Digital versus Conventional Radiography for Imaging Fatigue Cracks in Riveted Lap Joints of Hybrid Glass Reinforced Fiber/Metal Laminate

A round robin program zoos conducted to assess the ability of three different X-radiographic systems for imaging internal fatigue cracks in riveted lap joints of composite glass reinforced fiber/metal laminate. From an engineering perspective, conventional film radiography and direct radiography have produced the best results, identifying and characterizing in detail internal damage on metallic faying surfaces of fastened glass reinforced fiber/metal laminate joints. On the other hand, computed radiographic images presented large projected geometric distortions and feature shifts due to the angular incident radiation beam, disclosing only partial internal cracking patterns.

Instrumented indentation testing of an epoxy adhesive used in automobile body assembling

Instrumented indentation has been used to investigate the mechanical properties of BETAMATE 1496 (R) Epoxy adhesive. The properties of the adhesive were analyzed by measuring its hardness and its Young`s modulus in samples extracted from six different positions of the front door of a commercial passenger vehicle in two phases of processing: after application of the adhesive in the door assembling (""pre-cured"" state) and after final cure in the painting oven (""cured"" state). Special attention was given to setting the optimal parameters (""creep"" time and unloading time step) for the instrumented indentation testing for the present application. Young`s modulus values around 1.1 +/- 0.2 GPa and hardness values around 0.15 +/- 0.05 GPa were obtained for all samples, irrespective of the variation of the indentation parameters in the testing procedure and of the relative position of the adhesive in the door frame in both states. (C) 2008 Elsevier Ltd. All rights reserved.

Investigation on the intergranular corrosion resistance of the AISI 316L(N) stainless steel after long time creep testing at 600 degrees C

The effect of precipitation on the corrosion resistance of AISI 316L(N) stainless steel previously exposed to creep tests at 600 degrees C for periods of up to 10 years, has been studied. The corrosion resistance was investigated in 2 M H(2)SO(4)+0.5 M NaCl+0.01 M KSCN solution at 30 degrees C by electrochemical methods. The results showed that the susceptibility to intergranular corrosion was highly affected by aging at 600 degrees C and creep testing time. The intergranular corrosion resistance decreased by more than twenty times when the creep testing time increased from 7500 h to 85,000 h. The tendency to passivation decreased and less protective films were formed on the creep tested samples. All tested samples also showed susceptibility to pitting. Grain boundary M(23)C(6) carbides were not found after long-term exposure at 600 degrees C and the corrosion behavior of the creep tested samples was attributed to intermetallic phases (mainly sigma phase) precipitation. (C) 2007 Elsevier Inc. All rights reserved.

Study of calcium oxalate monohydrate of kidney stones by X-ray diffraction

X-ray powder diffraction was used to study the phase composition of human renal calculi. The stones were collected from 56 donors in Vitoria, Espirito Santo state, southeastern Brazil. An XRD phase quantification revealed that 61% of the studied renal stones were composed exclusively of calcium oxalate [34% formed only by calcium oxalate rnonohydrate (COM) and 27% presents both monohydrate and dihydratate calcium oxalate]. The 39% multi-composed calculi have various other phases such as uric acid and calcium phosphate. Rietveld refinement of XRD data of one apparent monophasic (COM) renal calculus revealed the presence of a small amount of hydroxyapatite. The presence of this second phase and the morphology of the stone (ellipsoidal) indicated that this calculus can be classified as non-papillary type and its nucleation process developed in closed kidney cavities. In order to show some advantages of the X-ray powder diffraction technique, a study of the phase transformation of monohydrate calcium oxalate into calcium carbonate (CaCO(3)) was carried out by annealing of a monophasic COM calculi at 200, 300, and 400 degrees C for 48 h in a N(2) gas atmosphere. The results of the XRD for the heat treated samples is ill good agreement with the thermogravimetric analysis found in the literature and shows that X-ray powder diffraction can be used as a suitable technique to study the composition and phase diagram of renal calculi. (C) 2008 International Centre for Diffraction Data.

Parametric model for the analysis of concrete expansion due to alkali-aggregate reaction

The alkali-aggregate reaction (AAR) is a chemical reaction that provokes a heterogeneous expansion of concrete and reduces important properties such as Young's modulus, leading to a reduction in the structure's useful life. In this study, a parametric model is employed to determine the spatial distribution of the concrete expansion, combining normalized factors that influence the reaction through an AAR expansion law. Optimization techniques were employed to adjust the numerical results and observations in a real structure. A three-dimensional version of the model has been implemented in a finite element commercial package (ANSYS(C)) and verified in the analysis of an accelerated mortar test. Comparisons were made between two AAR mathematical descriptions for the mechanical phenomenon, using the same methodology, and an expansion curve obtained from experiment. Some parametric studies are also presented. The numerical results compared very well with the experimental data validating the proposed method.

