Crystallographic characterization of silicon nitride ceramics sintered with Y(2)O(3)-Al(2)O(3) or E(2)O(3)-Al(2)O(3) additions

Silicon nitride ceramics were sintered using Y(2)O(3)-Al(2)O(3) or E(2)O(3)-Al(2)O(3) (E(2)O(3) denotes a mixed oxide Of Y(2)O(3) and rare-earth oxides) as sintering additives. The intergranular phases formed after sintering was investigated using high-resolution X-ray diffraction (HRXRD). The use of synchrotron radiation enabled high angular resolution and a high signal to background ratio. Besides the appearance Of beta-Si(3)N(4) phase the intergranular phases Y(3)Al(5)O(12) (YAG) and Y(2)SiO(5) were identified in both samples. The refinement of the structural parameters by the Rietveld method indicated similar crystalline structure Of beta-Si(3)N(4) for both systems used as sintering additive. On the other hand, the intergranular phases Y(3)Al(5)O(12) and Y(2)SiO(5) shown a decrease of the lattice parameters, when E(2)O(3) was used as additive, indicating the formation of solid solutions of E(3)Al(5)O(12) and E(2)SiO(5), respectively. (C) 2007 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Wetting behaviour of silicon nitride ceramics by Ti-Cu alloys

The wetting of Ti-Cu alloys on Si3N4 was analyzed by the sessile drop method, using an imaging system with a CCD camera during the heating under argon flow. The contact angle was measured as a function of temperature and time. The samples were cut transversally and characterized by scanning electron microscopy and energy dispersive spectrometry (SEM/EDS). Wettability of the Ti-Cu alloy on Si3N4 is influenced by the reaction between the Ti and the ceramic. The TC1 and TC2 alloys presented low final contact angle values around 2 degrees and 26 degrees, respectively, indicating good wetting on Si3N4. (c) 2006 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Structural and morphological studies on SiOxNy thin films

In this work, the structure and morphology of silicon oxynitride films deposited by the PECVD technique were studied. The films were deposited under two different conditions: (a) SiOxNy with chemical compositions varying from SiO2 to Si3N4 via the control of a N2O + N-2 + SiH4 gas mixture, and (b) Si-rich SiOxNy films via the control of a N2O + SiH4 gas mixture. The analyses were performed using X-ray near edge spectroscopy (XANES) at the Si-K edge, transmission electron microscopy (TEM) and Rutherford backscattering spectroscopy (RBS). For samples with chemical composition varying from SiO2 to Si3N4, the diffraction patterns obtained by TEM exhibited changes with the chemical composition, in agreement with the XANES results. For silicon-rich silicon oxynitride samples, the formation of a-Si clusters was observed and the possibility of obtaining Si nanocrystals after annealing depending on the composition and temperature was realized. (C) 2007 Elsevier B.V. All rights reserved.

Tunable Bragg filter using silicon compound films

In this work, we present the simulation, fabrication and characterization of a tunable Bragg filter employing amorphous dielectric films deposited by plasma enhanced chemical vapor deposition technique on a crystalline silicon substrate. The optical device was built using conventional microelectronic processes and consisted of fifteen periodic intervals of Si3N4 layers separated by air with appropriated thickness and lengths to produce transmittance attenuation peaks in the visible region. For this, previous simulations were realized based in the optical parameters of the dielectric film, which were extracted from ellipsometry and profilometry techniques. For the characterization of the optical interferential filter, a 633 nm monochromatic light was injected on the filter, and then the transmitted output light was collected and conducted to a detector through an optical waveguide made also of amorphous dielectric layers. Afterwards, the optical filter was mounted on a Peltier thermoelectric device in order to control the temperature of the optical device. When the temperature of filter changes, a refractive index variation is originated in the dielectric film due to the thermo-optic effect, producing a shift of attenuation peak, which can be well predicted by numerical simulations. This characteristic allows this device to be used as a thermo-optic sensor. (C) 2007 Elsevier B.V. All rights reserved.