Retention at room temperature of the tetragonal t ``-form in Sc(2)O(3)-doped ZrO(2) nanopowders

Synchrotron X-ray powder diffraction was applied to the study of the effect of crystallite size on the crystal structure of ZrO(2)-10 mol% Sc(2)O(3) nanopowders synthesized by a nitrate-lysine gel-combustion route Nanopowders with different average crystallite sizes were obtained by calcination at several temperatures, ranging from 650 to 1200 degrees C The metastable t""-form of the tetragonal phase, exhibiting a cubic unit cell and tetragonal P4(2)/nmc spatial symmetry, was retained at room temperature in fine nanocrystalline powders, completely avoiding the presence of the stable rhombohedral beta phase. Differently, this phase was identified in samples calcined at high temperatures and its content increased with increasing crystallite size The critical maximum crystallite size for the retention of the mestastable t""-form resulted of about 35 nm (C) 2009 Elsevier B.V All rights reserved

Metastable Phase Diagram of Nanocrystalline ZrO(2)-Sc(2)O(3) Solid Solutions

We have investigated the crystal structures and phase transitions of nanocrystalline ZrO(2)-1 to -13 mol % Sc(2)O(3) by synchrotron X-ray powder diffraction and Raman spectroscopy. ZrO(2)-Sc(2)O(3) nanopowders were synthesized by using a stoichiometric nitrate-lysine get-combustion route. Calcination processes at 650 and at 850 degrees C yielded nanocrystalline materials with average crystallite sizes of (10 +/- 1) and (25 +/- 2) nm, respectively. Only metastable tetragonal forms and the cubic phase were identified, whereas the stable monoclinic and rhombohedral phases were not detected in the compositional range analyzed in this work. Differently from the results of investigations reported in the literature for ZrO(2)-Sc(2)O(3) materials with large crystallite sizes, this study demonstrates that, if the crystallite sizes are small enough (in the nanometric range), the metastable t ``-form of the tetragonal phase is retained. We have also determined the t`-t `` and t ``-cubic compositional boundaries at room temperature and analyzed these transitions at high temperature. Finally, using these results, we built up a metastable phase diagram for nanocrystalline compositionally homogeneous ZrO(2)-Sc(2)O(3) solid solutions that strongly differs from that previously determined from compositionally homogeneous ZrO(2)-Sc(2)O(3), Solid solutions with much larger crystallite sizes.

Footemineite, the Mn-analog of atencioite, from the Foote mine, Kings Mountain, Cleveland County, North Carolina, USA, and its relationship with other roscherite-group minerals

Footemineite, ideally Ca2Mn2+square Mn22+Be4(PO4)(6)(OH)(4)-6H(2)O, triclinic, is a new member of the roscherite group. It occurs on thin fractures crossing quartz-microcline-spodumene pegmatite at the Foote mine, Kings Mountain, Cleveland County, North Carolina, U.S.A. Associated minerals are albite, analcime, eosphorite, siderite/rhodochrosite, fairfieldite, fluorapatite, quartz, milarite, and pyrite. Footemineite forms prismatic to bladed generally rough to barrel-shaped crystals up to about 1.5 mm long and I mm in diameter. Its color is yellow, the streak is white, and the luster is vitreous to slightly pearly. Footemineite is transparent and non-fluorescent. Twinning is simple, by reflection, with twin boundaries across the length of the crystals. Cleavage is good on {0 (1) over bar1}) and {100}. Density (calc.) is 2.873 g/cm(3). Footemineite is biaxial (-), n(alpha) = 1.620(2), n(beta) = 1.627(2), n(gamma) = 1.634(2) (white light). 2V(obs) = 80 degrees, 2V(calc) = 89.6 degrees. Orientation: X boolean AND b similar to 12 degrees, Y boolean AND c similar to 15 degrees, Z boolean AND a similar to 15 degrees. Elongation direction is c, dispersion: r > v or r < v, weak. Pleochroism: beta (brownish yellow) > alpha = gamma (yellow). Mossbauer and IR spectra are given. The chemical composition is (EDS mode electron microprobe, Li and Be by ICP-OES, Fe3+:Fe2+ y Mossbauer, H2O by TG data, wt%): Li2O 0.23, BeO 9.54, CaO 9.43, SrO 0.23, BaO 0.24, MgO 0.18, MnO 26.16, FeO 2.77, Fe2O3 0.62, Al2O3 0.14, P2O5 36.58, SiO2 0.42, H2O 13.1, total 99.64. The empirical formula is (Ca1.89Sr0.03Ba0.02)Sigma(1.94)(Mn-0.90(2+)square(0.10))Sigma(1.00)(square 0.78Li0.17Mg0.05) Sigma(1.00)(Mn3.252+Fe0.432+ Fe0.093+Al0.03)Sigma(3.80) Be-4.30(P5.81Si0.08O24)[(OH)3.64(H2O)0.36]Sigma(4.00)center dot 6.00H(2)O . The strongest reflection peaks of the powder diffraction pattern [d, angstrom (1, %) (hkl)] are 9.575 (53) (010), 5.998 (100) (0 (1) over bar1), 4.848 (26) (021), 3.192 (44) (210), 3.003 (14) (0 (2) over bar2), 2.803 (38) ((1) over bar 03), 2.650 (29) ((2) over bar 02), 2.424 (14) (231). Single-crystal unit-cell parameters are a = 6.788(2), b = 9.972(3), c = 10.014(2) A, (x = 73.84(2), beta = 85.34(2), gamma = 87.44(2)degrees,V = 648.74 angstrom(3), Z = 1. The space group is P (1) over bar. Crystal structure was refined to R = 0.0347 with 1273 independent reflections (F > 2(5). Footemineite is dimorphous with roscherite, and isostructural with atencioite. It is identical with the mineral from Foote mine described as ""triclinic roscherite."" The name is for the Foote mine, type locality for this and several other minerals.