Biobased films prepared from NaOH/thiourea aqueous solution of chitosan and linter cellulose

In the present study, films based on linter cellulose and chitosan were prepared using an aqueous solution of sodium hydroxide (NaOH)/thiourea as the solvent system. The dissolution process of cellulose and chitosan in NaOH/thiourea aqueous solution was followed by the partial chain depolymerization of both biopolymers, which facilitates their solubilization. Biobased films with different chitosan/cellulose ratios were then elaborated by a casting method and subsequent solvent evaporation. They were characterized by X-ray analysis, scanning electron microscopy (SEM), atomic force microscopy (AFM), thermal analysis, and tests related to tensile strength and biodegradation properties. The SEM images of the biofilms with 50/50 and 60/40 ratio of chitosan/cellulose showed surfaces more wrinkled than the others. The AFM images indicated that higher the content of chitosan in the biobased composite film, higher is the average roughness value. It was inferred through thermal analysis that the thermal stability was affected by the presence of chitosan in the films; the initial temperature of decomposition was shifted to lower levels in the presence of chitosan. Results from the tests for tensile strength indicated that the blending of cellulose and chitosan improved the mechanical properties of the films and that an increase in chitosan content led to production of films with higher tensile strength and percentage of elongation. The degradation study in a simulated soil showed that the higher the crystallinity, the lower is the biodegradation rate.

Hydrolytic Activity of Free and Immobilized Cellulase

Cellulase is an enzymatic complex which synergically promotes the degradation of cellulose to glucose. The adsorption behavior of cellulase from Trichoderma reesei onto Si wafers or amino-terminated surfaces was investigated by means of ellipsometry and atomic force microscopy (AFM) as a function of temperature. Upon increasing temperature from (24 +/- 1) to (60 +/- 1) degrees C, adsorption of cellulase became faster and more pronounced and the mean roughness of cellulase adsorbed layers increased. In the case of cellulase adsorbed onto Si wafers, Arrhenius`s plot allowed us to estimate the adsorption energy as 24.2 kJ mol(-1). The hydrolytic activity of free cellulase and cellulase immobilized onto Si wafers was tested using cellulose dispersions as substrates. The incubation temperature ranged from (37 +/- 1) to (60 +/- 1) degrees C. The highest efficiency was observed at (60 +/- 1) degrees C. The amount of glucose produced by free cellulase was similar to 20% higher than that obtained from immobilized cellulase. However, immobilizing cellulase onto Si wafers proved to be advantageous because they could be reused six times while retaining their original activity level. Such an effect was attributed to surface hydration, which prevents enzyme denaturation. The hydrolytic activity of cellulase immobilized onto amino-terminated surfaces was slightly lower than that observed for cellulase adsorbed onto Si wafers, and reuse was not possible.

A physical organic chemistry approach to dissolution of cellulose: effects of cellulose mercerization on its properties and on the kinetics of its decrystallization

The effects of alkali treatment on the structural characteristics of cotton linters and sisal cellulose samples have been studied. Mercerization results in a decrease in the indices of crystallinity and the degrees of polymerization, and an increase in the alpha-cellulose contents of the samples. The relevance of the structural properties of cellulose to its dissolution is probed by studying the kinetics of cellulose decrystallization, prior to its solubilization in LiCl/N,N-dimethylacetamide (DMAc). Our data show that the decrystallization rate constants and activation parameters are only slightly dependent on the physico-chemical properties of the starting celluloses. This multi-step reaction is accompanied by a small enthalpy and large, negative, entropy of activation. These results are analyzed in terms of the interactions within the biopolymer chains during decrystallization, as well as those between the two ions of the electrolyte and both DMAc and cellulose.

Removal of Zn(2+) from Electroplating Wastewater Using Modified Wood Sawdust and Sugarcane Bagasse

This paper describes the preparation of new adsorbents derived from sugarcane bagasse and wood sawdust (Manilkara sp.) to remove zinc (II) ions from electroplating wastewater. The first part deals with the chemical modification of sugarcane bagasse and wood sawdust, using succinic anhydride to introduce carboxylic acid functions into the material. The obtained materials (modified sugarcane bagasse MB2 and modified wood sawdust MS2) were then characterized by infrared spectroscopy (IR) and used in adsorption experiments. The adsorption experiments evaluates Zn(2+) removal from aqueous single metal solution and real electroplating wastewater on both batch and continuous experiments using fixed-bed columns prepared in laboratorial scale with the obtained adsorbents. Adsorption isotherms were then developed using Langmuir model and the Thomas kinetic model. The calculated Zn(2+) adsorption capacities were found to be 145 mg/g for MS2 and 125 mg/g for MB2 in single metal aqueous solution, whereas for the industrial wastewater these values were 61 mg/g for MS2 and 55 mg/g for MB2.

