Roughness of Human Enamel Surface Submitted to Different Prophylaxis Methods

The purpose of this in vitro study was to evaluate alterations in the surface roughness and micromorphology of human enamel submitted to three prophylaxis methods. Sixty-nine caries-free molars with exposed labial surfaces were divided into three groups. Group I was treated with a rotary instrument set at a low speed, rubber clip and a mixture of water and pumice; group II with a rotary instrument set at a low speed, rubber cup and prophylaxis paste Herjos-F (Vigodent S/A Industria e Comercio, Rio de Janeiro, Brazil); and group III with sodium bicarbonate spray Profi II Ceramic (Dabi A dante Indtistrias Medico Odontologicas Ltda, Ribeirao Preto, Brazil). All procedures were performed by the same operator for 10 s, and samples were rinsed and stored in distilled water. Pre and post-treatment surface evaluation was completed using a surface profilometer (Perthometer S8P Marh, Perthen, Germany) in 54 samples. In addition, the other samples were coated with gold and examined in a scanning electron microscope (SEM). The results of this study were statistically analyzed with the paired t-test (Student), the Kruskal-Wallis test and the Dunn (5%) test. The sodium bicarbonate spray led to significantly rougher surfaces than the pumice paste. The use of prophylaxis paste showed no statistically significant difference when compared with the other methods. Based on SEM analysis, the sodium bicarbonate spray presented an irregular surface with granular material and erosions. Based on this study, it can be concluded that there was an increased enamel stuface roughness when teeth were treated with sodium bicarbonate spray when compared with teeth treated with pumice paste.

Network structures of Bis-GMA/TEGDMA resins differ in DC, shrinkage-strain, hardness and optical properties as a function of reducing agent

Objectives. To evaluate the influence of different tertiary amines on degree of conversion (DC), shrinkage-strain, shrinkage-strain rate, Knoop microhardness, and color and transmittance stabilities of experimental resins containing BisGMA/TEGDMA (3: 1 wt), 0.25wt% camphorquinone, 1wt% amine (DMAEMA, CEMA, DMPT, DEPT or DABE). Different light-curing protocols were also evaluated. Methods. DC was evaluated with FTIR-ATR and shrinkage-strain with the bonded-disk method. Shrinkage-strain-rate data were obtained from numerical differentiation of shrinkage-strain data with respect to time. Color stability and transmittance were evaluated after different periods of artificial aging, according to ISO 7491: 2000. Results were evaluated with ANOVA, Tukey, and Dunnett`s T3 tests (alpha = 0.05). Results. Studied properties were influenced by amines. DC and shrinkage-strain were maximum at the sequence: CQ < DEPT < DMPT <= CEMA approximate to DABE < DMAEMA. Both DC and shrinkage were also influenced by the curing protocol, with positive correlations between DC and shrinkage-strain and DC and shrinkage-strain rate. Materials generally decreased in L* and increased in b*. The strong exception was the resin containing DMAEMA that did not show dark and yellow shifts. Color varied in the sequence: DMAEMA < DEPT < DMPT < CEMA < DABE. Transmittance varied in the sequence: DEPT approximate to DABE < DABE approximate to DMPT approximate to CEMA < DMPT approximate to CEMA approximate to DMAEMA, being more evident at the wavelength of 400 nm. No correlations between DC and optical properties were observed. Significance. The resin containing DMAEMA showed higher DC, shrinkage-strain, shrinkage-strain rate, and microhardness, in addition to better optical properties. (C) 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.