The direct determination of rare earth elements in basaltic and related rocks using ICP-MS: Testing the efficiency of microwave oven sample decomposition procedures

Tests are described showing the results obtained for the determination of REE and the trace elements Rb, Y, Zr, Nb, Cs, Ba, Hf, Ta, Pb, Th and U with ICP-MS methodology for nine basaltic reference materials, and thirteen basalts and amphibolites from the mafic-ultramafic Niquelandia Complex, central Brazil. Sample decomposition for the reference materials was performed by microwave oven digestion (HF and HNO(3), 100 mg of sample), and that for the Niquelandia samples also by Parr bomb treatment (5 days at 200 degrees C, 40 mg of sample). Results for the reference materials were similar to published values, thus showing that the microwave technique can be used with confidence for basaltic rocks. No fluoride precipitates were observed in the microwave-digested solutions. Total recovery of elements, including Zr and Hf, was obtained for the Niquelandia samples, with the exception of an amphibolite. For this latter sample, the Parr method achieved a total digestion, but not so the microwave decomposition; losses, however, were observed only for Zr and Hf, indicating difficulty in dissolving Zr-bearing minerals by microwave acid attack.

A method for Ca, Fe, Ga, Na, Si and Zn determination in alumina by inductively coupled plasma optical emission spectrometry after aluminum precipitation

In this present work a method for the determination of Ca, Fe, Ga, Na, Si and Zn in alumina (Al(2)O(3)) by inductively coupled plasma optical emission spectrometry (ICP OES) with axial viewing is presented. Preliminary studies revealed intense aluminum spectral interference over the majority of elements and reaction between aluminum and quartz to form aluminosilicate, reducing drastically the lifetime of the torch. To overcome these problems alumina samples (250 mg) were dissolved with 5 mL HCl + 1.5 mLH(2)SO(4) + 1.5 mL H(2)O in a microwave oven. After complete dissolution the volume was completed to 20 mL and aluminum was precipitated as Al(OH)(3) with NH(3) (by bubbling NH(3) into the solution up to a pH similar to 8, for 10 min). The use of internal standards (Fe/Be, Ga/Dy, Zn/In and Na/Sc) was essential to obtain precise and accurate results. The reliability of the proposed method was checked by analysis of alumina certified reference material (Alumina Reduction Grade-699, NIST). The found concentrations (0.037%w(-1) CaO, 0.013% w w(-1) Fe(2)O(3), 0.012%w w(-1)Ga(2)O(3), 0.49% w w(-1) Na(2)O, 0.014% w w(-1) SiO(2) and 0.013% w w(-1) ZnO) presented no statistical differences compared to the certified values at a 95% confidence level. (C) 2011 Elsevier B.V. All rights reserved.