Influence of interimplant distance on bone microstructure: A histomorphometric study in dogs

The microstructure of the crestal alveolar bone is important for both the maintenance of osseointegration and the location of the gingival soft tissues. The aim of this study was to evaluate and compare the bone microstructure of the alveolar bone and of the interimplant bone in implants inserted at different interimplant distances. The mandibular bilateral premolars of six dogs were extracted, and after 12 weeks, each dog received eight implants, for a total of 48 implants. Two pairs of implants, one for each hemiarch, were separated by 2 mm (group 1) and by 3 mm (group 2). After 12 weeks, the implants received temporary acrylic prostheses. After four more weeks, metallic crowns substituted the temporary prostheses. After an additional 8 weeks the animals were sacrificed and the hemimandibles were removed, dissected, and processed. The longitudinal collagen fiber orientation was 43.2% for the alveolar bone; it was 30.3% for the 2-mm group and 43.9% for the 3-mm group. There was a statistically significant difference between the 2-mm and 3-mm groups (p < .05). The orientation of transverse collagen fibers was 47.8% for the alveolar bone; it was 37.3% for the 2-mm group and 56.3% for the 3-mm group. There was a statistically significant difference between the 2-mm and 3-mm groups (p < .05). The marrow spaces were 34.87% for the alveolar bone, 52.3% for the 2-mm group, and 59.9% for the 3-mm group. There was a statistically significant difference between the alveolar bone and the 3-mm group (p < .05). The low mineral density index was 36.29 for the alveolar bone, 46.76 for the 2-mm group, and 17.91 for the 3-mm group. There was a statistically significant difference between the 2-mm and 3-mm groups (p < .05). The high mineral density was 87.57 for the alveolar bone, 72.58 for the 2-mm group, and 84.91 for the 3-mm group. There was a statistically significant difference between the alveolar bone and the 2-mm group (p < .05). The collagen fiber orientation resulted in statistically significant differences in both the 2-mm and 3-mm groups compared with the alveolar bone. The marrow spaces appeared significantly increased in the 3-mm group compared with the alveolar bone. The low mineral density index was significantly higher in the 2-mm group, while the high mineral density index was significantly higher in the alveolar bone. In conclusion, the interimplant distance should not be less than 3 mm.

Shear strength of the bond to primary dentin: influence of Er:YAG laser irradiation distance

The aim of this study was to assess in vitro the influence of Er:YAG laser irradiation distance on the shear strength of the bond between an adhesive restorative system and primary dentin. A total of 60 crowns of primary molars were embedded in acrylic resin and mechanically ground to expose a flat dentin surface and were randomly assigned to six groups (n = 10). The control group was etched with 37% phosphoric acid. The remaining five groups were irradiated (80 mJ, 2 Hz) at different irradiation distances (11, 12, 16, 17 and 20 mm), followed by acid etching. An adhesive agent (Single Bond) was applied to the bonding sites, and resin cylinders (Filtek Z250) were prepared. The shear bond strength tests were performed in a universal testing machine (0.5 mm/min). Data were submitted to statistical analysis using one-way ANOVA and the Kruskal-Wallis test (p < 0.05). The mean shear bond strengths were: 7.32 +/- 3.83, 5.07 +/- 2.62, 6.49 +/- 1.64, 7.71 +/- 0.66, 7.33 +/- 0.02, and 9.65 +/- 2.41 MPa in the control group and the groups irradiated at 11, 12, 16, 17, and 20 mm, respectively. The differences between the bond strengths in groups II and IV and between the bond strengths in groups II and VI were statistically significant (p < 0.05). Increasing the laser irradiation distance resulted in increasing shear strength of the bond to primary dentin.