Impact and fracture resistance of an experimental acrylic polymer with elastomer in different proportions

The purpose of this study was to evaluate the impact and fracture resistance of acrylic resins: a heat-polymerized resin, a high-impact resin and an experimental polymethyl methacrylate with elastomer in different proportions (10, 20, 40 and 60%). 120 specimens were fabricated and submitted to conventional heat-polymerization. For impact test, a Charpy-type impact tester was used. Fracture resistance was assessed with a 3-point bending test by using a mechanical testing machine. Ten specimens were used for each test. Fracture (MPa) and impact resistance values (J.m-1) were submitted to ANOVA - Bonferroni's test - 5% significance level. Materials with higher amount of elastomer had statistically significant differences regarding to impact resistance (p < 0.05). Fracture resistance was superior (p < 0.01) for high-resistance acrylic resin. The increase in elastomer concentration added to polymethyl methacrylate raised the impact resistance and decreased the fracture resistance. Processing the material by injection decreased its resistance to impact and fracture.

Influence of ferrule preparation with or without glass fiber post on fracture resistance of endodontically treated teeth

OBJECTIVE: This study evaluated the effect of ferrule preparation (Fp) on the fracture resistance of endodontically treated teeth, restored with composite resin cores with or without glass fiber posts. MATERIAL AND METHODS: Forty-four bovine teeth were sectioned 19 or 17 mm (2 mm ferrule) from the apex, endodontically treated and assigned to four groups (n = 11): Group 1: Fp and post; Group 2: Fp and without post; Group 3: without Fp and with post; Group 4: without Fp and without post. All specimens were restored with composite resin core and metal crown. Specimens were subjected to fracture resistance testing in a universal testing machine at a crosshead speed of 0.5 mm/min. The data were analyzed by two-way ANOVA and Tukey's tests (α=0.05). RESULTS: The mean fracture resistance values were as follows: Group 1: 573.3 N; Group 2: 552.5 N; Group 3: 275.3 N; Group 4: 258.6 N. Significantly higher fracture resistance was found for the groups with Fp (p<0.001). CONCLUSION: There was no statistically significant interaction between the "Fp" and "post" factors (p = 0.954). The ferrule preparation increased the fracture resistance of endodontically treated teeth. However, the use of glass fiber post showed no significant influence on the fracture resistance.

Long-term effects of rapid maxillary expansion on nasal area and nasal airway resistance

Background: Rapid maxillary expansion (RME) may improve the nasal respiratory pattern This study was performed to evaluate the effect of RME on the nasal cavity by acoustic rhinometry and computed rhinomanometry and to determine nasal and maxillary width by posteroanterior cephalometric radiography, up to 30 months after the orthodontic procedure Methods: Twenty-seven children with oral breathing, ranging in age from 7 to 70 years, and with mixed dentition were selected The children had unior bilateral posterior crossbite involving deciduous canines and the first permanent molars All subjects were submitted to nasofibroscopy, acoustic rhinometry, and computed rhinomanometry and posteroanterior cephalometric radiography at four different tunes, i e, before expansion, immediately, 90 days and 30 months after expansion Results: The mean linear left-to-right nasal cavity lateral prominence and left-to-right jugal ponds cephalometric measures increased considerably after expansion and this increase was maintained throughout the period of evaluation There was an immediate significant decrease in nasal resistance, up to 90 days after RME, but the nasal resistance increased 30 months after the procedure The acoustic rhinometry results did not show any difference in values throughout time Conclusion: RME significantly increased nasal and maxillary width as measured by frontal cephalometry, but the nasal mucosal effects were more subtle Also, the influence of RME on nasal resistance was not stable, and nasal resistance values returned to close to the initial ones after 30 months (Am J Rhinol Allergy 24, 161-165, 2010, doi 10.2500/ajra.2010.24.3440)

