Feasibility of using in situ fusion for the determination of Co, Cr and Mn in Portland cement by direct solid sampling graphite furnace atomic absorption spectrometry

In situ fusion on the boat-type graphite platform has been used as a sample pretreatment for the direct determination of Co, Cr and Mn in Portland cement by solid sampling graphite furnace atomic absorption spectrometry (SS-GF AAS). The 3-field Zeeman technique was adopted for background correction to decrease the sensitivity during measurements. This strategy allowed working with up to 200 mu g of sample. The in situ fusion was accomplished using 10 mu L of a flux mixture 4.0% m/v Na(2)CO(3) + 4.0% m/v ZnO + 0.1% m/v Triton (R) X-100 added over the cement sample and heated at 800 degrees C for 20 s. The resulting mould was completely dissolved with 10 mu L of 0.1% m/v HNO(3). Limits of detection were 0.11 mu g g(-1) for Co, 1.1 mu g g(-1) for Cr and 1.9 mu g g(-1) for Mn. The accuracy of the proposed method has been evaluated by the analysis of certified reference materials. The values found presented no statistically significant differences compared to the certified values (Student`s t-test, p<0.05). In general, the relative standard deviation was lower than 12% (n = 5). (C) 2009 Elsevier B.V. All rights reserved.

Feasibility study for the preparation of a tuna fish candidate reference material for total As determination

This work describes the evaluation of several parameters for the preparation of a tuna fish candidate as a reference material (RM) in order to measure the total As mass fraction by slurry sampling graphite furnace atomic absorption spectrometry (SLS-GF AAS) and slurry sampling hydride generation atomic absorption spectrometry (SLS-HG AAS). The main parameters investigated were the homogeneity, analyte segregation and composition during material production. For candidate RM preparation, tuna fish was collected at a local market, cleaned, freeze-dried and treated using different procedures as follows: (1) ground in a cutting mill and separated in different particle sizes (2) ground in cryogenic mill. The mass fraction of As in the cryogenically ground sample was (4.77 +/- A 0.19) mu g g(-1) for SLS-GF AAS and (4.61 +/- A 0.34) mu g g(-1) for SLS-HG AAS. The accuracy of the procedures was checked with tuna fish certified reference material (BCR 627) with recoveries of 102 and 94% for SLS-GF AAS and SLS-HG AAS, respectively. The homogeneity factor was calculated for different pretreatment procedures and for particle sizes in the range of 500-150 mu g, indicating good homogeneity, except for raw fish. There was no observed analyte segregation and no losses, no contamination and no changes in the microdistribution of material during preparation.