Ferromagnetic coupling in a Co-doped graphenelike ZnO sheet

Using first-principles calculations it is demonstrated that Co doped graphenelike ZnO sheet presents ferromagnetic coupling. The Co atoms are energetically barrierless absorbed in the Zn sites, suffering a Jahn-Teller distortion. The results reveal that the origin of the ferromagnetic coupling, different from the bulk 3D ZnO stacking, is mainly guided by a direct exchange interaction without any additional defect. This ferromagnetic coupling is due to the system topology, namely, it is a direct consequence of the two-dimensional character of the ZnO monolayer within graphenelike structure. Increasing the number of ZnO layers the ferromagnetic coupling vanishes.

Falling sheet envelope method for non-destructive testing time-dependent signals

In this work, an algorithm to compute the envelope of non-destructive testing (NDT) signals is proposed. This method allows increasing the speed and reducing the memory in extensive data processing. Also, this procedure presents advantage of preserving the data information for physical modeling applications of time-dependent measurements. The algorithm is conceived to be applied for analyze data from non-destructive testing. The comparison between different envelope methods and the proposed method, applied to Magnetic Bark Signal (MBN), is studied. (C) 2010 Elsevier Ltd. All rights reserved.

Cracking of 2.25Cr-1.0Mo steel tube/stationary tube-sheet weldment of a heat-exchanger

The premature failure of a horizontal heat-exchanger, which occurred after service exposure at 580 degrees C for 50,000 h, revealed the occurrence of extensive through-thickness cracking in approximately 40% of the tube/stationary tube-sheet welds. Additionally, the internal surface of the welded joint featured intensive secondary intergranular cracking (up to 250 mu m deep), preferential formation of a 150 mu m thick layer of (Fe, Cr)(3)O-4 and internal intergranular oxidation (40 mu m deep). The welded region also showed intense carbon pick-up and, as consequence, severe precipitation of intergranular M7C3 and M23C6 carbides. The fracture surface was composed of two distinct regions: a ""planar"" region of 250 mu m, formed due to the stable crack growth along by the intergranular oxidation; and a slant region with radial marks, formed by the fast crack growth along the network of intergranular carbides. The association of intergranular oxidation pre-cracks with microstructural embrittlement promoted the premature failure, which took place by an overload mechanism, probably due to the jamming of the floating tube-sheet during the maintenance halt (cooling operation). (C) 2007 Elsevier Ltd. All rights reserved.