A hybrid material assembled by anthocyanins from acai fruit intercalated between niobium lamellar oxide

Organic-inorganic hybrid materials can be prepared dispersing organic species into well-defined inorganic nanoblocks. This paper describes the immobilization of natural dyes from the extract of the Brazilian acai-fruit into two types of layered hexaniobate precursors derived from H(2)K(2)Nb(6)O(17): (i) colloidal dispersion of niobate exfoliated nanoparticles and (ii) niobate pre-intercalated with tetraethylammonium cations (TEA(+)). The restacking of exfoliated particles in the presence of acai anthocyanins promotes their intercalation and produces stacked layers showing large basal spacing (ca. 50 angstrom). The TEA(+) pre-intercalated niobate provides particles with lower content of dye species than the exfoliated precursor but with higher degree of organization and regularity according to X-ray diffraction data and images obtained by electron microscopies. Vibrational (FTIR and Raman) and (13)C NMR spectroscopies indicate the presence of flavylium cations in the hybrid materials and spectral profiles characteristic of glycosylated anthocyanidins. According to thermal analysis results, the purplish hybrids materials are more stable than the free acai-dyes. One hybrid sample was heated under air up to 170 degrees C and maintained at this temperature for 240 min. No weight loss events were observed and the sample retained its original color, indicating that the intercalation of anthocyanin into hexaniobate increases its thermal stability. Considering the structural, chemical, optical and thermal properties of the synthesized hybrid materials, they might be good candidates to be investigated for future specialized applications.

Visible and near-infrared luminescent Eu(3+) or Er(3+) doped laponite-derived xerogels and thick films: Structural and spectroscopic properties

Laponite-derived materials represent promising materials for optical applications. In this work, Eu(3+)- or Er(3+)-doped laponite xerogels and films were prepared from colloidal dispersion. Homogeneous, crack-free and transparent single layers were deposited on soda-lime substrates with a thickness of 10 mu m. Structural and spectroscopic properties were analyzed by thermal analyses, X-ray diffractometry, transmission electron microscopy, infrared spectroscopy, and luminescence spectroscopy. The addition of a rare earth ion to the laponite does not promote any changes in thermal stability or phase transition. Laponite clay was identified after annealing up to 500 degrees C, with a decrease in basal spacing when the annealing temperature is changed from 100 degrees C to 500 degrees C. Enstatite polymorphs and amorphous silicate phases were observed after heat treatment at 700 degrees C and 900 degrees C. Stationary and time-dependent luminescence spectra in the visible region for Eu(3+), and (5)D(0) lifetime are discussed in terms of thermal treatment and structural evolution. In the layered host, the Eu(3+) ions are distributed in many different local environments. However, Eu(3+) ions were found to occupy at least two symmetry sites, and the ions are preferentially incorporated into the crystalline enstatite for the materials annealed at 700 degrees C and 900 degrees C. A (5)D(0) lifetime of 1.3 ms and 3.1 ms was obtained for Eu(3+) ions in an amorphous silicate and crystalline MgSiO(3) local environment, respectively. Strong Er(3+) emission at the 1550 nm region was observed for the materials annealed at 900 degrees C, with a bandwidth of 44 nm. (C) 2008 Elsevier B.V. All rights reserved.

Protein-polysaccharide viscoelastic matrices: synergic effects of amylose on lysozyme physical gelation in aqueous dimethylsulfoxide

A synergic effect of amylose on rheological characteristics of lysozyme physical gels evolved out of dimethylsulfoxide-water was verified and analyzed. The dynamics of the gels were experimentally approached by oscillatory rheology. The synergic effect was characterized by a decrease in the threshold DMSO volume fraction required for lysozyme gelation, and by a significant strengthening of the gel structure at over-critical solvent and protein concentrations. Drastic changes in the relaxation and creep curve patterns for systems in the presence of amylose were verified. Complex viscosity dependence on temperature was found to conform to an Arrhenius-like equation, allowing the determination of an activation energy term (Ea, apparent) for discrimination of gel rigidity. A dilatant effect was found to be induced by temperature on the flow behavior of lysozyme dispersions in DMSO-H(2)O in sub-critical conditions for gelation, which was greatly intensified by the presence of amylose in the samples. That transition was interpreted as reflecting a change from a predominant colloidal flow regime, where globular components are the prevailing structural elements, to a mainly fibrillar, polymeric flow behavior.