Fracture resistance of Class II glass-ionomer cement restorations

Purpose: To investigate in vitro the effect of retentive grooves, GIC type and insertion method on the fracture resistance of Class II glass-ionomer cement (GIC) restorations. Methods: Premolars were divided into 12 groups (n=10) according to three variables: retentive grooves [presence (PR) or absence AR)], GICs type [Ketac-Molar (KM), Fuji VIII (F8) and RelyX Luting (RX)], and insertion method [syringe injector (SI) or spoon excavator (SE)]. The specimens were subjected to fracture resistance test. Data were submitted to three-way ANOVA and multiple comparisons were performed using a Tukey test (P < 0.05). Results: Mean fracture resistance values (Kgf) +/- standard deviations (SD) were: KM (PR+SI) 65.66 +/- 2.5; KM (PR+SE) = 62.58 +/- 2.1; KM (AR+SI) = 57.11 +/- 1.9; KM (AR+SE) = 51.94 +/- 2.3; F8 (PR+SI) = 63.05 +/- 2.1; F8 (PR+SE) = 60.12 +/- 2.3; F8 (AR+SI) = 55.11 +/- 1.9; F8(AR+SE)=49.20 +/- 1.6; RX (PR+SI)=50.99 +/- 2.4; RX (PR+SE)=48.81 +/- 2.5; RX (AR+SI)=45.53 +/- 2.6; RX (AR+SE)=41.88 +/- 3.0. Statistically significant differences were observed among all the groups tested (P=0.001). There was significant difference when pooled means for GIC type were compared with retentive grooves (P=0.01) and when pooled means for retentive grooves were compared with insertion method (P=0.01).

Cutaneous Resistance to Evaporative Water Loss in Brazilian Rhinella (Anura: Bufonidae) from Contrasting Environments

Influenced by taxonomic position. For example, bufonids are regarded as exhibiting a permeable skin that seems typical for terrestrial anurans. However, this assumption is supported by information on only four bufonid species; therefore, the enormous ecological diversity of the family remains poorly Investigated. To assess whether variation in R(s) within related bufonids correlates with environmental aridity, we measured area-specific rates of EWL of two Brazilian populations of Rhinella granulosa (previously Bufo granulosus), one from the Atlantic Forest and other from the semi-arid Caatinga, and compared both with the forest species R. ornato. Rhinella granulosa from the Atlantic Forest had higher cutaneous resistance than conspecifics from Caatinga and R. ornata. Rhinella ornato presented the lowest cutaneous resistance values. However, Rs were very close to zero In all three populations. We conclude that enhanced Rs is not part of the suite of traits allowing R. granulosa to exploit the Caatinga, and that variation in R(s) within bufonids may relate to traits other than water conservation. Some Information on microhabitat occupation and ventral skin morphology supports the idea that exceptional abilities for detecting and taking up water may be the key factors enhancing the survival of R. granulosa, and possibly other bufonids, in xeric environments.

Investigation of the electrical and electrochemical properties of nanocomposites from V2O5, polypyrrole, and polyaniline

In this work, an investigation of the electrical and electrochemical properties responsible for the energy storage capability of nanocomposites has been carried out. We demonstrate that, in the case of the V2O5 xerogel and the nanocomposites polypyrrole (Ppy)/V2O5 and polyaniline (PANI)/V2O5, the quadratic logistic equation (QLE) can be used to fit the inverse of the resistance values as a function of the injected charge in non-steady-state conditions. This contributes to a phenomenological understanding of the lithium ion and electron transport. The departure of the experimental curve from the fitting observed for the V2O5 xerogel can be attributed to the trapping sites formed during the lithium electroinsertion, which was observed by electrochemical impedance spectroscopy. The amount of trapping sites was obtained on the basis of the QLE. Similar values used to fit the inverse of the resistance were also used to fit the absorbance changes, which is also associated with the small polaron hopping from the V(IV) to the V(V) sites. On the other hand, there was good agreement between the experimental and the theoretical data when the profile of the inverse of the resistance as a function of the amount of inserted lithium ions of the nanocomposites Ppy/V2O5 and PANI/ V2O5 was concerned. We suggest that the presence of the conducting polymers is responsible for the different electrical profile of the V2O5 xerogel compared with those of the nanocomposites. In the latter case, interactions between the lithium ions and oxygen atoms from V2O5 are shielded, thus decreasing the trapping effect of lithium ions in the V2O5 sites. The different values of the lithium ion diffusion coefficient into these intercalation materials are in agreement with this hypothesis.

