Thermal and mechanical characteristics of polyurethane/curaua fiber composites

Polyurethane composites reinforced with curaua fiber at 5, 10 and 20% mass/mass proportions were prepared by using the conventional melt-mixing method. The influence of curaua fibers on the thermal behavior and polymer cohesiveness in polyurethane matrix was evaluated by dynamic mechanical thermal analysis (DMTA) and by differential scanning calorimetry (DSC). This specific interaction between the fibers and the hard segment domain was influenced by the behavior of the storage modulus E` and the loss modulus EaEuro(3) curves. The polyurethane PU80 is much stiffer and resistant than the other composites at low temperatures up to 70A degrees C. All samples were thermoplastic and presented a rubbery plateau over a wide temperature range above the glass transition temperature and a thermoplastic flow around 170A degrees C.

Effect of cooking on non-starch polysaccharides of hard-to-cook beans

Experiments carried out to study changes induced by hard-to-cook (HTC) phenomenon in the non-starch polysaccharides of beans stored at 30 degrees C and 75% RH for 8 months showed that the development of HTC did not affect the amounts of soluble and insoluble fibre in cooked seeds but changed their carbohydrates physical properties. Aged beans non-starch polysaccharides presented lower water-solubility and underwent lower degradation of galacturonans and arabinose-rich polysaccharides when submitted to cooking. The decrease in non-starch polysaccharides water-solubility produced a shift in the polymers fractionation profile which resulted in an increase of weak and middle-alkali soluble polymers bulk as well as in their arabinose and uronic acid contents. Uronic acid contents were higher in polymers released by 1 M NaOH and in the cellulose-rich residues while the arabinose contents were higher in the mild-alkali soluble polymers of aged seeds. Methylation analysis showed no evident alterations in the xyloglucans and arabinans branching degree with beans ageing. However, both, the molecular mass of water-soluble pectins and CDTA-soluble pectins, increased. Even though changes in the non-starch polysaccharide solubility were not related to the decrease in the arabinan and xyloglucan degree of branching they may be related to the formation of new chemical interactions other than hydrogen bond. There was a correlation between acidic and neutral polysaccharides insolubilisation in beans ageing and probably in beans hardening. After processing, aged seeds present higher amounts of insoluble fibre when compared to normal beans. (C) 2008 Elsevier Ltd. All rights reserved.