Correlation between vertical misfits and stresses transmitted to implants from metal frameworks

An inappropriate prosthetic fit could cause stress over the interface implant/bone. The objective of this study was to compare stresses transmitted to implants from frameworks cast using different materials and to investigate a possible correlation between vertical misfits and these stresses. Fifteen one-piece cast frameworks simulating bars for fixed prosthesis in a model with five implants were fabricated and arranged into three different groups according to the material used for casting: CP Ti (commercially pure titanium), Co-Cr (cobalt-chromium) or Ni-Cr-Ti (nickel-chromium-titanium) alloys. Each framework was installed over the metal model with all screws tightened to a 10 N cm torque and then, vertical misfits were measured using an optical microscope. The stresses transmitted to implants were measured using quantitative photoelastic analysis in values of maximum shear stress (T), when each framework was tightened to the photoelastic model to a 10 N cm standardized torque. Stress data were statistically analyzed using one-way ANOVA and Tukey`s test and correlation tests were performed using Pearson`s rank correlation (alpha = 0.05). Mean and standard deviation values of vertical misfit are presented for CP Ti (22.40 +/- 9.05 mu m), Co-Cr (66.41 +/- 35.47 mu m) and Ni-Cr-Ti (32.20 +/- 24.47 mu m). Stresses generated by Co-Cr alloy (tau = 7.70 +/- 2.16 kPa) were significantly higher than those generated by CP Ti (tau = 5.86 +/- 1.55 kPa, p = 0.018) and Ni-Cr-Ti alloy (tau =5.74 +/- 3.05 kPa, p = 0.011), which were similar (p = 0.982). Correlations between vertical misfits and stresses around the implants were not significant as for any evaluated materials. (C) 2011 Elsevier Ltd. All rights reserved.

Stress distribution in orthodontic mini-implants

The objective of this study was to evaluate the stress distribution in the resin in contact with the spirals of cylindrical and conical mini-implants, when submitted to lateral load and insertion torsion. A photoelastic model was fabricated using transparent gelatin to simulate the alveolar bone. The model was observed with a plane polariscope and photographically recorded before and after activation of the two screws with a lateral force and torsion. The lateral force application caused bending moments on both mini-implants, with the uprising of fringes or isochromatics, characteristics of stresses, along the threads of the mini-implants and in the apex. When the torsion was exerted in the mini-implants, a great concentration of stress upraised close to the apex. The conclusion was that, comparing conical with cylindrical mini-implants under lateral load, the stresses were similar on the traction sides. The differences appear (1) on the apex, where the cylindrical mini-implant showed a greater concentration of stress, and (2) along the spirals, in the compression side, where the conical mini-implant showed a greater concentration of stress. The greater part of the stress produced by both mini-implants, after torsion load in insertion, were concentrated on the apex. With the cylindrical mini-implant, the greater concentration of tension was close to the apex, while with the conical one, the stresses were distributed along a greater amount of apical threads.