Colloidal Processing of Glass-Ceramics for Laminated Object Manufacturing

Green tapes of Li(2)O-ZrO(2)-SiO(2)-Al(2)O(3) (LZSA) parent glass were produced by aqueous tape casting as the starting material for the laminated object manufacturing (LOM) process. The rheological behavior of the powder suspensions in aqueous media, as well as the mechanical properties of the cast tapes, was evaluated. According to xi potential measurements, the LZSA glass powder particles showed acid surface characteristics and an IEP of around 4 when in aqueous media. The critical volume fraction of solids was about 72 wt% (27 vol%), which hindered the processability of more concentrated slurries. The glass particles also showed an anisometric profile, which contributed to an increase in the interactions between particles during flow. Therefore, the suspensions could not be processed at high solids loadings. Aqueous-based glass suspensions were also characterized by shear thickening after the addition of dispersants. Three slurry compositions were formulated, suitable green tapes were cast, and tapes were successfully laminated by LOM to a gear wheel geometry. A higher tensile strength of the green tapes corresponded to a higher tensile strength of the laminates. Thermal treatment was then applied to the laminates: pyrolysis at 525 degrees C, sintering at 700 degrees C for 1 h, and crystallization at 850 degrees C for 30 min. A 20% volumetric shrinkage was observed, but no surface flaws or inhomogeneous areas were detected. The sintered part maintained the curved edges and internal profile after heat treatment.

Aqueous two-phasemicellar systems in an oscillatory flowmicro-reactor: study of perspectives and experimental performance

BACKGROUND: Aqueous two-phase micellar systems (ATPMS) are micellar surfactant solutions with physical properties that make them very efficient for the extraction/concentration of biological products. In this work the main proposal that has been discussed is the possible applicability and importance of a novel oscillatory flow micro-reactor (micro-OFR) envisaged for parallel screening and/or development of industrial bioprocesses in ATPMS. Based on the technology of oscillatory flow mixing (OFM), this batch or continuous micro-reactor has been presented as a new small-scale alternative for biological or physical-chemical applications. RESULTS: ATPMS experiments were carried out in different OFM conditions (times, temperatures, oscillation frequencies and amplitudes) for the extraction of glucose-6-phosphate dehydrogenase (G6PD) in Triton X-114/buffer with Cibacron Blue as affinity ligand. CONCLUSION: The results suggest the potential use of OFR, considering this process a promising and new alternative for the purification or pre-concentration of bioproducts. Despite the applied homogenization and extraction conditions have presented no improvements in the partitioning selectivity of the target enzyme, when at rest temperature they have influenced the partitioning behavior in Triton X-114 ATPMS. (C) 2011 Society of Chemical Industry

Derivatives of Biomacromolecules as Stabilizers of Aqueous Alumina Suspensions

The stabilization of alumina suspensions is key to the development of high-performance materials for the ceramic industry, which has motivated extensive research into synthetic polymers used as stabilizers. In this study, mimosa tannin extract and a chitosan derivative, that is, macromolecules obtained from renewable resources, are shown to be promising to replace synthetic polymers, yielding less viscous suspensions with smaller particles and greater fluidity, that is, more homogeneous suspensions that may lead to better-quality products. The functional groups of tannin present in mimosa extract and N,N,N-trimethylchitosan (TMC) are capable of establishing interactions with the alumina surface, thus leading to repulsion between the particles mainly due to steric and electrosteric mechanisms, respectively. The stabilization of the suspension induced by either TMC or mimosa tannin was confirmed by a considerable decrease in viscosity and average particle size, in comparison with alumina suspensions without stabilizing agents. The viscosity/average particle size decreased by 49/84% and 52/87% for suspensions with TMC and mimosa tannin, respectively. In addition, the increase in the absolute zeta potential upon addition of either TMC or mimosa tannin extract, especially at high pHs, points to an increased stability of the suspension. The feasibility of using derivatives of macromolecules from renewable sources to stabilize aqueous alumina suspensions was therefore demonstrated. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 117: 58-66, 2010