Archaeological Mounds in Marajo Island in Northern Brazil: A Geological Perspective Integrating Remote Sensing and Sedimentology

Earthen mounds with archaeological artifacts have been well known in Marajo Island since the 19th century. Their documented dimensions are impressive, e.g., up to 20m high, and with areas large as 90 ha. The mounds, locally known as lesos, impose a significant. relief on the very low-lying landscape of this region, which averages 4 to 6 in above present. sea level. These features have been traditionally interpreted as artificial constructions of the Marajoara culture, designed for defense, cemetery purposes, or escape from flooding. Here, we provide sedimentological and geomorphological data that suggest an alternative origin for these structures that is more consistent with their monumental sizes. Rather than artificial, the Marajoara tesos seem to consist of natural morphological features related to late Pleistocene and Holocene fluvial, and possibly tidal-influenced, paleochannels and paleobars that became abandoned as depositional conditions changed through dine. Although utilized and modified by the Marajoara since at least 2000 years ago, these earthen mounds contain a significant non-anthropogenically modified sedimentary substratum. Therefore, the large Marajoara tesos are not entirely artificial. Ancient, Marajoara cultures took advantage of these natural, preexisting elevated surfaces to base their communities and develop their activities, locally increasing the sizes of these fluvial landforms. This alternative interpretation suggests less cumulative labor investment, in the construction of the mounds and might. have significant implications for reconstructing the organization of the Marajoara culture. (C) 2009 Wiley Periodicals, Inc.

Synthesis and Characterization of Magnetic Composites Based on Cis-Polyisoprene and CoFe(2)O(4) Nanoparticles

CoFe(2)O(4) nanoparticles were obtained by the co-precipitation method. They were further modified by the adsorption of ricinoleic acid (RA). The non-modified and modified CoFe(2)O(4)/RA nanoparticles were characterized by transmission electron microscopy (TEM), atomic force microscopy (AFM), Raman, and Fourier transform infrared (FTIR) spectroscopy. The modified particles present a mean diameter < 20 nm. The adsorption of RA on the CoFe(2)O(4) surface is characterized by the IR absorptions of the RA while in the Raman spectrum the predominant signals are those from the CoFe(2)O(4). The cis-polyisoprene (PI) composite was prepared by dissolving PI in cyclohexane followed by the addition of a magnetic fluid based on CoFe(2)O(4)/RA nanoparticles dispersed in cyclohexane. After solvent evaporation a magnetic composite was obtained and characterized by AFM, Raman, and FTIR measurements. AFM images show uniformly CoFe(2)O(4)/RA particles distributed in the PI matrix. Raman spectra obtained for the composites reveal the characteristic Raman peaks of PI and CoFe(2)O(4) nanoparticles.

Approximate solution of the autocatalytic hydrolysis of cellulose

Depolymerization of cellulose in homogeneous acidic medium is analyzed on the basis of autocatalytic model of hydrolysis with a positive feedback of acid production from the degraded biopolymer. The normalized number of scissions per cellulose chain, S(t)/nA degrees A = 1 - C(t)/C(0), follows a sigmoid behavior with reaction time t, and the cellulose concentration C(t) decreases exponentially with a linear and cubic time dependence, C(t) = C(0)exp[-at - bt (3)], where a and b are model parameters easier determined from data analysis.

