This study aimed to evaluate the efficacy of SmearClear (SybronEndo, Orange, CA) and EDTA for smear layer removal from root canals of permanent teeth after instrumentation. Thirty extracted human permanent teeth (n = 10) were randomly assigned to the following groups: group 1 = 14.3% EDTA, group 2 = SmearClear, and group 3 = no smear layer removal procedure was undertaken (control). The specimens were submitted to scanning electron microscopy analysis. Magnifications of 200x and 750x were used to evaluate cleaning at the apical, middle, and cervical thirds according to a three-point scoring system. Data were analyzed statistically by the Mann-Whitney U test (5% significance level). Groups 1 and 2 differed significantly from group 3 (p < 0.01). However, there was no statistically significant difference (p > 0.05) between groups 1 and 2. In conclusion, SmearClear was able to remove the smear layer from the root canals of permanent teeth similarly as 14.3% EDTA, suggesting that both solutions may be indicated for such purpose. (J Endod 2008,34:1541-1544)

Crystallization of nordstrandite in ethylene glycol water solutions: electron microscopic studies

The present work shows the growth of nordstrandile microcrystals observed by transmission and scanning electron microscopy. Nordstrandite was synthesised from non-crystalline aluminium hydroxide reacted in 20% ethylene glycol/water solution, at room temperature. This material was characterized by TEM, SEM, SAED, XRD and EDS/TEM, during six month and revealed the formation and growth of nordstrandite. Fibrillar pseudoboehmite is the only aluminium hydroxide which could be identified during the first two weeks. The nuclei grow, from complete dissolution/recrystallization of pseudoboehmite fibrils, into platy rectangular microscrystals of nordstrandite. Some tabular microcrystals recrystallise, forming after six months only the mufti-point nordstrandite stars. This electron-optical study suggest that the star shape results from the overlapping of rectangular plates, and pseudoboehmite fibrils act as the precursor of nordstrandite crystallisation in ethylene glycol/water solution.