Dielectric properties and physical features of phosphate glasses containing iron oxide

Microwave techniques were applied to the study of dielectric properties of phosphate glasses on the basis of contributions from permanent and induced dipolar polarization of local structural units interacting with the electrical component of the electromagnetic radiation. The dielectric constant of the selected glass system (100-x)(50P(2)O(5)center dot 25Li(2)O center dot 25Na(2)O)center dot xFe(2)O(3), where 0 <= x <= 21 is in mol%, was measured using a microwave setup assembled to measure the phase shift of the standing wave pattern produced by the insertion of the sample. It is shown that the Fe2+ ions contribute effectively to the dielectric constant, as expected from the interactions of the dipoles of the local charge compensation pairs with the microwave radiation. However, there is the possibility of occurrence of some ions Fe3+, in general, at low iron content, which reinforces the glass structure and, therefore, decreases the dielectric constant. There is a gradual conversion from Fe3+ to Fe2+ as the iron ions increases. This is possibly the reason of the anomaly in the dielectric constant values observed in the results. These assumptions can be checked by results of electronic paramagnetic resonance (EPR) and optical absorption (OA). The dielectric constant of the glasses studied in this work was found to increase with the temperature in the range of 25-330 degrees C. (C) 2007 Elsevier B.V. All rights reserved.

On the pH dependence of electroactivity of poly(methylene blue) films

The electrochemical behavior of poly(methylene blue) on different electrodes has been investigated by electrochemical quartz crystal microbalance and in situ spectrophotometric measurements coupled to cyclic voltammetry. Polymeric films were obtained potentiodynamically and the charge transport mechanism was analyzed. The electrochemical results show that polymer electroactivity depends not only on pH but also on the substrate. Charge compensation changes with both pH and the size of the anions showing a transition in the pH range of polymer pKa. It was demonstrated by spectroelectrochemical experiments that the electroactivity of the film depends on the radical/radical cation equilibrium. The potentials where the most electroactive species are formed have been determined. (C) 2009 Elsevier Ltd. All rights reserved.

Optical energy storage properties of Sr(2)MgSi(2)O(7):Eu(2+),R(3+) persistent luminescence materials

The details of the mechanism of persistent luminescence were probed by investigating the trap level structure of Sr(2)MgSi(2)O(7):Eu(2+),R(3+) materials (R: Y, La-Lu, excluding Pm and Eu) with thermoluminescence (TL) measurements and Density Functional Theory (DFT) calculations. The TL results indicated that the shallowest traps for each Sr(2)MgSi(2)O(7):Eu(2+),R(3+) material above room temperature were always ca. 0.7 eV corresponding to a strong TL maximum at ca. 90 A degrees C. This main trap energy was only slightly modified by the different co-dopants, which, in contrast, had a significant effect on the depths of the deeper traps. The combined results of the trap level energies obtained from the experimental data and DFT calculations suggest that the main trap responsible for the persistent luminescence of the Sr(2)MgSi(2)O(7):Eu(2+),R(3+) materials is created by charge compensation lattice defects, identified tentatively as oxygen vacancies, induced by the R(3+) co-dopants.

Electrostatic layer-by-layer deposition and electrochemical characterization of thin films composed of MnO(2) nanoparticles in a room-temperature ionic liquid

Thin films of MnO(2) nanoparticles were grown using the layer-by-layer method with poly (diallyldimetylammonium) as the intercalated layer. The film growth was followed by UV-vis, electrochemical quartz crystal microbalance (EQCM), and atomic force microscopy. Linear growth due to electrostatic immobilization of layers was observed up to 30 bilayers, but electrical connectivity was maintained only for 12 MnO(2)/PPDA bilayers. The electrochemical characterization of this film in 1-butyl-2,3-dimethyl-imidazolium (BMMI) bis(trifluoromethanesulfonyl)imide (TFSI) (BMMITFSI) with and without addition of a lithium salt indicated a higher electrochemical response of the nanostructured electrode in the lithium-containing electrolyte. On the basis of EQCM experiments, it was possible to confirm that the charge compensation process is achieved mainly by the TFSI anion at short times (<2 s) and by BMMI and lithium cations at longer times. The fact that large ions like TFSI and BMMI participate in the electroneutrality is attributed to the redox reaction that occurs at the superficial sites and to the high concentration of these species compared to that of lithium cations.