CCT diagrams of tricalcium silicate decomposition

The mechanical properties of Portland cement are closely related to the chemical composition of the clinker and particularly to the concentration of tricalcium silicate, C3S. In the industrial production process, the clinker must be rapidly quenched, to avoid its decomposition into dicalcium silicate and lime and also to avoid the transformation from higher temperature phases to lower temperature phases. This study investigated the kinetics of thermal decomposition of the C3S. Samples of laboratory-made C3S were thermally treated under specific conditions to determine the continuous cooling transformation (CCT) diagram of the material. The CCT diagram of the C3S showed decomposition rates with values that were much higher than the values traditionally accepted in the literature.

Applications of the Rietveld method to quantify the crystalline phases of Portland cement clinker doped with nickel and chromium

The effects of chromium or nickel oxide additions on the composition of Portland clinker were investigated by X-ray powder diffraction associated with pattern analysis by the Rietveld method. The co-processing of industrial waste in Portland cement plants is an alternative solution to the problem of final disposal of hazardous waste. Industrial waste containing chromium or nickel is hazardous and is difficult to dispose of. It was observed that in concentrations up to 1% in mass, the chromium or nickel oxide additions do not cause significant alterations in Portland clinker composition. (C) 2008 International Centre for Diffraction Data.

Effect of silicate fertilization on soil and on palisade grass plants under grazing intensities

Application of calcium silicate (SiCa) as soil acidity corrective was evaluated in a Rhodic Hapludox soil with palisade grass conducted under pasture rotation system with different grazing intensities. Experimental design was complete randomized blocks with four grazing intensities - grazing intensities were imposed by forage supply (50, 100, 150 and 200 kg t-1 of DM per LW) - in experimental plots with four replicates and, in the subplots, with seven doses of calcium silicate combined with lime: 0+0, 2+0, 4+0, 6+0, 2+4, 4+2 and 0+6 t ha-1, respectively. In the soil, it was evaluated the effect of four levels of calcium silicate (0, 2, 4 and 6 t ha-1) at 45, 90, and 365 days at three depths (0-10, 10-20 and 20-40 cm) and at 365 days, it was included one level of lime (6 t ha-1). For determination of leaf chemical composition and silicate content in the soil, four levels of calcium silicate (0, 2, 4 and 6 t ha-1) were evaluated at 45 and 365 days and at 45 days only for leaf silicate, whereas for dry matter production, all corrective treatments applied were evaluated in evaluation seasons. Application of calcium silicate was positive for soil chemical traits related to acidity correction (pH(CaCl2), Ca, Mg, K, H+Al and V), but the limestone promoted better results at 365 days. Leaf mineral contents were not influenced by application of calcium silicate, but there was an increase on silicate contents in leaves and in the soil. Dry matter yield and chemical composition of palisade grass improved with the application of correctives.

Influence of Granulometry and Organic Treatment of a Brazilian Montmorillonite on the Properties of Poly(styrene-co-n-butyl acrylate)/Layered Silicate Nanocomposites Prepared by Miniemulsion Polymerization

The influence of granulometry and organic treatment of a Brazilian montmorillonite (MMT) clay on the synthesis and properties of poly(styrene-co-n-butyl acrylate)/layered silicate nanocomposites was studied. Hybrid latexes of poly(styrene-co-butyl acrylate)/MMT were synthesized via miniemulsion polymerization using either sodium or organically modified MMT. Five clay granulometries ranging from clay particles smaller than 75 mu m to colloidal size were selected. The size of the clay particles was evaluated by Specific surface area measurements (BET). Cetyl trimethyl ammonium chloride was used as an organic modifier to enhance the clay compatibility with the monomer phase before polymerization and to improve the clav distribution and dispersion within the polymeric matrix after polymerization. The sodium and organically modified natural clays as well as the composites were characterized by X-ray diffraction analysis. The latexes were characterized by dynamic light scattering. The mechanical, thermal, and rheological properties of the composites obtained were characterized by dynamical-mechanical analysis, thermogravimetry, and small amplitude oscillatory, shear tests, respectively. The results showed that smaller the size of the organically modified MMT, the higher the degree of exfoliation of nanoplatelets. Hybrid latexes in presence of Na-MMT resulted in materials with intercalated structures. (C) 2009 Wiley, Periodicals, Inc. J Appl Polym Sci 112: 1949-1958, 2009

Influence of the Type of Quaternary Ammonium Salt Used in the Organic Treatment of Montmorillonite on the Properties of Poly(Styrene-co-Butyl Acrylate)/Layered Silicate Nanocomposites Prepared by In Situ Miniemulsion Polymerization

