Environment-friendly soy flour-based resins without formaldehyde

Glyoxalated soy flour adhesives for wood particleboard added with a much smaller proportion of glyoxalated lignin or tannin and without any addition of either formaldehyde or formaldehyde-based resin are shown to yield results satisfying the relevant standard specifications for interior wood boards. Adhesive resin formulations in which the total content of natural material is either 70 or 80% of the total resin solids content gave good results. The resins comprising 70% by weight of natural material can be used in a much lower proportion on wood chips and can afford pressing times fast enough to be significant under industrial panel pressing conditions. The best formulation of all the ones tried was the one based on glyoxalated precooked soy flour (SG), to which a condensed tannin was added in water solution and a polymeric isocyanate (pMDI), where the proportions of the components SG/T/pMDI was 54/16/30 by weight. (C) 2008 Wiley Periodicals, Inc.

Blocked diisocyanates as reactive coupling agents: Application to pine fiber-polypropylene composites

In this paper, composites from polypropylene and Kraft pulp (from Pinus radiata) were prepared. Phenyl isocyanate, unblocked and phenol blocked derivatives of 4,4`-methylenebis (phenyl isocyanate) (MDI) were used as coupling agents and the mechanical properties of the obtained composites analyzed. The results showed that the addition of such compatibilizers readily improved the tensile and flexural strengths of the composites. However, no significant variation in the mechanical properties was observed for composite formulations comprising different isocyanate compounds. Accordingly, the chemical structure of isocyanate derivatives did not affect extensively the mechanical properties of MDI-coupled pine fiber reinforced composites. These results were similar to those obtained in previous studies regarding the efficiency of organosilane coupling agents. In comparison to monoreactive isocyanates, the addition of MIDI increased considerably the mechanical properties of pine fiber-polypropylene composites. The mechanical anchoring of polymeric PP chains onto the irregular reinforcement surface supported this result. Non-isothermal DSC analysis showed a slowing effect of MDI on the crystallization kinetics of the coupled composites. This may have been the result of diminished polymer chain mobility in the matrix due to mechanical anchoring onto the fiber surface. Considering these results, the occurrence of strong bonds between the composite components was stated, rather than the unique existence of Van der Waals interactions among the non-polar structures. (c) 2008 Elsevier Ltd. All rights reserved.