, such as finishing and retention. These steels demonstrate appropriate mechanical properties, such as high ultimate tensile strength and good corrosion resistance. A new class of materials, the austenic-ferritic stainless steels, is substituting for austenitic stainless steels in several industrial applications where these properties are necessary. This work supports the hypothesis that orthodontic wires of austenic-ferritic stainless steels can replace austenitic stainless steels. The advantages are cost reduction and decrease of the nickel hypersensitivity effect in patients undergoing orthodontic treatments. The object of this study was to evaluate wires of austenitic-ferritic stainless steel SEW 410 Nr. 14517 (Cr26Ni6Mo3Cu3) produced by cold working through rolling and drawing processes. Tests were performed to evaluate the ultimate tensile strength, hardness, ductility, and formability. In accordance with technical standards the wires exhibited ultimate tensile strength and ductility suitable for orthodontic clinical applications. These austenitie-ferritic wires can be an alternative to substitute the common commercial wires of austenic stainless steels with the advantage of decreasing the nickel content.

Bending fatigue of stainless steel shear pins belonging to a hydroelectric plant

Coaracy Nunes was the first hydroelectric power plant in the Amazon region, being located in Araguari River, Amapa State, Brazil. The plant operates since 1976, presenting now a nominal capacity of 78 MW. The shear pins, which are installed in the turbine hydraulic arms to control the wicket gate and regulate the water flow into the turbine blades, suffered several breakdowns since 2004. These shear pins are made of an ASTM 410 stainless steel and were designed to break by a shear overload of 120 kN. Fractographic investigation of the pins, however, revealed two types of fracture topographies: a region of stable crack propagation area, with non-pronounced striation and secondary cracks; and a region of unstable propagation, featuring elongated dimples. These results indicated that the stable crack propagation occurred by fatigue (bidirectional bending), which was nucleated at machining marks under high nominal load. Finite element analysis was carried out using two loading conditions (pure shear and a combination of shear and bending) and the results indicated that the presence of a bending stress strongly increased the stress concentration factor (85% rise in the shear stress and 130% rise in the Von Mises stress). Misalignment during shear pins assembly associated with vibration might have promoted the premature failure of the shear by bending fatigue. (C) 2008 Elsevier Ltd. All rights reserved.

Use of SECM to study the electrochemical behavior of DIN 1.4575 superferritic stainless steel aged at 475 degrees C

In order to lower the excessive costs of metallic prosthesis materia Is alternatives to Ti and Ti alloys have been searched. in this study, the corrosion resistance of the DIN 1.4575 superferritic stainless steel, either solution annealed or solution annealed and aged at 475 degrees C for periods varying from 100 to 1080 h, was investigated by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization methods in Hanks` solution. The solution annealed and the aged for 1080 h samples were also tested using scanning electrochemical microscopy (SECM) in a 0.1 mol/L NaCl solution at 25 degrees C. The EIS results showed that the corrosion resistance of the DIN 1.4575 steel decreases with heat treatment time at 475 degrees C probably due to alpha prime formation. Besides the diminution of the overall impedance values, the low frequency limit of the Nyquist diagrams show a progressive change from an almost capacitive response to a resistive behavior as the heat treatment time increases. Pitting corrosion resistance also decreased with aging time at 475 degrees C.

Lactobacillus sakei 1 and its bacteriocin influence adhesion of Listeria monocytogenes on stainless steel surface

