Protein Adsorption onto Polyelectrolyte Layers: Effects of Protein Hydrophobicity and Charge Anisotropy

Ellipsometry was used to investigate the influence of ionic strength (I) and pH on the adsorption of bovine serum albumin (BSA) or beta-lactoglobulin (BLG) onto preabsorbed layers of two polycations: poly(diallyldimethylammonium chloride) (PDADMAC) or poly(4-vinylpyridine bromide) quaternized with linear aliphatic chains of two (QPVP-C2) or five (QPVP-C5) carbons. Comparisons among results for the three polycations reveal hydrophobic interactions, while comparisons between BSA and BLG-proteins of very similar isoelectric points (pI)-indicate the importance of protein charge anisotropy. At pH close to pI, the ionic strength dependence of the adsorbed amount of protein (Gamma) displayed maxima in the range 10 < I < 25 mM corresponding to Debye lengths close to the protein radii. Visualization of protein charge by Delphi suggested that these ionic strength conditions corresponded to suppression of long-range repulsion between polycations and protein positive domains, without diminution of short-range attraction between polycation segments and locally negative protein domains, in a manner similar to the behavior of PE-protein complexes in solution.(1-4) This description was consistent with the disappearance of the maxima at pH either above or below pI. In the former case, Gamma values decrease exponentially with I(1/2), due to screening of attractions, while in the latter case adsorption of both proteins decreased at low I due to strong repulsion. Close to or below pI both proteins adsorbed more strongly onto QPVP-C5 than onto QPVP-C2 or PDADMAC due to hydrophobic interactions with the longer alkyl group. Above pI, the adsorption was more pronounced with PDADMAC because these chains may assume more loosely bound layers due to lower linear charge density.

Lysozyme binding to poly(4-vinyl-N-alkylpyridinium bromide)

The adsorption behavior of polycations at ionic strengths (1) ranging from 0.001 to 0.1 onto silicon wafers was studied by means of ellipsometry, contact angle measurements and atomic force microscopy (AFM). Polycations chosen were bromide salts of poly(4-vinylpyridine) N-alkyl quaternized with linear aliphatic chains of 2 and 5 carbon atoms, QPVP-C2 and QPVP-C5, respectively. Under 1 0.001 the reduction of screening effects led to low adsorbed amounts of QPVP-C2 or QPVP-C5 (1.0 +/- 0.1 mg/m(2)), arising from the adsorption of extended chains. Upon increasing l to 0.1, screening effects led to conformational changes of polyelectrolyte chains ill Solution and to higher adsorbed amount values (1.9 +/- 0.2 mg/m(2)). Advancing contact angle theta(a) measurements performed with water drops onto QPVP-C2 and QPVP-C5 adsorbed layers varied from (45 +/- 2)degrees to (50 +/- 5)degrees, evidencing the exposure of both hydrophobic alkyl groups and charged moieties. The adsorption of lysozyme (LYZ) molecules to QPVP-C5 layers was more pronounced than to QPVP-C2 films. Antimicrobial effect of LYZ bound to QPVP-C2 or QPVP-C5 layers or to Si wafers was evaluated with enzymatic assays using Micrococcus luteus as Substrates. The adsorption behavior of QPVP-C2 and QPVP-C5 at the water-air interface was studied by means Of surface tension measurements. Only QPVP-C5 was able to reduce water Surface tension. Mixtures of LYZ and QPVP-C5 were more efficient in reducing Surface tension than pure LYZ solution, evidencing co-adsorption at liquid-air interface. Moreover, antimicrobial action observed for mixtures of LYZ and QPVP-C5 was more pronounced than that measured for pure LYZ. Hydrophobic interaction between LYZ and QPVP-C5 ill Solution seems to drive the binding and to preserve LYZ secondary structure. (c) 2008 Elsevier Inc. All rights reserved.