Effect of power densities and irradiation times on the degree of conversion and temperature increase of a microhybrid dental composite resin

The different parameters used for the photoactivation process provide changes in the degree of conversion (DC%) and temperature rise (TR) of the composite resins. Thus, the purpose of this study was to evaluate the DC (%) and TR of the microhybrid composite resin photoactivated by a new generation LED. For the KBr pellet technique, the composite resin was placed into a metallic mould (1-mm thickness and 4-mm diameter) and photoactivated as follows: continuous LED LCU with different power density values (50-1000 mW/cm(2)). The measurements for the DC (%) were made in a FTIR Spectrometer Bomen (model MB-102, Quebec-Canada). The spectroscopy (FTIR) spectra for both uncured and cured samples were analyzed using an accessory for the diffuse reflectance. The measurements were recorded in the absorbance operating under the following conditions: 32 scans, 4-cm(-1) resolution, and a 300 to 4000-cm(-1) wavelength. The percentage of unreacted carbon-carbon double bonds (% C=C) was determined from the ratio of the absorbance intensities of aliphatic C=C (peak at 1638 cm(-1)) against an internal standard before and after the curing of the specimen: aromatic C-C (peak at 1608 cm-1). For the TR, the samples were made in a metallic mould (2-mm thickness and 4-mm diameter) and photoactivated during 5, 10, and 20 s. The thermocouple was attached to the multimeter to allow the temperature readings. The DC (%) and TR were calculated by the standard technique and submitted to ANOVA and Tukey`s test (p < 0.05). The degree of conversion values varied from 35.0 (+/- 1.3) to 45.0 (+/- 2.4) for 5 s, 45.0 (+/- 1.3) to 55.0 (+/- 2.4) for 10 s, and 47.0 (+/- 1.3) to 52.0 (+/- 2.4) for 20 s. For the TR, the values ranged from 0.3 (+/- 0.01) to 5.4 (+/- 0.11)degrees C for 5 s, from 0.5 (+/- 0.02) to 9.3 (+/- 0.28)degrees C for 10 s, and from 1.0 (+/- 0.06) to 15.0 (+/- 0.95)degrees C for 20 s. The power densities and irradiation times showed a significant effect on the degree of conversion and temperature rise.

PAIN IN FIBROMYALGIA AND DISCRIMINATIVE POWER OF THE INSTRUMENTS: VISUAL ANALOG SCALE, DOLORIMETRY AND THE MCGILL PAIN QUESTIONNAIRE

Objective: The aim of this study was to verify the discriminative power of the most widely used pain assessment instruments. Methods: The sample consisted of 279 subjects divided into Fibromyalgia Group (FM- 205 patients with fibromyalgia) and Control Group (CG-74 healthy subjects), mean age 49.29 +/- 10.76 years. Only 9 subjects were male, 6 in FM and 3 in CG. FM were outpatients from the Rheumatology Clinic of the University of Sao Paulo - Hospital das Clinicas (HCFMUSP); the CG included people accompanying patients and hospital staff with similar socio-demographic characteristics. Three instruments were used to assess pain: the McGill Pain Questionnaire (MPQ), the Visual Analog Scale (VAS), and the Dolorimetry, to measure pain threshold on tender points (generating the TP index). In order to assess the discriminative power of the instruments, the measurements obtained were submitted to descriptive analysis and inferential analysis using ROC Curve - sensibility (S), specificity (S I) and area under the curve (AUC) - and Contingence tables with Chi-square Test and odds ratio. Significance level was 0.05. Results: Higher sensibility, specificity and area under the curve was obtained by VAS (80%, 80% and 0.864, respectively), followed by Dolorimetry (S 77%, S177% and AUC 0.851), McGill Sensory (S 72%, S167% and AUC 0.765) and McGill Affective (S 69%, S1 67% and AUC 0.753). Conclusions: VAS presented the higher sensibility, specificity and AUC, showing the greatest discriminative power among the instruments. However, these values are considerably similar to those of Dolorimetry.

Room Temperature Ionic Liquid-Lithium Salt Mixtures: Optical Kerr Effect Dynamical Measurements

The addition of lithium salts to ionic liquids causes an increase in viscosity and a decrease in ionic mobility that hinders their possible application as an alternative solvent in lithium ion batteries. Optically heterodyne-detected optical Kerr effect spectroscopy was used to study the change in dynamics, principally orientational relaxation, caused by the addition of lithium bis(trifluoromethylsulfonyl)imide to the ionic liquid 1-buty1-3-methylimidazolium bis(trifluoromethylsulfonyl)imide. Over the time scales studied (1 ps-16 ns) for the pure ionic liquid, two temperature-independent power laws were observed: the intermediate power law (1 ps to similar to 1 ns), followed by the von Schweidler power law. The von Schweidler power law is followed by the final complete exponential relaxation, which is highly sensitive to temperature. The lithium salt concentration, however, was found to affect both power laws, and a discontinuity could be found in the trend observed for the intermediate power law when the concentration (mole fraction) of lithium salt is close to chi(LiTf(2)N) = 0.2. A mode coupling theory (MCT) schematic model was also used to fit the data for both the pure ionic liquid and the different salt concentration mixtures. It was found that dynamics in both types of liquids are described very well by MCT.