Corrosion behavior of Ti-xNb-13Zr alloys in Ringer`s solution

Ti-6Al-4V alloy has been widely used in restorative surgery due to its high corrosion resistance and biocompatibility. Nevertheless, some studies showed that V and Al release in the organism might induce cytotoxic effects and neurological disorders, which led to the development of V-free alloys and both V- and Al-free alloys containing Nb, Zr, Ta, or Mo. Among these alloys, Ti-13Nb-13Zr alloy is promising due to its better biomechanical compatibility than Ti-6Al-4V. In this work, the corrosion behavior of Ti, Ti-6Al-4V, and Ti-xNb-13Zr alloys (x=5, 13, and 20) was evaluated in Ringer`s solution (pH 7.5) at 37 degrees C through open-circuit potential measurements, potentiodynamic polarization, and electrochemical impedance spectroscopy. Spontaneous passivity was observed for all materials in this medium. Low corrosion current densities (in the order of 10(-7) A/cm(2)) and high impedance values (in the order of 10(5) Omega cm(2) at low frequencies) indicated their high corrosion resistance. EIS results showed that the passivating films were constituted of an outer porous layer (very low resistance) and an inner compact layer (high resistance), the latter providing the corrosion resistance of the materials. There was evidence that the Ti-xNb-13Zr alloys were more corrosion resistant than both Ti and Ti-6Al-4V in Ringer`s solution.

The electrochemical behaviour of Ti-13Nb-13Zr alloy in various solutions

The electrochemical behaviour of a near-beta Ti-13Nb-13Zr alloy for the application as implants was investigated in various solutions. The electrolytes used were 0.9 wt% NaCl solution, Hanks` solution and a culture medium known as minimum essential medium (MEM) composed of salts, vitamins and amino acids, all at 37 degrees C. The electrochemical behaviour was investigated by the following electrochemical techniques: open circuit potential measurements as a function of time, electrochemical impedance spectroscopy (EIS) and determination of polarisation curves. The obtained results showed that the Ti alloy was passive in all electrolytes. The EIS results were analysed using an equivalent electrical circuit representing a duplex structure oxide layer, composed of an inner barrier layer, mainly responsible for the alloy corrosion resistance, and an outer and porous layer that has been associated to osteointegration ability. The properties of both layers were dependent on the electrolyte used. The results suggested that the thickest porous layer is formed in the MEM solution whereas the impedance of the barrier layer formed in this solution was the lowest among the electrolytes used. The polarisation curves showed a current increase at potentials around 1300 mV versus saturated calomel electrode (SCE), and this increase was also dependent on the electrolyte used. The highest increase in current density was also associated to the MEM solution suggesting that this is the most aggressive electrolyte to the Ti alloy among the three tested solutions.

Use of SECM to study the electrochemical behavior of DIN 1.4575 superferritic stainless steel aged at 475 degrees C

In order to lower the excessive costs of metallic prosthesis materia Is alternatives to Ti and Ti alloys have been searched. in this study, the corrosion resistance of the DIN 1.4575 superferritic stainless steel, either solution annealed or solution annealed and aged at 475 degrees C for periods varying from 100 to 1080 h, was investigated by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization methods in Hanks` solution. The solution annealed and the aged for 1080 h samples were also tested using scanning electrochemical microscopy (SECM) in a 0.1 mol/L NaCl solution at 25 degrees C. The EIS results showed that the corrosion resistance of the DIN 1.4575 steel decreases with heat treatment time at 475 degrees C probably due to alpha prime formation. Besides the diminution of the overall impedance values, the low frequency limit of the Nyquist diagrams show a progressive change from an almost capacitive response to a resistive behavior as the heat treatment time increases. Pitting corrosion resistance also decreased with aging time at 475 degrees C.