Specific surface area and structures of aluminas from fibrillar pseudoboehmite

By heating powders of the aluminum monohydroxide fibrillar pseudoboehmite from 200 degrees C to 1400 degrees C several high surface area aluminas are prepared and characterized by X-ray diffraction and electron optical methods. Aqueous sols with pseudoboehmite fibrils of different lengths were dried by two methods: at room temperature and spray-dried. The following aluminas were obtained after treatment of the powders at increasing temperatures and having a range of specific surface areas: gamma-Al(2)O(3) (470 degrees C - 770 degrees C; 179 m(2)/g 497 m(2)/g); delta-Al(2)O(3) (770 degrees C - 930 degrees C; 156 m(2)/g - 230 m(2)/g); theta-Al(2)O(3) (930 degrees C - 1050 degrees C; 11 m(2)/g - 200 m(2)/g); alpha-Al(2)O(3) (1050 degrees C - 1400 degrees C; 2 m(2)/g - 17 m(2)/g). Spray-dried powders, fired at the same temperature than the ground powders, showed higher specific surface areas. The higher surface area alumina have values of the same order of magnitude of the commercial ""ad-cat"" aluminas.

Crystallization of nordstrandite in ethylene glycol water solutions: electron microscopic studies

The present work shows the growth of nordstrandile microcrystals observed by transmission and scanning electron microscopy. Nordstrandite was synthesised from non-crystalline aluminium hydroxide reacted in 20% ethylene glycol/water solution, at room temperature. This material was characterized by TEM, SEM, SAED, XRD and EDS/TEM, during six month and revealed the formation and growth of nordstrandite. Fibrillar pseudoboehmite is the only aluminium hydroxide which could be identified during the first two weeks. The nuclei grow, from complete dissolution/recrystallization of pseudoboehmite fibrils, into platy rectangular microscrystals of nordstrandite. Some tabular microcrystals recrystallise, forming after six months only the mufti-point nordstrandite stars. This electron-optical study suggest that the star shape results from the overlapping of rectangular plates, and pseudoboehmite fibrils act as the precursor of nordstrandite crystallisation in ethylene glycol/water solution.