Composition of Diesel Particles Influences Acute Pulmonary Toxicity: An Experimental Study in MICE

Ambient particles have been consistently associated with adverse health effects, yielding mainly high cardiorespiratory morbidity and mortality. Diesel engines represent a major source of particles in the urban scenario. We aimed to modify the composition of diesel particles, by means of different extraction procedures, to relate changes in chemical profile to corresponding indicators of respiratory toxicity. Male BALB/c mice were nasally instilled with saline, or with diesel particles, treated or not, and assigned to five groups: saline ( SHAM), intact diesel particles (DEP), and diesel particles previously treated with methanol ( METH), hexane ( HEX), or nitric acid (NA). Elemental composition and organic compounds were analyzed. Twenty-four hours after nasal instillation, respiratory parameters were measured and lung tissue was collected for histological analysis. Static elastance was significantly increased in groups DEP and MET in relation to the other groups. HEX and NA were different from DEP but not significantly different from SHAM and METH groups. The difference between dynamic and static elastance was increased in DEP, METH, and NA treatments; HEX was not statistically different from SHAM. DEP and METH groups presented significantly increased upper airways resistance, while DEP, METH, and NA showed higher peripheral airways resistance values. All groups had a higher total resistance than SHAM. DEP, METH, and NA showed significant increased infiltration of polymorphonuclear cells. In conclusion, diesel particles treated with hexane ( HEX) resulted in a respiratory-system profile very similar to that in SHAM group, indicating that hexane treatment attenuates pulmonary inflammation elicited by diesel particles.

Physical properties of edible films based on cassava starch as affected by the plasticizer concentration

The aim of this work was to investigate the effect of glycerol contents on physical properties of cassava starch films. The films were prepared from film-forming solutions (FFS) with 2g cassava starch/100g water and 0, 15, 30 and 45g glycerol/100g starch, and were analysed to determine its mechanical properties by tensile tests, the glass-transition temperature (T-g) by differential scanning calorimetry (DSC) and the crystallinity by X-ray diffraction (XRD). The infrared spectra of the films were also recorded. The resistance values of the films decreased, while those of the elasticity increased with an increase in glycerol concentration due to the plasticizer effect of glycerol, which was also observed in DSC curves. The T-g of the films prepared decreased with the glycerol content. However, for samples with 30 and 45g glycerol/100g starch, two T-g curves were observed, probably due to a phase separation phenomenon. According to the XRD diffractograms, the films with 0 and 15gglycerol/100g starch presented an amorphous character, but some tendency to show crystalline peaks were observed for films with 30 and 45g glycerol/100g starch. The results obtained with Fourier transform infrared (FTIR) corroborated these observations. Copyright (C) 2007 John Wiley & Sons, Ltd.

Physical properties of palm fruits processed with tools by wild bearded capuchins (Cebus libidinosus)