Hybrid latices of poly(styrene-co-butyl acrylate) were synthesized via in situ miniemulsion polymerization in the presence of 3 and 6 wt % organically modified montmorillonite (OMMT). Three different ammonium salts: cetyl trimethyl ammonium chloride (CTAC), alkyl dimethyl benzyl ammonium chloride (Dodigen), and distearyl dimethyl ammonium chloride (Praepagen), were investigated as organic modifiers. Increased affinity for organic liquids was observed after organic modification of the MMT. Stable hybrid latices were obtained even though miniemulsion stability was disturbed to some extent by the presence of the OMMTs during the synthesis. Highly intercalated and exfoliated polymer-MMT nanocomposites films were produced with good MMT dispersion throughout the polymeric matrix. Materials containing MMT modified with the 16 carbons alkyl chain salt (CTAC) resulted in the largest increments of storage modulus, indicating that single chain quaternary salts provide higher increments on mechanical properties. Films presenting exfoliated structure resulted in the largest increments in the onset temperature of decomposition. For the range of OMMT loading studied, the nanocomposite structure influenced more significantly the thermal stability properties of the hybrid material than did the OMMT loading. The film containing 3 wt % MMT modified with the two 18 carbons alkyl chains salt (Praepagen) provided the highest increment of onset temperature of decomposition. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 119: 3658-3669, 2011

Differences in both matrix metalloproteinase 9 concentration and zymographic profile between plasma and serum with clot activators are due to the presence of amorphous silica or silicate salts in blood collection devices

Matrix metalloproteinases (MMPs) are promising diagnostic tools, and blood sampling/handling alters MMP concentrations between plasma and serum and between serum with and without clot activators. To explain the higher MMP-9 expression in serum collected with clot accelerators relative to serum with no additives and to plasma, we analyzed the effects of increasing amounts of silica and silicates (components of clot activators) in,citrate plasma, serum, and huffy coats collected in both plastic and glass tubes from 50 healthy donors, and we analyzed the effects of silica and silicate on cultured leukemia cells. The levels of MMP-2 did not show significant changes between glass and plastic tubes, between serum and plasma, between serum with and without clot accelerators, or between silica and silicate treatments. No modification of MMP-9 expression was obtained by the addition of silica or silicate to previously separated plasma and serum. Increasing the amounts of nonsoluble silica and soluble silicate added to citrate and empty tubes prior to blood collection resulted in increasing levels of MMP-9 relative to citrate plasma and serum. Silica and silicate added to buffy coats and leukemia cells significantly induced MMP-9 release/secretion, demonstrating that both silica and silicate induce the release of pro- and complexed MMP-9 forms. We recommend limiting the misuse of serum and avoiding the interfering effects of clot activators. (c) 2007 Elsevier Inc. All rights reserved.

Alpha-Tricalcium Phosphate Bone Cement in the Surgical Treatment of Open Mastoid Cavity

Hypothesis: This study aimed to evaluate the biocompatibility of alpha-tricalcium phosphate bone cement in the obliteration of the mastoid cavity in guinea pigs. Background: Treatment with open cavity mastoidectomy can present poor functional results in chronic otitis media with cholesteatoma, especially if the cavity is large. Partial or total obliteration of the cavity can overcome these problems. Alpha-tricalcium phosphate bone cement has physicochemical characteristics that suggest its potential in mastoid cavity obliteration. Materials and Methods: Twenty guinea pigs were studied. All animals underwent surgery involving the dorsal tympanic bulla. In the study group animals (n = 10), mastoid cavity obliteration was performed with alpha-tricalcium phosphate bone cement. In the control group animals (n = 10), the cavity was left unfilled. On postoperative day 60, the animals were sacrificed and studied for signs of rejection of the material and other complications. Temporal bones were removed for histopathological study, in which the type and degree of inflammatory response, as well as the degree of ossification, were analyzed. Results: The mortality rate was the same in both groups. Deaths were attributed to anesthetic complications in the initial postoperative period. In the animals that survived, there were no complications, and there was good healing of the incision in both groups. There were no clinical signs of rejection of the material, and the histopathological analysis of the cement group revealed no signs of foreign body reaction (inflammatory response). Conclusion: Alpha-tricalcium phosphate bone cement is biocompatible in the mastoid cavity of guinea pigs.

