Material properties and nondestructive evaluation of laminated veneer lumber (LVL) made from Pinus oocarpa and P. kesiya

This study aimed at evaluating the mechanical, physical and biological properties of laminated veneer lumber (LVL) made from Pinus oocarpa Schiede ex Schltdl (PO) and Pinus kesiya Royle ex Gordon (PK) and at providing a nondestructive characterization thereof. Four PO and four PK LVL boards from 22 randomly selected 2-mm thickness veneers were produced according to the following characteristics: phenol-formaldehyde (190 g/m(2)), hot-pressing at 150A degrees C for 45 min and 2.8 N/mm(2) of specific pressure. After board production, nondestructive evaluation was conducted, and stress wave velocity (v (0)) and dynamic modulus of elasticity (E (Md) ) were determined. The following mechanical and physical properties were then evaluated: static bending modulus of elasticity (E (M) ), modulus of rupture (f (M) ), compression strength parallel to grain (f (c,0)), shear strength parallel to glue-line (f (v,0)), shear strength perpendicular to glue-line (f (v,90)), thickness swelling (TS), water absorption (WA), and permanent thickness swelling (PTS) for 2, 24, and 96-hour of water immersion. Biological property was also evaluated by measuring the weight loss by Trametes versicolor (Linnaeus ex Fries) Pilat (white-rot) and Gloeophyllum trabeum (Persoon ex Fries.) Murrill (brown-rot). After hot-pressing, no bubbles, delamination nor warping were observed for both species. In general, PK boards presented higher mechanical properties: E (M) , E (Md) , f (M) , f (c,0) whereas PO boards were dimensionally more stable, with lower values of WA, TS and PTS in the 2, 24, and 96-hour immersion periods. Board density, f (v,0), f (v,90) and rot weight loss were statistically equal for PO and PK LVL. The prediction of flexural properties of consolidated LVL by the nondestructive method used was not very efficient, and the fitted models presented lower predictability.

COLOR STABILITY OF DENTAL CERAMICS SUBMITTED TO ARTIFICIAL ACCELERATED AGING AFTER REPEATED FIRINGS

Statement of problem. Color stability is an important factor to ensure the long-term clinical success of ceramic restorations. There is a lack of information on how color is affected by fabrication procedures, such as the number of firings. Purpose. The purpose of this study was to evaluate the effects that the number of firings and type of substrate have on the color stability of dental ceramic submitted to artificial accelerated aging. Material and methods. Sixty specimens were fabricated: 30 metal ceramic (Verabond II + IPS d.SIGN) and 30 all-ceramic (IPS d.SIGN). Specimens were divided into 3 groups (n=10), and submitted to 2, 3, or 4 firings (+/- 900 degrees C), respectively, according to the manufacturer`s instructions. Color readings were obtained with a spectro photometer before and after artificial accelerated aging, and L*, a*, and b* coordinates and total color variation (Delta E) were analyzed (2-way ANOVA, Bonferroni, (alpha=05). Results. For metal ceramic specimens, differences for the L* coordinates were significant (P<.05) only for the group submitted to 3 firings. With respect to the all-ceramic specimens, smaller L* coordinates were obtained for greater a* and b* coordinates, indicating that the greater the number of firings, the darker and more reddish/yellowish the specimen. All Delta E values, for all groups, were below 1.0. All-ceramic specimens submitted to 3 and 4 firings presented Delta E means differing statistically (P<.05) from those of the metal ceramic group. Conclusions. The type of substrate and number of firings affected the color stability of the ceramic material tested. Artificial accelerated aging did not produce perceptible color stability changes (Delta E<1.0). (J Prosthet Dent 2009-101:13-18)