Habitually, capuchin monkeys access encased hard foods by using their canines and premolars and/or by pounding the food on hard surfaces. Instead, the wild bearded capuchins (Cebus libidinosus) of Boa Vista (Brazil) routinely crack palm fruits with tools. We measured size, weight, structure, and peak-force-at-failure of the four palm fruit species most frequently processed with tools by wild capuchin monkeys living in Boa Vista. Moreover, for each nut species we identify whether peak-force-at-failure was consistently associated with greater weight/volume, endocarp, thickness, and structural complexity. The goals of this study were (a) to investigate whether these palm fruits are difficult, or impossible, to access other than with tools and (b) to collect data on the physical properties of palm fruits that are comparable to those available for the nuts cracked open with tools by wild chimpanzees. Results showed that the four nut species differ in terms of peak-force-at-failure and that peak-force-at-failure is positively associated with greater weight (and consequently volume) and apparently with structural complexity (i.e. more kernels and thus more partitions); finally for three out of four nut species shell thickness is also positively associated with greater volume. The finding that the nuts exploited by capuchins with tools have very high resistance values support the idea that tool use is indeed mandatory to crack them open. Finally, the peak-force-at-failure of the piassava nuts is similar to that reported for the very tough panda nuts cracked open by wild chimpanzees; this highlights the ecological importance of tool use for exploiting high resistance foods in this capuchin species.

In vitro wear resistance of three types of polymethyl methacrylate denture teeth

The wear resistance of denture teeth is important to the longevity of removable prostheses of edentulous patients. The ability of denture teeth to maintain a stable occlusal relationship over time may be influenced by this property. The purpose of this in vitro study was to evaluate the wear resistance of polymethyl methacrylate (PMMA) denture teeth based on their chemical composition when opposed by a ceramic antagonist. The maxillary canines (n=10) of 3 PMMA denture teeth (Trubyte Biotone, cross-linked PMMA; Trilux, highly cross-linked IPN (interpenetrating polymer network)-PMMA; and Vivodent, highly cross-linked PMMA) were secured in an in vitro 2-body wear-testing apparatus that produced sliding contact of the specimens (4.5 cycles/s, sliding distance of 20 mm, under 37°C running water) against glazed or airborne particle abraded ceramic. Wear resistance was measured as height loss (mm) under 300 g (sliding force) after 100,000 cycles, using a digital measuring microscope. Mean values were analyzed by 2-way ANOVA and Tukey's test (a=0.05). The wear of Trubyte Biotone (0.93 ± 0.14 mm) was significantly higher than that of both other types of teeth tested against abraded ceramic (p<0.05). The Vivodent tooth (0.64 ± 0.17 mm) exhibited the best wear resistance among the denture teeth tested against airborne particle abraded ceramic. There were no statistically significant differences (p>0.05) in wear among the 3 denture teeth evaluated against glazed ceramic. Trilux and Vivodent teeth tested against either glazed or airborne particle abraded ceramic did not differ significantly from each other (p<0.05). All teeth showed significantly more wear against airborne particle abraded ceramic than against glazed ceramic (p<0.05). In conclusion, the three types of PMMA denture teeth presented significantly different wear resistance against the abraded ceramic. The high-strength PMMA denture teeth were more wear-resistant than the conventional PMMA denture tooth.

Abrasion wear resistance of different artificial teeth opposed to metal and composite antagonists

One of the most important properties of artificial teeth is the abrasion wear resistance, which is determinant in the maintenance of the rehabilitation's occlusal pattern. OBJECTIVES: This in vitro study aims to evaluate the abrasion wear resistance of 7 brands of artificial teeth opposed to two types of antagonists. MATERIAL AND METHODS: Seven groups were prepared with 12 specimens each (BIOLUX & BL, TRILUX & TR, BLUE DENT & BD, BIOCLER & BC, POSTARIS & PO, ORTHOSIT & OR, GNATHOSTAR & GN), opposed to metallic (M & nickel-chromium alloy), and to composite antagonists (C & Solidex indirect composite). A mechanical loading device was used (240 cycles/min, 4 Hz speed, 10 mm antagonist course). Initial and final contours of each specimen were registered with aid of a profile projector (20x magnification). The linear difference between the two profiles was measured and the registered values were subjected to ANOVA and Tukey's test. RESULTS: Regarding the antagonists, only OR (M = 10.45 ± 1.42 µm and C = 2.77 ± 0.69 µm) and BC (M = 6.70 ± 1.37 µm and C = 4.48 ± 0.80 µm) presented statistically significant differences (p < 0.05). Best results were obtained with PO (C = 2.33 ± 0.91 µm and M = 1.78 ± 0.42 µm), followed by BL (C = 3.70 ± 1.32 µm and M = 3.70 ± 0.61 µm), statistically similar for both antagonists (p>0.05). Greater result variance was obtained with OR, which presented the worse results opposed to Ni-Cr (10.45 ± 1.42 µm), and results similar to the best ones against composite (2.77 ± 0.69 µm). CONCLUSIONS: Within the limitations of this study, it may be concluded that the antagonist material is a factor of major importance to be considered in the choice of the artificial teeth to be used in the prosthesis.