THE COMPTON-THICK SEYFERT 2 NUCLEUS OF NGC 3281: TORUS CONSTRAINTS FROM THE 9.7 mu m SILICATE ABSORPTION

We present mid-infrared (mid-IR) spectra of the Compton-thick Seyfert 2 galaxy NGC 3281, obtained with the Thermal-Region Camera Spectrograph at the Gemini-South telescope. The spectra present a very deep silicate absorption at 9.7 mu m, and [S IV] 10.5 mu m and [Ne II] 12.7 mu m ionic lines, but no evidence of polycyclic aromatic hydrocarbon emission. We find that the nuclear optical extinction is in the range 24 mag <= A(V) <= 83 mag. A temperature T = 300 K was found for the blackbody dust continuum component of the unresolved 65 pc nucleus and the region at 130 pc SE, while the region at 130 pc NW reveals a colder temperature (200 K). We describe the nuclear spectrum of NGC 3281 using a clumpy torus model that suggests that the nucleus of this galaxy hosts a dusty toroidal structure. According to this model, the ratio between the inner and outer radius of the torus in NGC 3281 is R(0)/R(d) = 20, with 14 clouds in the equatorial radius with optical depth of tau(V) = 40 mag. We would be looking in the direction of the torus equatorial radius (i = 60 degrees), which has outer radius of R(0) similar to 11 pc. The column density is N(H) approximate to 1.2 x 10(24) cm(-2) and the iron K alpha equivalent width (approximate to 0.5-1.2 keV) is used to check the torus geometry. Our findings indicate that the X-ray absorbing column density, which classifies NGC 3281 as a Compton-thick source, may also be responsible for the absorption at 9.7 mu m providing strong evidence that the silicate dust responsible for this absorption can be located in the active galactic nucleus torus.

The Determination of Total Hydrogen, Carbon, Nitrogen and Sulfur in Silicates, Silicate Rocks, Soils and Sediments

Determinations of the volatile elements carbon, hydrogen, sulfur and nitrogen in many geological RM, performed with the LECO CHN and SC analysers, are presented. The method allowed the determination of S in concentrations from a few % m/m to 0.001% m/m or less, of C from % m/m to 0.01% m/m and of H from % m/m to 0.004% m/m. Accuracy was usually better than the XRF method (for S). All obtained values passed the Sutarno-Steger test, which establishes that vertical bar(mean(analysed) - mean(certified))vertical bar/ S(certified) < 2, for the cases with an appropriate number of determinations (n > 10 for each element). It was possible to perform routine determination of C, H and S with the instrumentation, coupled with the determination of major and minor elements in geological materials. Determination of nitrogen could also be performed on an exploratory basis, with improvements in the method dependent on the future availability of more reference materials with reliable composition of this element.

Tryptophan photooxidation promoted by new hybrid materials prepared by condensation of naphthalene imides with silicate by the sol-gel process

Three novel hybrid organic/inorganic materials were synthesized from 4-substituted (NO(2), Br, H) 1,8-naphthalene imide-N-propyltriethoxysilane by the sol-gel process. These materials were obtained as a xerogel and partially characterized. The ability to photosensitize the oxidation and degradation of tryptophan indole ring by these materials was studied through photophysical and photochemical techniques. Although the derivatives containing Br and NO(2) as substituent do not cause efficient tryptophan photodamage, the hybrid material obtained from 1,8-naphthalic anhydride is very efficient to promote tryptophan photooxidation. By using laser flash photolysis it was possible to verify the presence of naphthalene imide transient radical species. The presence of oxygen causes an increase of the yield of radical formation. These results suggest that the mechanism of photodegradation of tryptophan occurs by type I, i.e. the transient radical (TrpH(center dot+)) formed by the direct reaction of the triplet state of the naphthalene imide moiety with tryptophan. Thus a inorganic-organic hybrid material that can be used to promote the oxidation of biomolecules was obtained. (C) 2009 Elsevier B.V. All rights reserved.

Efeito residual da silicatagem no solo e na produtividade do capim-marandu sob pastejo

A escória siderúrgica é uma alternativa para a correção da acidez dos solos e é constituída de silicato de cálcio. Neste estudo, avaliaram-se os efeitos residuais da aplicação de silicato de cálcio nos atributos químicos do solo e da planta em Latossolo Vermelho distroférrico típico com capim-Marandu (Brachiaria brizantha cv. Marandu), sob intensidades de pastejo em lotação rotacionada. O delineamento experimental foi de blocos ao acaso, com intensidades de pastejo avaliadas pelas ofertas diárias de forragem de 50, 100, 150 e 200 kg t-1 de MS por PV nas parcelas experimentais, enquanto a aplicação superficial de silicato de cálcio combinado com calcário dolomítico, respectivamente, nas doses 0 + 0; 2 + 0; 4 + 0; 6 + 0; 2 + 4; 4 + 2 e 0 + 6 t ha- 1 nas subparcelas com quatro repetições, duas épocas (verão e inverno) e avaliação em três profundidades do solo (0-10, 10-20 e 20-40 cm). Os atributos químicos do solo pH em CaCl2, Ca, Mg, K, H + Al e V, avaliados 720 dias após a aplicação, apresentaram resultados favoráveis do poder residual do silicato de Ca e do calcário. A oferta de forragem 200 kg t-1 e o tratamento somente com calcário dolomítico (0 + 6 t ha-1) elevaram o valor de pH em CaCl2 e o V, principalmente na camada de 0-10 cm. Os teores de Si no solo foram influenciados pelas doses aplicadas de silicato de Ca, apesar de não terem causado alterações significativas nos teores foliares de Si. A composição químico-bromatológica foi afetada somente pelas ofertas e épocas. As ofertas, épocas e a interação época x oferta resultaram em efeitos na produção de matéria seca no pré-pastejo, com maiores produções para a oferta 200 kg t-1 e menores para a de 50 kg t-1 nas duas épocas. O resíduo (pós-pastejo) foi influenciado pelas ofertas e épocas. As ofertas 50 e 100 kg t-1 e o tratamento com 2 t ha-1 de silicato de Ca promoveram as maiores taxas de acúmulo de matéria seca.