Internal stresses and textures of nanostructured alumina scales growing on polycrystalline Fe(3)Al alloy

The evolution of internal stresses in oxide scales growing on polycrystalline Fe(3)Al alloy in atmospheric air at 700 degrees C was determined using in situ energy-dispersive synchrotron X-ray diffraction. Ex situ texture analyses were performed after 5 h of oxidation at 700 degrees C. Under these conditions, the oxide-scale thickness, as determined by X-ray photoelectron spectroscopy, lies between 80 and 100 nm. The main phase present in the oxide scales is alpha-Al(2)O(3), with minor quantities of metastable theta-Al(2)O(3) detected in the first minutes of oxidation, as well as alpha-Fe(2)O(3). alpha-Al(2)O(3) grows with a weak (0001) fiber texture in the normal direction. During the initial stages of oxidation the scale develops, increasing levels of compressive stresses which later evolve to a steady state condition situated around -300 MPa. (C) 2010 International Centre for Diffraction Data. [DOI: 10.1154/1.3402764]

Applications of the Rietveld method to quantify the crystalline phases of Portland cement clinker doped with nickel and chromium

The effects of chromium or nickel oxide additions on the composition of Portland clinker were investigated by X-ray powder diffraction associated with pattern analysis by the Rietveld method. The co-processing of industrial waste in Portland cement plants is an alternative solution to the problem of final disposal of hazardous waste. Industrial waste containing chromium or nickel is hazardous and is difficult to dispose of. It was observed that in concentrations up to 1% in mass, the chromium or nickel oxide additions do not cause significant alterations in Portland clinker composition. (C) 2008 International Centre for Diffraction Data.

High-temperature X-ray powder diffraction study of the tetragonal-cubic phase transition in nanocrystalline, compositionally homogeneous ZrO2-CeO2 solid solutions

Crystal structure of compositionally homogeneous, nanocrystalline ZrO2-CeO2 solutions was investigated by X-ray powder diffraction as a function of temperature for compositions between 50 and 65 mol % CeO2 center dot ZrO2-50 and 60 mol % CeO2 solid solutions, which exhibit the t'-form of the tetragonal phase at room temperature, transform into the cubic phase in two steps: t'-to-t '' followed by t ''-to-cubic. But the ZrO2-65 mol % CeO2, which exhibits the t ''-form, transforms directly to the cubic phase. The results suggest that t'-to-t '' transition is of first order, but t ''-to-cubic seems to be of second order. (C) 2008 International Centre for Diffraction Data.

Synchrotron X-ray powder diffraction study of the tetragonal-cubic phase transition in nanostructured ZrO2-Sc2O3 solid solutions

The transition between tetragonal and cubic phases in nanostructured ZrO2-Sc2O3 solid solutions by high-temperature X-ray powder diffraction using synchrotron radiation is presented. ZrO2-8 and 11 mol% Sc2O3 nanopowders that exhibit the t'- and t ''-forms of the tetragonal phase, respectively, were synthesized by a stoichiometric nitrate-lysine gel-combustion route. The average crystallite size treated at 900 degrees C was about 25 nm for both compositions. Our results showed that t'-t '' and t ''-cubic transitions take place for the 8 and 11 mol% Sc2O3 samples, respectively. (C) 2008 International Centre for Diffraction Data.

X-ray diffraction data of tibolone Delta(4) isomer (isotibolone)

Tibolone is used for hormone reposition of postmenopause women and isotibolone is considered the major degradation product of tibolone. Isotibolone can also be present in tibolone API raw materials due to some inadequate synthesis. Its presence is then necessary to be identified and quantified in the quality control of both API and drug products. In this work we present the indexing of an isotibolone X-ray diffraction pattern measured with synchrotron light (lambda=1.2407 angstrom) in the transmission mode. The characterization of the isotibolone sample by IR spectroscopy, elemental analysis, and thermal analysis are also presented. The isotibolone crystallographic data are a=6.8066 angstrom, b=20.7350 angstrom, c=6.4489 angstrom, beta=76.428 degrees, V=884.75 angstrom(3), and space group P2(1), rho(o)= 1.187 g cm(-3), Z=2. (C) 2009 International Centre for Diffraction Data. [DOI: 10.1154/1.3257612]

Microstructural characterization of rapidly solidified and heat-treated Ti(92)B(8) eutectic alloy

In this work, Ti(92)B(8) alloy was processed via rapid solidification (splat-cooling) and then heat-treated at 700 degrees C and 1000 degrees C. A careful microstructural characterization indicated that, after rapid solidification, a very fine two-phase microstructure was produced with no significant saturation of B in alpha/beta Ti. There was no indication of amorphous formation in the rapidly solidified splats. Both alpha Ti and TiB were observed in the microstructures of the splats after heat-treatment at 700 degrees C and 1000 degrees C, confirming the stability of the alpha Ti+TiB two-phase region in this temperature range. (C) 2008 Elsevier Inc. All rights reserved.