Listeria monocytogenes is of particular concern for the food industry due to its psychrotolerant and ubiquitous nature. In this work, the ability of L monocytogenes culturable cells to adhere to stainless steel coupons was studied in co-culture with the bacteriocin-producing food isolate Lactobacillus sakei 1 as well as in the presence of the cell-free neutralized supernatant of L sakei 1 (CFSN-S1) containing sakacin 1. Results were compared with counts obtained using a non bacteriocin-producing strain (L sakei ATCC 15521) and its bacteriocin free supernatant (CFSN-SA). Culturable adherent L monocytogenes and lactobacilli cells were enumerated respectively on PALCAM and MRS agars at 3-h intervals for up to 12 h and after 24 and 48 h of incubation. Bacteriocin activity was evaluated by critical dilution method. After 6 h of incubation, the number of adhered L monocytogenes cells in pure culture increased from 3.8 to 5.3 log CFU/cm(2) (48h). Co-culture with L sakei 1 decreased the number of adhered L monocytogenes cells (P < 0.001) during all sampling times with counts lower than 3.0 log CFU/cm(2). The CFNS-S1 also led to a significant and similar reduction in culturable adhered L. monocytogenes counts for up to 24 h of incubation, however after 48 h of incubation, re-growth of L monocytogenes number of adhered cells was observed, likely due to lack of competition for nutrients. L sakei ATCC 15521 or its supernatant (CFNS-SA) did not reduce the number of adhered L monocytogenes cells on stainless steel surface and from 6 h of incubation, listerial counts were between 4.3 and 4.5 log CFU/cm(2). These results indicate that L sakei 1 and its bacteriocin sakacin 1 may be useful to inhibit early stages of L monocytogenes adherence to abiotic surface. (C) 2011 Elsevier Ltd. All rights reserved.

The influence of albumin on the anodic dissolution of chromium present in UNSS31254 stainless steel in chloride environment

The influence of bovine serum albumin (BSA) on the anodic dissolution of chromium present in UNS S31254 stainless steel (SS) in 0.15 mol L-1 NaCl at 37.0 +/- 0.5 degrees C has been studied, using anodic potentiostatic polarization curves and optical emission spectroscopy. Electrochemical results have shown that BSA has little effect on the transpassivation potential (E-T) and on the passivation current density values. However on the passivation range, BSA diminishes the intensity of the anodic wave seen at about E=750mV versus SCE attributed to Cr(III)/Cr(VI) oxidation. Optical emission spectroscopy results have shown that BSA prevents the anodic dissolution of chromium to occur and minimizes iron dissolution above the transpassivation potential (E=1160 mV versus SCE). (C) 2007 Elsevier B.V. All rights reserved.

The corrosion of austenitic 304 stainless steel in biodiesel

Fuel distribution uses 304 stainless steel containers for the storage of biofuels, however there are few reports in the literature about the corrosive aspects this. steel in biodiesel. The objective of this research is to study the corrosive behavior of 304 austenitic stainless steel in the presence of biodiesel, unwashed and washed, with aqueous solutions of citric, oxalic, acetic and ascorbic acids 0,01 mol L(-1), and compare with results obtained for the copper (ASTM D130). The employedtechniques were: atomic absorption spectrometry (AAS) and optical microscopy (OM). The results of EA A showed a low rate of corrosion for the stainless steel, the alloys elements studied were Cr, Ni and Fe, the highest rate was observed for the chrome, 1.78 ppm / day in biodiesel with or without washing. The OM of the 304 steel, when compared with that of copper has a low corrosion rate in the 304 steel/biodiesel system. Not with standing, this demonstrates that not only the 304 steel, but also the copper corrodes in biodiesel

Influence of chloride ion concentration and temperature on the electrochemical properties of passive films formed on a superduplex stainless steel

Polarization measurements were conducted to monitor the corrosion behavior of superduplex stainless steel ASTM A995M-Gr.SA/EN 10283-Mat#1.4469(GX2CrNiMo26-7-4) when exposed to a) an electrolyte containing 22,700 parts per million (ppm) of chloride ions at seven different temperatures and b) an electrolyte at 25 GC and different chloride ion concentrations (5800, 22,700, 58,000 and 80,000 ppm of Cl(-)). The polarization curves indicate that the passive films formed are only slightly affected by NaCl concentration, but the pitting potential decreases drastically increasing the temperature, in particular >60 degrees C. The image analysis of the microstructure after potentiodynamic polarization showed that the pitting number and size vary in function of the temperature of the tested medium. Nyquist diagrams were determined by electrochemical impedance spectroscopy to characterize the resistance of the passive layer. According to Nyquist plots, the arc polarization resistance decreases increasing the temperature due to a catalytic degradation of the oxide passive films. (C) 2009 Elsevier Inc. All rights reserved.

