The Effects of Different Loading Times on the Bone Response Around Dental Implants: A Histomorphometric Study in Dogs

Purpose: The aim of this study was to evaluate, through histomorphometric analysis, the effect that different loading times would have on the bone response around implants. Materials and Methods: Three Replace Select implants were placed on each side of the mandible in eight dogs (n = 48 implants). One pair of implants was selected for an immediate loading protocol (IL). After 7 days, the second pair of implants received prostheses for an early loading protocol (EL). Fourteen days after implant placement, the third pair of implants received prostheses for advanced early loading (AEL). Following 12 weeks of prosthetics, counted following the positioning of the metallic crowns for the AEL group, the animals were sacrificed and the specimens were prepared for histomorphometric analysis. The differences between loading time in the following parameters were evaluated through analysis of variance: bone-to-implant contact, bone density, and crestal bone loss. Results: The mean percentage of bone-to-implant contact for IL was 77.9% +/- 1.71%, for EL it was 79.25% +/- 2.11%, and for AEL it was 79.42% +/- 1.49%. The mean percentage of bone density for IL was 69.97% +/- 3.81%, for EL it was 69.23% +/- 5.68%, and for AEL it was 69.19% +/- 2.90%. Mean crestal bone loss was 1.57 +/- 0.22 mm for IL, 1.23 +/- 0.19 mm for EL, and 1.17 +/- 0.32 mm for AEL. There was no statistical difference for any of the parameters evaluated (P > .05). Conclusion: Different early loading times did not seem to significantly affect the bone response around dental implants. INT J ORAL MAXILLOFAC IMPLANTS 2010;25:473-481

Studies on the resonance Raman spectra of polyaniline obtained with near-IR excitation

The effects of near-IR (NIR) laser power over the Raman spectra of poly(aniline) emeraldine salt (PANIES) and base (PANI-EB) were investigated. The reasons for the existence of several bands from 1324 to 1500 cm-1 in the Raman spectra of poly(aniline) obtained at NIR region were also studied. The bands from 1324 to 1375 cm-` were associated to vC-N of polarons with different conjugation lengths and the bands from 1450 to 1500 cm-1 in Raman spectra of PANI emeraldine and pernigraniline base forms were correlated to vC=N modes associated with quinoid units having different conjugation lengths. The increase of laser power at 1064.0 run causes the deprotonation of PANI-ES and the formation of cross-linking segments having phenazine and/or oxazine rings. For PANI-EB only a small spectral change is observed when the laser power is increased, owing to the low absorption of this form in the NIR region. Copyright (c) 2007 John Wiley & Sons, Ltd.