Modeling Adsorption Processes of Poly-p-phenylenevinylene Precursor and Sodium Acid Dodecylbenzenesulfonate onto Layer-by-Layer Films Using a Langmuir-type Metastable Equilibrium Model

The adsorption kinetics curves of poly(xylylidene tetrahydrothiophenium chloride) (PTHT), a poly-p-phenylenevinylene (PPV) precursor, and the sodium salt of dodecylbenzene sulfonic acid (DBS), onto (PTHT/DBS)(n) layer-by-layer (LBL) films were characterized by means of UV-vis spectroscopy. The amount of PTHT/DBS and PTHT adsorbed on each layer was shown to be practically independent of adsorption time. A Langmuir-type metastable equilibrium model was used to adjust the adsorption isotherms data and to estimate adsorption/desorption coefficients ratios, k = k(ads)/k(des), values of 2 x 10(5) and 4 x 10(6) for PTHT and PTHT/DBS layers, respectively. The desorption coefficient has been estimated, using literature values for poly(o-methoxyaniline) desorption coefficient, as was found to be in the range of 10(-9) to 10(-6) s(-1), indicating that quasi equilibrium is rapidly attained.

Controlling the absorption and emission properties of polyparaphenylenevinylene films

In this work we used the conversion process of a precursor polymer into polyparaphenylenevinylene (PPV) at low temperatures in order to control the effective conjugation degree of spin-casted PPV films. The absorption and emission spectra of the films were studied by following a partial substitution of chloride counterions from poly(xylylidene tetrahydrothiophenium chloride) (PTHT), used as a precursor, by sodium acid dodecyl benzenesulfonate (DBS), added as a surfactant salt. Upon controlling the DBS amount and conversion temperature (T-c) of PTHT/DBS to PPV films, the band gap of PPV changed from 409 to 506 nm, and 505 to 532 nm, values obtained from absorbance and emission measurements, respectively. Based on these experimental data, we proposed a physical model which represents the chemical structure of PPV as a distribution of conjugated chain segments (like oligomers) alternated by non-conjugated segments (structural defects and/or from the precursor polymer). (C) 2008 Elsevier B.V. All rights reserved.

Detection of microwaves using the organic semiconductor poly(p-phenylenevinylene)

We report a new procedure to convert the polymer precursor poly(xylylidene tetrahydrothiophenium chloride) (PTHT) into poly(p-phenylenevinylene) (PPV) using microwave irradiation. Spin-coated PTHT films were irradiated at room temperature under ambient conditions in a commercial microwave oven, with varying power from 20W to 100W. Complete conversion was reached within only 5 min of irradiation for powers above 50W, yielding PPV films with absorption and photoluminescence spectra that are practically indistinguishable from the spectra of thermally converted PPV films, which require ca. 2 h of a high temperature (similar to 200 degrees C) thermal treatment. In addition to a much faster conversion procedure, the irradiation with microwaves led to a red shift in the absorption spectrum of a PTHT film, which varied linearly with the time of irradiation. These films can then be used as low-cost, easy-to-use detectors of microwaves. (C) 2010 Elsevier B.V. All rights reserved.

Influence from the sulfonate group (RSO(3)(-)) on the conversion process and emission efficiency of poly(p-phenylene vinylene)

The discovery of an alternative route to convert poly(xylyliden tetrahydrothiophenium chloride) (PTHT) into poly(p-phenylene vinylene) (PPV) using dodecylbenzenesulfonate (DBS) has allowed the formation of ultrathin films with unprecedented control of architecture and emission properties. In this work, we show that this route may be performed with several sufonated compounds where RSO(3)(-) replaces the counter-ion (Cl(-)) of PTHT, some of which are even more efficient than DBS. Spin-coating films were produced from PTHT and azo-dye molecules, an azo-polymer and organic salts as counter-ions of PTHT. The effects of the thermal annealing step of PTHT/RSO(3)(-) films at 110 and 230 degrees C were monitored by measuring the absorption and emission spectra. The results indicate that the exchange of the counterion Cl(-) of PTHT by a linear long chain with RSO(3)(-) group is a general procedure to obtain PPV polymer at lower conversion temperature (ca. 110 degrees C) with significant increase in the emission efficiency, regardless of the chemical position and the number of sulfonate groups. With the enhanced emission caused by Congo Red and Tinopal as counter-ions, it is demonstrated that the new synthetic route is entirely generic, which may allow accurate control of conversion and emission properties. (C) 2010 Elsevier B.V. All rights reserved.