Nanostructured thin films obtained by electrodeposition over a colloidal crystal template: applications in electrochemical devices

Colloidal particles have been used to template the electrosynthesis of several materials, such as semiconductors, metals and alloys. The method allows good control over the thickness of the resulting material by choosing the appropriate charge applied to the system, and it is able to produce high density deposited materials without shrinkage. These materials are a true model of the template structure and, due to the high surface areas obtained, are very promising for use in electrochemical applications. In the present work, the assembly of monodisperse polystyrene templates was conduced over gold, platinum and glassy carbon substrates in order to show the electrodeposition of an oxide, a conducting polymer and a hybrid inorganic-organic material with applications in the supercapacitor and sensor fields. The performances of the resulting nanostructured films have been compared with the analogue bulk material and the results achieved are depicted in this paper.

Characterization of aqueous silver nitrate solutions for leakage tests

OBJECTIVE: To determine the pH over a period of 168 h and the ionic silver content in various concentrations and post-preparation times of aqueous silver nitrate solutions. Also, the possible effects of these factors on microleakage test in adhesive/resin restorations in primary and permanent teeth were evaluated. MATERIAL AND METHODS: A digital pHmeter was used for measuring the pH of the solutions prepared with three types of water (purified, deionized or distilled) and three brands of silver nitrate salt (Merck, Synth or Cennabras) at 0, 1, 2, 24, 48, 72, 96 and 168 h after preparation, and storage in transparent or dark bottles. Ionic silver was assayed according to the post-preparation times (2, 24, 48, 72, 96, 168 h) and concentrations (1, 5, 25, 50%) of solutions by atomic emission spectrometry. For each sample of each condition, three readings were obtained for calculating the mean value. Class V cavities were prepared with enamel margins on primary and permanent teeth and restored with the adhesive systems OptiBond FL or OptiBond SOLO Plus SE and the composite resin Filtek Z-250. After nail polish coverage, the permanent teeth were immersed in 25% or 50% AgNO3 solution and the primary teeth in 5% or 50% AgNO3 solutions for microleakage evaluation. ANOVA and the Tukey's test were used for data analyses (α=5%). RESULTS: The mean pH of the solutions ranged from neutral to alkaline (7.9±2.2 to 11.8±0.9). Mean ionic silver content differed depending on the concentration of the solution (4.75±0.5 to 293±15.3 ppm). In the microleakage test, significant difference was only observed for the adhesive system factor (p=0.000). CONCLUSIONS: Under the tested experimental conditions and based on the obtained results, it may be concluded that the aqueous AgNO3 solutions: have neutral/alkaline pH and service life of up to 168 h; the level of ionic silver is proportional to the concentration of the solution; even at 5% concentration, the solutions were capable of indicating loss of marginal seal in the composite restorations; the 3-step conventional adhesive system had better performance regarding microleakage in enamel on primary and permanent teeth.

Yerba Maté (Ilex paraguariensis) aqueous extract decreases intestinal SGLT1 gene expression but does not affect other biochemical parameters in alloxan-diabetic wistar rats

Yerba mate´ (Ilex paraguariensis) is rich in polyphenols, especially chlorogenic acids. Evidence suggests that dietary polyphenols could play a role in glucose absorption and metabolism. The aim of this study was to evaluate the antidiabetic properties of yerba mate´ extract in alloxan-induced diabetic Wistar rats. Animals (n ) 41) were divided in four groups: nondiabetic control (NDC, n=11), and diabetic yerba maté (DY, n = 10). The intervention consisted in the administration of yerba mate´ extract in a 1 g extract/ kg body weight dose for 28 days; controls received saline solution only. There were no significant differences in serum glucose, insulin, and hepatic glucose-6-phosphatase activity between the groups that ingested yerba maté extract (NDY and DY) and the controls (NDC and DC). However, the intestinal SGLT1 gene expression was significantly lower in animals that received yerba maté both in upper (p = 0.007) and middle (p < 0.001) small intestine. These results indicate that bioactive compounds present in yerba maté might be capable of interfering in glucose absorption, by decreasing SGLT1 expression

