Long-term stability of dentin matrix following treatment with various natural collagen cross-linkers

Objectives: Collagen disorganization is one of the main degradation patterns found in unsuccessful adhesive restorations. The hypothesis of this study was that pretreatment using natural collagen cross-linking agents rich in proanthocyanidin (PA) would improve mechanical properties and stability over time of the dentin collagen and, thus, confer a more resistant and lasting substrate for adhesive restorations. Methods: PA-based extracts, from grape seed (GSE), cocoa seed (CSE), cranberry (CRE), cinnamon (CNE) and acai berry (ACE) were applied over the demineralized dentin. The apparent elastic modulus (E) of the treated dentin collagen was analyzed over a 12 month period. Specimens were immersed in the respective solution and E values were obtained by a micro-flexural test at baseline, 10, 30, 60, 120 and 240 min. Samples were stored in artificial saliva and re-tested after 3, 6 and 12 months. Data was analyzed using ANOVA and Tukey test. Results: GSE and CSE extracts showed a time-dependent effect and were able to improve [240 min (MPa): GSE = 108.96 +/- 56.08: CSE = 59.21 +/- 24.87] and stabilize the E of the organic matrix [12 months (MPa): GSE = 40.91 +/- 19.69; CSE = 42.11 +/- 13.46]. CRE and CNE extracts were able to maintain the E of collagen matrices constant over 12 months [CRE = 11.17 +/- 7.22; CNE = 9.96 +/- 6.11; MPa]. ACE (2.64 +/- 1.22 MPa) and control groups immersed in neat distilled water (1.37 +/- 0.69 MPa) and ethanol-water (0.95 +/- 0.33 MPa) showed no effect over dentin organic matrix and enable their degradation and reduction of mechanical properties. Significance: Some PA-based extracts were capable of improving and stabilizing collagen matrices through exogenous cross-links induction. (C) 2011 Elsevier Ltd. All rights reserved.

Mechanical characterization of proanthocyanidindentin matrix interaction

Objectives To characterize the properties of dentin matrix treated with two proanthocyanidin rich cross-linking agents and their effect on dentin bonded interfaces. Methods Sound human molars were cut into 0.5mm thick dentin slabs, demineralized and either treated with one of two cross-linking agents (grape seedGSE and cocoa seedCOE extracts) or left untreated. The modulus of elasticity of demineralized dentin was assessed after 10 or 60min and the swelling ratio after 60min treatment. Bacterial collagenase was also used to assess resistance to enzymatic degradation of samples subjected to ultimate tensile strength. The effect of GSE or COE on the resindentin bond strength was evaluated after 10 or 60min of exposure time. Data were statistically analyzed at a 95% confidence interval. Results Both cross-linkers increased the elastic modulus of demineralized dentin as exposure time increased. Swelling ratio was lower for treated samples when compared to control groups. No statistically significant changes to the UTS indicate that collagenase had no effect on dentin matrix treated with either GSE or COE. Resindentin bonds significantly increased following treatment with GSE regardless of the application time or adhesive system used. Significance Increased mechanical properties and stability of dentin matrix can be achieved by the use of PA-rich collagen cross-linkers most likely due to the formation of a PAcollagen complex. The short term resindentin bonds can be improved after 10min dentin treatment.(C) 2010 Academy of Denta lMaterials. Published by Elsevier Ltd. All rights reserved.

Solubility study of phytochemical cross-linking agents on dentin stiffness

Objectives: The effects of interactions between cross-linking proanthocyanidins (PA) in polar solvents and type-I collagen of demineralized dentin were investigated. Methods: Three PA-rich extracts, two from grape seed (GSEP and GSES) and one from cocoa (COE), were dissolved (water, ethanol:water and acetone:water) and analyzed for their ability to increase the modulus of elasticity of demineralized dentin. Sound dentin beams (0.5 mm x 1.7 mm x 7 mm) were fully demineralized and divided into 12 groups according to the type of cross-linking agent and solvents used. Specimens were immersed in the respective solutions and tested at baseline, 10, 30, 60, 120 and 240 min. Results: The elastic modulus (EM) of dentin was significantly increased by the PA treatment regardless of time (p < 0.05 for all times). The extracts showed different solubility in different solvents. GSEP showed the highest increase in EM when diluted in distilled water and acetone at all exposure times. Both GSEs showed superior results when diluted in distilled water and after 4 h of treatment, while COE produced strongest enhancement when dissolved in ethanol:water. Conclusions: The results indicates that herbal extraction process and other pharmacognostic parameters have an important influence on extract solubility as well as constitution and, consequently, on the PA-dentin matrix interaction. (C) 2010 Elsevier Ltd. All rights reserved.