A hybrid material assembled by anthocyanins from acai fruit intercalated between niobium lamellar oxide

Organic-inorganic hybrid materials can be prepared dispersing organic species into well-defined inorganic nanoblocks. This paper describes the immobilization of natural dyes from the extract of the Brazilian acai-fruit into two types of layered hexaniobate precursors derived from H(2)K(2)Nb(6)O(17): (i) colloidal dispersion of niobate exfoliated nanoparticles and (ii) niobate pre-intercalated with tetraethylammonium cations (TEA(+)). The restacking of exfoliated particles in the presence of acai anthocyanins promotes their intercalation and produces stacked layers showing large basal spacing (ca. 50 angstrom). The TEA(+) pre-intercalated niobate provides particles with lower content of dye species than the exfoliated precursor but with higher degree of organization and regularity according to X-ray diffraction data and images obtained by electron microscopies. Vibrational (FTIR and Raman) and (13)C NMR spectroscopies indicate the presence of flavylium cations in the hybrid materials and spectral profiles characteristic of glycosylated anthocyanidins. According to thermal analysis results, the purplish hybrids materials are more stable than the free acai-dyes. One hybrid sample was heated under air up to 170 degrees C and maintained at this temperature for 240 min. No weight loss events were observed and the sample retained its original color, indicating that the intercalation of anthocyanin into hexaniobate increases its thermal stability. Considering the structural, chemical, optical and thermal properties of the synthesized hybrid materials, they might be good candidates to be investigated for future specialized applications.

Intralamellar structural modifications related to the proton exchanging in K(4)Nb(6)O(17) layered phase

Basic structural aspects about the layered hexaniobate of K(4)Nb(6)O(17) composition and its proton-exchanged form were investigated mainly by spectroscopic techniques. Raman spectra of hydrous K(4)Nb(6)O(17) and H(2)K(2)Nb(6)O(17)center dot H(2)O show significant modifications in the 950-800 cm(-1) region (Nb-O stretching mode of highly distorted NbO(6) octahedra). The band at 900 cm(-1) shifts to 940 cm(-1) after the replacement of K(+) ion by proton. Raman spectra of the original materials and the related deuterated samples are similar suggesting that no isotopic effect occurs. Major modifications were observed when H(2)K(2)Nb(6)O(17) was dehydrated: the relative intensity of the band at 940 cm(-1) decreases and new bands seems to be present at about 860-890 cm(-1). The H(+) ions should be shielded by the hydration sphere what preclude the interaction with the layers. Removing the water molecules, H(+) ions can establish a strong interaction with oxygen atoms, decreasing the bond order of Nb-O linkage. X-ray absorption near edge structure studies performed at Nb K-edge indicate that the niobium coordination number and oxidation state remain identical after the replacement of potassium by proton. From the refinement of the fine structure, it appears that the Nb-Nb coordination shell is divided into two main contributions of about 0.33 and 0.39 nm, and interestingly the population, i.e., the number of backscattering atoms is inversed between the two hexaniobate materials. 2009 Elsevier Ltd. All rights reserved.

Lithium Ion Electro-Insertion and Spectroelectrochemical Properties of Films from Hexaniobate

Layer-by-layer (LbL) films from K(2)Nb(6)O(17)(2-) and polyallylamine (PAH) and dip-coating films of H(2)K(2)Nb(6)O(17) were prepared on a fluorine-doped tin-oxide (FTO)-coated glass. The atomic force microscopy (AFM) images were carried out for morphological characterization of both materials. The real surface area and the roughness factor were determined on the basis of pseudocapacitive processes involved in the electroreduction/electrooxidation of gold layers deposited on these films. Next, lithium ion insertion into these materials was examined by means of electrochemical and spectroelectrochemical measurements. More specifically, cyclic voltammetry and current pulses under visible light beams were used to investigate mass transport and chromogenic properties. The lithium ion diffusion coefficient (D(Li)) within the LbL matrix is significantly higher than that within the dip-coating film, ensuring high storage capacity of lithium ions in the self-assembled electrode. Contrary to the LbL film, the potentiodynamic profile of absorbance change (Delta A) as a function of time is not similar to that obtained in the case of current density for the dip-coating film. Aiming at analyzing the rate of the coloration front associated with lithium ion diffusion, a spectroelectrochemical method based on the galvanostatic intermittent titration technique (GITT) was employed so as to determine the ""optical"" diffusion coefficient (D(op)). In the dip-coating film, the method employed here revealed that the lithium ion rate is higher in diffusion pathways formed from K(2)Nb(6)O(17)(2-) sites that contribute more significantly to Delta A. Meanwhile, the presence of PAH contributed to the increased ionic mobility in diffusion pathways in the LbL film, with low contribution to the electrochromic efficiency. These results aided a better understanding of the potentiodynamic profile of the temporal change of absorbance and current density during the insertion/deinsertion of lithium ions into the electrochromic materials.