Woodgrain defect on tinned steel Flandres foil

Tin electrocoated steel strip, also referred to as Flandres foil, is largely used for manufacturing food containers. Tinplates must have good corrosion resistance, workability, weldability, as well as a bright appearance. The woodgrain defect, a not yet fully understood defect that occurs on tinplates and accounts for their high scrap rate, consists of alternate bands of bright/dull reflectivity and resembles longitudinally cut wood. Observations of the woodgrain defect by scanning electron microscopy showed that the molten tin spreads irregularly during both the melting and solidification stages. X-ray diffraction analyses showed that the metallic tin tended to crystallize in the (200) direction for coupons with and without the woodgrain defect. Nevertheless, the preferential orientation degree decreased for coupons with the woodgrain defect. The rocking curves, also known as omega-scan, showed that the tin grains were uniformly aligned parallel to the strip surface for coupons with no defects, whereas for tinplates with woodgrain, the tin grains were not uniformly oriented, probably due to the misalignment of the grains in relation to the surface. (C) 2011 Elsevier Inc. All rights reserved.

Microstructural characterization of as-cast Cr-B alloys

Accurate knowledge of several Me-B (Me - Metal) phase diagrams are important to evaluate higher order systems such as Me-Si-B ternaries. This work presents results of microstructural characterization of as-cast Cr-B alloys which are significant to assess the liquid compositions associated to most of the invariant reactions of this system. Alloys of different compositions were prepared by arc melting pure Cr and B pressed powder mixtures under argon atmosphere in a water-cooled copper crucible with non-consumable tungsten electrode and titanium getter. The phases were identified by scanning electron microscopy (SEM), using back-scattered electron (BSE) image mode and X-ray diffraction (XRD). In general, a good agreement was found between our data and those from the currently accepted Cr-B phase diagram. (c) 2006 Elsevier Inc. All rights reserved.

Microstructural characterization of as-cast Cr-Si alloys

This work presents results of microstructural characterization of as-cast Cr-Si alloys. The alloys were prepared by arc melting pure Cr (min. 99.996%) and Si (min. 99.998%) powder mixtures under argon atmosphere in a water-cooled copper crucible with nonconsumable tungsten electrode and titanium getter. The phases were identified by scanning electron microscopy (SEM), using the back-scattered electron (BSE) image mode and X-ray diffraction (XRD). The results confirm the currently accepted Cr-Si phase diagram in terms of the invariant reactions and solid phases present in this system. Small corrections are proposed for the compositions of the liquid phase in the following reactions: (i) L double left right arrow Cr-ss+Cr3Si, from 15 to 16 at.% Si; (ii) L+alpha Cr5Si3 double left right arrow CrSi, from 51 at.% Si to slightly above 53 at.% Si; (iii) L double left right arrow CrSi+CrSi2, from 56 to slightly above 57 at.% Si; (iv) L double left right arrow CrSi2+Si, from 82 to slightly above 85 at.% Si. (c) 2006 Elsevier Inc. All rights reserved.

Thermal diffusivity of polymers by modified angstrom method

The nature of the molecular structure of plastics makes the properties of such materials markedly temperature dependent. In addition, the continuous increase in the utilization of polymeric materials in many specific applications has demanded knowledge of their physical properties, both during their processing as raw material, as well as over the working temperature range of the final polymer product. Thermal conductivity, thermal diffusivity and specific heat, namely the thermal properties, are the three most important physical properties of a material that are needed for heat transfer calculations. Recently, among several different methods for the determination of the thermal diffusivity and thermal conductivity, transient techniques have become the preferable way for measuring thermal properties of materials. In this work, a very simple and low cost variation of the well known Angstrom method is employed in the experimental determination of the thermal diffusivity of some selected polymers. Cylindrical shaped samples 3 cm diameter and 7 cm high were prepared by cutting from long cylindrical commercial bars. The reproducibility is very good, and the results obtained were checked against results obtained by the hot wire technique, laser flash technique, and when possible, they were also compared with data found in the literature. Thermal conductivity may be then derived from the thermal diffusivity with the knowledge of the bulk density and the specific heat, easily obtained by differential scanning calorimetry. (C) 2009 Elsevier Ltd. All rights reserved.