Body trunk fat and insulin resistance in post-pubertal obese adolescents

CONTEXT AND OBJECTIVE: Insulin resistance is a metabolic disorder commonly associated with excess body fat accumulation that may increase chronic disease risk. The present study was undertaken to evaluate the relationship between body composition and insulin resistance among obese adolescents. DESIGN AND SETTING: Cross-sectional study, at the Adolescence Center, Pediatric Department, Universidade Federal de São Paulo. METHODS: Body composition was assessed using dual-energy X-ray absorptiometry. Dietary intake was evaluated using a three-day dietary record. The biochemical evaluation comprised glucose, insulin, serum lipid, leptin and ghrelin measurements. Insulin resistance was calculated by means of the homeostasis model assessment of insulin resistance (HOMA-IR). RESULTS: Forty-nine post-pubertal obese adolescents participated in the study: 12 boys and 37 girls of mean age 16.6 (1.4) years and mean body mass index (BMI) of 35.0 (3.9) kg/m². The mean glucose, insulin and HOMA values were 90.3 (6.4) mg/dl, 16.6 (8.1) µIU/ml and 3.7 (1.9), respectively. Hyperinsulinemia and insulin resistance were observed in 40.2% and 57.1% of the subjects, respectively. Adolescents with insulin resistance had higher BMI and body trunk fat. There was a trend towards higher leptin concentration in obese individuals with insulin resistance. Insulin resistance was positively correlated with body trunk fat, BMI, body fat mass (kg), leptin and body fat percentage. Furthermore, there was a negative correlation between HOMA-IR and lean body mass. The body composition predicted 30% of the HOMA-IR levels, according to linear regression models. CONCLUSION: Body trunk fat was significantly associated with insulin resistance, demonstrating the clinical importance of abdominal obesity during adolescence.

SALIVARY HORMONE AND IMMUNE RESPONSES TO THREE RESISTANCE EXERCISE SCHEMES IN ELITE FEMALE ATHLETES

Nunes, JA, Crewther, BT, Ugrinowitsch, C, Tricoli, V, Viveiros, L, de Rose Jr, D, and Aoki, MS. Salivary hormone and immune responses to three resistance exercise schemes in elite female athletes J Strength Cond Res 25(8): 2322-2327, 2011-This study examined the salivary hormone and immune responses of elite female athletes to 3 different resistance exercise schemes. Fourteen female basketball players each performed an endurance scheme (ES-4 sets of 12 reps, 60% of 1 repetition maximum (1RM) load, 1-minute rest periods), a strength-hypertrophy scheme (SHS-1 set of 5RM, 1 set of 4RM, 1 set of 3RM, 1 set of 2RM, and 1set of 1RM with 3-minute rest periods, followed by 3 sets of 10RM with 2-minute rest periods) and a power scheme (PS-3 sets of 10 reps, 50% 1RM load, 3-minute rest periods) using the same exercises (bench press, squat, and biceps curl). Saliva samples were collected at 07:30 hours, pre-exercise (Pre) at 09:30 hours, postexercise (Post), and at 17:30 hours. Matching samples were also taken on a nonexercising control day. The samples were analyzed for testosterone, cortisol (C), and immunoglobulin A concentrations. The total volume of load lifted differed among the 3 schemes (SHS > ES > PS, p < 0.05). Postexercise C concentrations increased after all schemes, compared to control values (p < 0.05). In the SHS, the postexercise C response was also greater than pre-exercise data (p < 0.05). The current findings confirm that high-volume resistance exercise schemes can stimulate greater C secretion because of higher metabolic demand. In terms of practical applications, acute changes in C may be used to evaluate the metabolic demands of different resistance exercise schemes, or as a tool for monitoring training strain.

