All solid-state electrochromic devices with gelatin-based electrolyte

6 x 8cm(2) electrochromic devices (ECDs) with the configuration K-glass/EC-layer/electrotype/ion-storage (IS) layer/K-glass, have been assembled using Nb2O5:Mo EC layers, a (CeO2)(0.81)-TiO2 IS-layer and a new gelatin electrolyte containing Li+ ions. The structure of the electrolyte is X-ray amorphous. Its ionic conductivity passed by a maximum of 1.5 x 10(-5) S/CM for a lithium concentration of 0.3g/15ml. The value increases with temperature and follows an Arrhenius law with an activation energy of 49.5 kJ/mol. All solid-state devices show a reversible gray coloration, a long-term stability of more than 25,000 switching cycles (+/- 2.0 V/90 s), a transmission change at 550 nm between 60% (bleached state) and 40% (colored state) corresponding to a change of the optical density (Delta OD = 0. 15) with a coloration efficiency increasing from 10cm(2)/C (initial cycle) to 23cm(2)/C (25,000th cycle). (c) 2007 Elsevier B.V. All rights reserved.

Measurement of the anodic potential in solid state: A tool for determination of the antioxidant potential of phytomedicine

The electroanalytical techniques are very promissing to perform the quality control of crude vegetable. Solid State Differential Pulse Voltammetry in the supporting electrolyte is able to detect the oxidation signals of the active material, which can be used as a parameter to identify the type of crude vegetable and its antioxidant activity. The working electrode consisted in a carbon paste electrode modified with the powder of vegetable raw material (EMF). The electrochemical measurements were performed in a cell containing the working (EMF), reference (Ag/AgCl, KClsat) and auxiliary (Pt) electrodes.

Amylopectin-rich starch plasticized with glycerol for polymer electrolyte application

This paper describes the preparation and characterization of a solid polymer electrolyte based on amylopectin-rich starch plasticized with glycerol. The samples were characterized through ionic conductivity (sigma) measurements, scanning electron microscopy, thermal analysis, and spectroscopy in the UV-Vis-NIR region. The results showed that the highest sigma (1.1 x 10(-4) Scm(-1) at 30 degrees C) was obtained for the sample with n = [O]/[Li] = 6.5 ratio. In addition, the samples plasticized with 30-35 wt.% of glycerol presented high ionic conductivity, transparency and conduction stability. The ionic conductivity measurements as a function of lithium salt contents showed a maximum for n=6.5. The ionic conductivity as a function of time for amylopectin-rich starch plasticized with 30 wt.% of glycerol and containing [O]/[Li] = 10 showed conduction stability over 6 months (sigma similar to 3.01 x 10(-5) S cm(-1)). (C) 2010 Elsevier B.V. All rights reserved.

Gelatin-based protonic electrolyte for electrochromic windows

Proton-conducting gel polymer electrolytes based on gelatin plasticized with glycerol and containing acetic acid were investigated, characterized, and applied to electrochromic window. For glycerol contents varying from 7% to 48%, the conductivity of the uniform and predominantly amorphous gel electrolyte was found to follow a Vogel-Tamman-Fulcher behavior with the temperature. Typically, for the electrolyte chosen to make 7 x 2 cm(2) electrochromic smart window with the configuration: glass/fluor-doped tin oxide (FTO)/WO(3)/gelatin electrolyte/CeO(2)-TiO(2)/FTO/glass and containing 28% of glycerol, the conductivities were found to be of the order of 5 x 10(-5) S/cm at room temperature and 3.6 x 10(-4) S/cm at 80 A degrees C. The device was characterized by spectroelectrochemical techniques and was tested up to 10,000 cycles showing a fast coloring/bleaching behavior, where the coloring process was achieved in 10 s and the bleaching in 2 s. The transmission variation at the wavelength of 550 nm was about 15%. The cyclic voltammograms showed a very good reversibility of the cathodic/anodic processes, and the charge density was about 3.5 mC/cm(2). The memory tests showed that the transmittance in the colored state increased by 8% in 90 min after removing the potential.