Numerical comparison between conventional dispersion compensating fibers and photonic crystal fibers as lumped Raman amplifiers

In this paper we discuss the use of photonic crystal fibers (PCFs) as discrete devices for simultaneous wideband dispersion compensation and Raman amplification. The performance of the PCFs in terms of gain, ripple, optical signal-to-noise ratio (OSNR) and required fiber length for complete dispersion compensation is compared with conventional dispersion compensating fibers (DCFs). The main goal is to determine the minimum PCF loss beyond which its performance surpasses a state-of-the-art DCF and justifies practical use in telecommunication systems. (C) 2009 Optical Society of America

Electrochemical Reduction Using Glassy Carbon Electrode in Aqueous Medium of a Potential Anti-Chagas Drug: NFOH

Nitrofurazone (NF) presents activity against Chagas' disease, yet it has a high toxicity. Its analog, hydroxymethylnitrofurazone (NFOH), is more potent against Trypanosoma cruzi and much less toxic than the parent drug, NF. The electrochemical reduction of NFOH in an aqueous medium using a glassy carbon electrode (GCE) is presented. By cyclic voltammetry in anacidic medium, one irreversible reduction peak related to hydroxylamine derivative formation was registered, being linearly pH dependent. However, from pH > 7, a reversible reduction peak at a more positive potential appears and corresponds to the formation of a nitro radical anion. The radical-anion kinetic stability was evaluated by Ip(a)/Ip(c) the current ratio of the R-NO(2)/R-NO(2)-redox couple. The nitro radical anion decays with a second-order rate constant (k(2)) of 6.07, 2.06, and 1.44(X 10(3)) L mol(-1) s(-1) corresponding to pH 8.29, 9.29, and 10.2, respectively, with a corresponding half-time life (t(1/2)) of 0.33, 0.97, and 1.4 s for each pH value. By polishing the GCE surface with diamond powder and comparing with the GCE surface polished with alumina, it is shown that the presence of alumina affects the lifetime of the nitro radical anion. (C) 2009 The Electrochemical Society. [DOI: 10.1149/1.3130082] All rights reserved.

Characterization of new IS elements and studies of their dispersion in two subspecies of Leifsonia xyli

Background: Leifsonia xyli is a xylem-inhabiting bacterial species comprised of two subspecies: L. xyli subsp. xyli (Lxx) and L. xyli subsp. cynodontis (Lxc). Lxx is the causal agent of ratoon stunting disease in sugarcane commercial fields and Lxc colonizes the xylem of several grasses causing either mild or no symptoms of disease. The completely sequenced genome of Lxx provided insights into its biology and pathogenicity. Since IS elements are largely reported as an important source of bacterial genome diversification and nothing is known about their role in chromosome architecture of L. xyli, a comparative analysis of Lxc and Lxx elements was performed. Results: Sample sequencing of Lxc genome and comparative analysis with Lxx complete DNA sequence revealed a variable number of IS transposable elements acting upon genomic diversity. A detailed characterization of Lxc IS elements and a comparative review with IS elements of Lxx are presented. Each genome showed a unique set of elements although related to same IS families when considering features such as similarity among transposases, inverted and direct repeats, and element size. Most of the Lxc and Lxx IS families assigned were reported to maintain transposition at low levels using translation regulatory mechanisms, consistent with our in silico analysis. Some of the IS elements were found associated with rearrangements and specific regions of each genome. Differences were also found in the effect of IS elements upon insertion, although none of the elements were preferentially associated with gene disruption. A survey of transposases among genomes of Actinobacteria showed no correlation between phylogenetic relatedness and distribution of IS families. By using Southern hybridization, we suggested that diversification of Lxc isolates is also mediated by insertion sequences in probably recent events. Conclusion: Collectively our data indicate that transposable elements are involved in genome diversification of Lxc and Lxx. The IS elements were probably acquired after the divergence of the two subspecies and are associated with genome organization and gene contents. In addition to enhancing understanding of IS element dynamics in general, these data will contribute to our ongoing comparative analyses aimed at understanding the biological differences of the Lxc and Lxx.

