Residual stresses in TiN, DLC and MoS(2) coated surfaces with regard to their tribological fracture behaviour

Thin hard coatings on components and tools are used increasingly due to the rapid development in deposition techniques, tribological performance and application skills. The residual stresses in a coated surface are crucial for its tribological performance. Compressive residual stresses in PVD deposited TiN and DLC coatings were measured to be in the range of 0.03-4 GPa on steel substrate and 0.1-1.3 GPa on silicon. MoS(2) coatings had tensional stresses in the range of 0.8-1.3 on steel and 0.16 GPa compressive stresses on silicon. The fracture pattern of coatings deposited on steel substrate were analysed both in bend testing and scratch testing. A micro-scale finite element method (FEM) modelling and stress simulation of a 2 mu m TiN-coated steel surface was carried out and showed a reduction of the generated tensile buckling stresses in front of the sliding tip when compressive residual stresses of 1 GPa were included in the model. However, this reduction is not similarly observed in the scratch groove behind the tip, possibly due to sliding contact-induced stress relaxation. Scratch and bending tests allowed calculation of the fracture toughness of the three coated surfaces, based on both empirical crack pattern observations and FEM stress calculation, which resulted in highest values for TiN coating followed by MoS(2) and DLC coatings, being K(C) = 4-11, about 2, and 1-2 MPa M(1/2), respectively. Higher compressive residual stresses in the coating and higher elastic modulus of the coating correlated to increased fracture toughness of the coated surface. (C) 2009 Elsevier B.V. All rights reserved.

Columbia revisited: Paleomagnetic results from the 1790 Ma colider volcanics (SW Amazonian Craton, Brazil)

In an attempt to improve our understanding of the Paleoproterozoic geodynamic evolution, a paleomagnetic study was performed on 10 sites of acid volcanic rocks of the Colider Suite, southwestern Amazonian Craton. These rocks have a well-dated zircon U-Pb mean age of 1789 +/- 7 Ma. Alternating field and thermal demagnetization revealed northern (southern) directions with moderate to high upward (downward) inclinations. Rock magnetism experiments and magnetic mineralogy show that this characteristic magnetization is carried by Ti-poor magnetite or by hematite that replaces magnetite by late-magmatic cleuteric alteration. Both magnetite and hematite carry the same characteristic component. The mean direction (Dm = 183.0 degrees, Im = 53.5 degrees, N = 10, alpha(95) = 9.8 degrees, K = 25.2) yielded a paleomagnetic pole located at 298.8 degrees E, 63.3 degrees S (alpha(95) = 10.2 degrees, K = 23.6), which is classified with a quality factor Q = 5. Paleogeographic reconstructions using this pole and other reliable Paleoproterozoic poles suggest that Laurentia, Baltica, North China Craton and Amazonian Craton were located in laterally contiguous positions forming a large continental mass at 1790 Ma ago. This is reinforced by geological evidence which support the existence of the supercontinent Columbia in Paleoproterozoic times. (C) 2008 Elsevier B.V. All rights reserved.