Atenolol blunts blood pressure increase during dynamic resistance exercise in hypertensives

center dot Dynamic resistance exercise promotes a sizeable increase in blood pressure during its execution in non medicated hypertensives. WHAT THIS STUDY ADDS center dot Atenolol not only decreases blood pressure level but also mitigates the increase of blood pressure during dynamic resistance exercise in hypertensive patients. An increase in blood pressure during resistance exercise might be at least in part attributed to an increase in cardiac output. AIMS This study was conducted to determine whether atenolol was able to decrease BP level and mitigate BP increase during dynamic resistance exercise performed at three different intensities in hypertensives. METHODS Ten essential hypertensives (systolic/diastolic BP between 140/90 and 160/105 mmHg) were blindly studied after 6 weeks of placebo and atenolol. In each phase, volunteers executed, in a random order, three protocols of knee-extension exercises to fatigue: (i) one set at 100% of 1 RM; (ii) three sets at 80% of 1 RM; and (iii) three sets at 40% of 1 RM. Intra-arterial radial blood pressure was measured throughout the protocols. RESULTS Atenolol decreased systolic BP maximum values achieved during the three exercise protocols (100% = 186 +/- 4 vs. 215 +/- 7, 80% = 224 +/- 7 vs. 247 +/- 9 and 40% = 223 +/- 7 vs. 252 +/- 16 mmHg, P < 0.05). Atenolol also mitigated an increase in systolic BP in the first set of exercises (100% = +38 +/- 5 vs. +54 +/- 9; 80% = +68 +/- 11 vs. +84 +/- 13 and 40% = +69 +/- 7 vs. +84 +/- 14, mmHg, P < 0.05). Atenolol decreased diastolic BP values and mitigated its increase during exercise performed at 100% of 1 RM (126 +/- 6 vs. 145 +/- 6 and +41 +/- 6 vs. +52 +/- 6, mmHg, P < 0.05), but not at the other exercise intensities. CONCLUSIONS Atenolol was effective in both reducing systolic BP maximum values and mitigating BP increase during resistance exercise performed at different intensities in hypertensive subjects.

Finger blood pressure during leg resistance exercise

Blood pressure (BP) assessment during resistance exercise can be useful to avoid high BP, reducing cardiovascular risk, especially in hypertensive individuals. However, non-invasive accurate technique for this purpose is not available. The aim of this study was to compare finger photoplethysmographic (FPP) and intra-arterial BP values and responses during resistance exercise. Eight non-medicated hypertensive subjects (5 males, 30-60 years) were evaluated during pre-exercise resting period and during three sets of the knee extension exercise performed at 80% of 1RM until fatigue. BP was measured simultaneously by FPP and intra-arterial methods. Data are mean +/- SD. Systolic BP was significantly higher with FPP than with intra-arterial: at pre-exercise (157 +/- 13 vs. 152 +/- 10 mmHg; p < 0.01) and the mean (202 +/- 29 vs. 198 +/- 26 mmHg; p < 0.01), and the maximal (240 +/- 26 vs. 234 +/- 16 mmHg; p < 0.05) values achieved during exercise. The increase in systolic BP during resistance exercise was similar between FPP and intra-arterial (+ 73 +/- 29 vs. + 71 +/- 18 mmHg; p = 0.59). Diastolic BP values and increases were lower with FPP. In conclusion, FPP provides similar values of BP increment during resistance exercise than intra-arterial method. However, it overestimates by 2.6 +/- 6.1% the maximal systolic BP achieved during this mode of exercise and underestimates by 8.8 +/- 5.8% the maximal diastolic BP.