Aqueous Extract of Brazilian Green Propolis: Primary Components, Evaluation of Inflammation and Wound Healing by Using Subcutaneous Implanted Sponges

Propolis is a chemically complex resinous bee product which has gained worldwide popularity as a means to improve health condition and prevent diseases. The main constituents of an aqueous extract of a sample of green propolis from Southeast Brazil were shown by high performance liquid chromatography/mass spectroscopy/mass spectroscopy to be mono- and di-O-caffeoylquinic acids; phenylpropanoids known as important constituents of alcohol extracts of green propolis, such as artepillin C and drupanin were also detected in low amounts in the aqueous extract. The anti-inflammatory activity of this extract was evaluated by determination of wound healing parameters. Female Swiss mice were implanted subcutaneously with polyesther-polyurethane sponge discs to induce wound healing responses, and administered orally with green propolis (500mg kg(-1)). At 4, 7 and 14 days post-implantation, the fibrovascular stroma and deposition of extracellular matrix were evaluated by histopathologic and morphometric analyses. In the propolis-treated group at Days 4 and 7 the inflammatory process in the sponge was reduced in comparison with control. A progressive increase in cell influx and collagen deposition was observed in control and propolis-treated groups during the whole period. However, these effects were attenuated in the propolis-treated group at Days 4 and 7, indicating that key factors of the wound healing process are modulated by propolis constituents.

Testing Evolutionary and Dispersion Scenarios for the Settlement of the New World

Background: Discussion surrounding the settlement of the New World has recently gained momentum with advances in molecular biology, archaeology and bioanthropology. Recent evidence from these diverse fields is found to support different colonization scenarios. The currently available genetic evidence suggests a ""single migration'' model, in which both early and later Native American groups derive from one expansion event into the continent. In contrast, the pronounced anatomical differences between early and late Native American populations have led others to propose more complex scenarios, involving separate colonization events of the New World and a distinct origin for these groups. Methodology/Principal Findings: Using large samples of Early American crania, we: 1) calculated the rate of morphological differentiation between Early and Late American samples under three different time divergence assumptions, and compared our findings to the predicted morphological differentiation under neutral conditions in each case; and 2) further tested three dispersal scenarios for the colonization of the New World by comparing the morphological distances among early and late Amerindians, East Asians, Australo-Melanesians and early modern humans from Asia to geographical distances associated with each dispersion model. Results indicate that the assumption of a last shared common ancestor outside the continent better explains the observed morphological differences between early and late American groups. This result is corroborated by our finding that a model comprising two Asian waves of migration coming through Bering into the Americas fits the cranial anatomical evidence best, especially when the effects of diversifying selection to climate are taken into account. Conclusions: We conclude that the morphological diversity documented through time in the New World is best accounted for by a model postulating two waves of human expansion into the continent originating in East Asia and entering through Beringia.

Theory of small-signal ac response of a dielectric liquid containing two groups of ions

The analysis of Macdonald for electrolytes is generalized to the case in which two groups of ions are present. We assume that the electrolyte can be considered as a dispersion of ions in a dielectric liquid, and that the ionic recombination can be neglected. We present the differential equations governing the ionic redistribution when the liquid is subjected to an external electric field, describing the simultaneous diffusion of the two groups of ions in the presence of their own space charge fields. We investigate the influence of the ions on the impedance spectroscopy of an electrolytic cell. In the analysis, we assume that each group of ions have equal mobility, the electrodes perfectly block and that the adsorption phenomena can be neglected. In this framework, it is shown that the real part of the electrical impedance of the cell has a frequency dependence presenting two plateaux, related to a type of ambipolar and free diffusion coefficients. The importance of the considered problem on the ionic characterization performed by means of the impedance spectroscopy technique was discussed. (c) 2008 American Institute of Physics.