Femtosecond third-harmonic generation in a glass ceramic containing sodium niobate nanocrystals

The third-harmonic optical susceptibility, chi((3))(3 omega; omega, omega, omega) of a silicate glass ceramic containing sodium niobate nanocrystals was measured for incident broadband light with central frequency omega corresponding to 1900nm. Absolute values of |chi((3))| and the dispersion of the refractive index from 600 to 1900nm were measured using the spectrally resolved femtosecond Maker fringes technique. The experiments show that |chi((3))| is 1 order of magnitude larger than silica, and it grows by similar to 50% when the volume fraction occupied by the nanocrystals increases up to 40%. (C) 2011 Optical Society of America

Sodium distribution in mixed alkali K-Na metaphosphate glasses

The local order and distribution of Na in the mixed alkali metaphosphate glasses K(x)Na(1-x)PO(3) were analyzed, with the aim to identify segregation or a random mixture of both cation species. X-Ray photoelectron spectroscopy and several nuclear magnetic resonance (NMR) techniques were applied, including (31)P and (23)Na high-resolution spectroscopy, (23)Na triple quantum-MAS NMR, rotational echo double resonance between (31)P and (23)Na, and (23)Na NMR spin echo decay. The structural picture emerging from these results reveals the similarity in the local Na environments in the glasses but also subtle structural adjustments with increasing degree of K replacement. While both cations are intimately mixed at the atomic scale, the (23)Na spin echo decay data suggest a detectable like-cation preference in the spatial distribution of the ions. These structural properties are consistent with those determined in Li-Rb metaphosphates, indicating that the origin of the mixed alkali effect observed in the conductivity of Na-K metaphosphate glasses may also be explained by structurally blocked ion diffusion.

Arsenic and Chromium in Brazilian Agricultural Supplies

Arsenic (As) and chromium (Cr) contents were measured in agricultural supplies used at different farms in Sao Paulo State, Brazil. The highest mass fractions of As were found in thermophosphates, reaching levels of 4 mg/kg. The highest mass fractions of Cr (21 g/kg) were found in calcium magnesium silicate, while the thermophosphates also presented high values reaching approximately 1 g/kg. The levels of As were within Brazilian guidelines, but the values of Cr in thermophosphates exceeded the levels permitted in Brazil. The As content in fertilizers may be considered safe (5 mg/kg) in terms of environmental pollution. However, the Cr content in calcium magnesium silicate following continuous use may constitute a significant problem in Brazil due to potentially increasing levels of this metal in soils.

Macronutrients in Marandu Palisade Grass as Influenced by Lime, Slag, and Nitrogen Fertilization

Soil acidity is one of the main limiting factors for the growth of pasture grasses in Brazilian soils. In addition to lime, slag can be used to correct soil acidity and help plants to absorb nutrients in adequate amounts. The objective of this experiment was to evaluate, under greenhouse conditions, the effects of slag and lime plus nitrogen (N) on marandu palisade grass plants` nutritional status as well as the absorption of macronutrients submitted to two cuts. The treatments consisted of two corrective materials (slag and lime), three corrective material rates (0.81, 1.61, and 3.22 g dm-3 of ECaCO3), three N rates (75, 150, and 300 mg dm-3) plus a control treatment, with four replications. Macronutrient contents in the forage plants were found to be present in adequate levels. The mean value of N accumulated in the shoot was 40.1 mg per plant, phosphorus (P) was 4.6 mg per plant, potassium (K) was 38.6 mg per plant, calcium (Ca) was 7.3 mg per plant, magnesium (Mg) was 6.7 mg per plant, and sulfur (S) was 3.5 mg per plant at the first cut. At the second cut, the nutrient accumulations values were N 50.8 mg per plant, P 6.3 mg per plant, K 20.7 mg per plant, Ca 21.6 mg per plant, Mg 24.0 mg per plant, and S 4.7 mg per plant. Macronutrients accumulation in the shoot of grass increased with the addition of both the correctives as well as the N rates.