Structural Investigation of MFe(2)O(4) (M = Fe, Co) Magnetic Fluids

Ferrites of the type M(II)Fe(2)O(4) (M = Fe and Co) have been prepared by the traditional coprecipitation method. These ferrites were modified by the adsorption of fatty acids derived from soybean and castor oil and were then dispersed in cyclohexane, providing very stable magnetic fluids, readily usable in nonpolar media. The structural properties of the ferrites and modified ferrites as well as the magnetic fluids were characterized by XRD (X-ray powder diffraction), TEM (transmission electron microscopy), DRIFTS (diffusion reflectance infrared Fourier transform spectroscopy), FTMR (Fourier transform near-infrared), UV-vis, normal Raman spectroscopy, and surface-enhanced Raman scattering (SERS). XRD and TEM analysis have shown that the magnetic nanoparticles (nonmodified and modified) present diameters in the range of 10-15 nm. DRIFTS measurements have shown that the carboxylate groups of soybean and castor oil fatty acids adsorb on the ferrite surface, forming three different structures: a bridging bidentate, a bridging monodentate, and a bidentate chelate structure. The FTIR and Raman spectra of nonmodified Fe(3)O(4) and CoFe(2)O(4) nanoparticles have shown that the number of observed phonons is not compatible with the expected O(h)(7) symmetry, since IR-only active phonons were observed. in the Raman spectra and vice versa. SERS measurements of a CoFe(2)O(4) thin film on a SERS-active gold electrode at different applied potentials made possible the assignment of the signals near 550 and 630 cm(-1) to Co-O motions and the signals near 470 and 680 cm(-1) to Fe-O motions.

Quenching of Photoactivity in Phthalocyanine Copper(II)-Titanate Nanotube Hybrid Systems

Titanate nanotubes (TiNTs) were obtained by hydrothermal treatment of anatase powder in aqueous NaOH solution and then modified with 2,9,16,23-tertracarboxyl phthalocyanine copper(H) (CuPc). This hybrid organic inorganic nanoscopic system was characterized by X-ray diffraction, microscopy, and spectroscopy. Transmission electron microscopy (TEM) images of pure and modified TiNTs revealed multiwall structures with an average outer diameter of 9 nm and a length of several hundred nanometers. The tubular morphology of the TiNTs was covered with CuPc-film. The amount of CuPc adsorbed onto the TiNTs was quantified by electron paramagnetic resonance (EPR). Using the same technique and spin-trapping methodology, the photogeneration of reactive oxygen species (ROS) from the TiNTs was systematically investigated. A drastic quenching of photoactivity was observed in the CuPc/TiNT hybrid system. Electron transfer from excited CuPc states to the TiNT conduction band followed by electron recombination may be the cause of this quenching.

Investigating the Nature of Noble Gas-Copper Bonds by the Quantum Theory of Atoms in Molecules

We investigated noble gas copper bonds in linear complexes represented by the NgCuX general formula in which Ng and X stand for a noble gas (neon, argon, krypton, or xenon) and a halogen (fluorine, chlorine or bromine), respectively, by coupled cluster methods and modified cc-pVQZ basis sets. The quantum theory of atoms in molecules (QTAIM) shows a linear relation between the dissociation energy or noble gas-copper bonds and the amount of electronic charge transferred mainly from the noble gas to copper during complexation. Large changes in the QTAIM quadrupole moments of copper and noble gases resulting from this bonding and a comparison between NgCuX and NgNaCl systems indicate that these noble gas-copper bonds should be better interpreted as predominantly covalent. Finally, QTAIM atomic dipoles of noble gases in NgNaCl systems agree satisfactorily with atomic dipoles given by a simple model for these NgNa van der Waals bonds.

Extrusion and characterization of functionalized cellulose whiskers reinforced polyethylene nanocomposites

The surface of ramie cellulose whiskers has been chemically modified by grafting organic acid chlorides presenting different lengths of the aliphatic chain by an esterification reaction. The occurrence of the chemical modification was evaluated by FTIR and X-ray photoelectron spectroscopies, elemental analysis and contact angle measurements. The crystallinity of the particles was not altered by the chain grafting, but it was shown that covalently grafted chains were able to crystallize at the cellulose surface when using C18. Both unmodified and functionalized nanoparticles were extruded with low density polyethylene to prepare nanocomposite materials. The homogeneity of the ensuing nanocomposites was found to increase with the length of the grafted chains. The thermomechanical properties of processed nanocomposites were studied by differential scanning calorimetry (DSC), dynamical mechanical analysis (DMA) and tensile tests. A significant improvement in terms of elongation at break was observed when sufficiently long chains were grafted on the surface of the nanoparticles. It was ascribed to improved dispersion of the nanoparticles within the LDPE matrix. (C) 2009 Elsevier Ltd. All rights reserved.