Quality of martensitic stainless steel type AISI-420 utilized in the manufacture surgical implements

Until now the martensitic stainless steel type AISI-420 is widely used in the manufacture of surgical implements. These implements present premature corrosion problems identified after cleaning, sterilization and cutting edge loss and/or rupture during the surgical processes.. This study evaluates the steel as to the chemical composition, hardness, microstructure and pitting corrosion resistance in a solution of enzyme detergent diluted in water by anodic cyclic polarization. This mixture is used in the cleaning of surgical implements that are submerged in this solution for 2 h before cleaning and sterilization. The results show steels with martensite microstructures in the ferrite phase, together with impurities. These presented low pitting potential values in compariston to steels with a fully martensitic microstructure.

Sigma phase morphologies in cast and aged super duplex stainless steel

Solution annealed and water quenched duplex and super duplex stainless steels are thermodynamically metastable systems at room temperature. These systems do not migrate spontaneously to a thermodynamically stable condition because an energy barrier separates the metastable and stable states. However, any heat input they receive, for example through isothermal treatment or through prolonged exposure to a voltaic arc in the welding process, cause them to reach a condition of stable equilibrium which, for super duplex stainless steels, means precipitation of intermetallic and carbide phases. These phases include the sigma phase, which is easily identified from its morphology, and its influence on the material`s impact strength. The purpose of this work was to ascertain how 2-hour isothermal heat treatments at 920 degrees C and 980 degrees C affect the microstructure of ASTM A890/A890M GR 6A super duplex stainless steel. The sigma phase morphologies were found to be influenced by these two aging temperatures, with the material showing a predominantly lacy microstructure when heat treated at 920 degrees C and block-shaped when heat treated at 980 degrees C. (C) 2009 Elsevier Inc. All rights reserved.

Microstructural characteristics and corrosion behavior of a super duplex stainless steel casting

The machining of super duplex stainless steel castings is usually complicated by the difficulty involved in maintaining the dimensional tolerances required for given applications. Internal stresses originating from the solidification process and from subsequent heat treatments reach levels that exceed the material`s yield strength, promoting plastic strain. Stress relief heat treatments at 520 degrees C for 2 h are an interesting option to solve this problem, but because these materials present a thermodynamically metastable condition, a few precautions should be taken. The main objective of this work was to demonstrate that, after solution annealing at 1130 degrees C and water quenching, stress relief at 520 degrees C for 2 h did not alter the duplex microstructure or impair the pitting corrosion resistance of ASTM A890/A890M Grade 6A steel. This finding was confirmed by microstructural characterization techniques, including light optical and scanning electron microscopy, and X-ray diffraction. Corrosion potential measurements in synthetic sea water containing 20,000 ppm of chloride ions were also conducted at three temperatures: 5 degrees C, 25 degrees C and 60 degrees C. (c) 2008 Elsevier Inc. All rights reserved.

Ultrasound, eddy current and magnetic Barkhausen noise as tools for sigma phase detection on a UNS S31803 duplex stainless steel

Sigma phase is a deleterious one which can be formed in duplex stainless steels during heat treatment or welding. Aiming to accompany this transformation, ferrite and sigma percentage and hardness were measured on samples of a UNS S31803 duplex stainless steel submitted to heat treatment. These results were compared to measurements obtained from ultrasound and eddy current techniques, i.e., velocity and impedance, respectively. Additionally, backscattered signals produced by wave propagation were acquired during ultrasonic inspection as well as magnetic Barkhausen noise during magnetic inspection. Both signal types were processed via a combination of detrended-fluctuation analysis (DFA) and principal component analysis (PCA). The techniques used were proven to be sensitive to changes in samples related to sigma phase formation due to heat treatment. Furthermore, there is an advantage using these methods since they are nondestructive. (C) 2010 Elsevier B.V. All rights reserved.