COLOR STABILITY OF DENTAL CERAMICS SUBMITTED TO ARTIFICIAL ACCELERATED AGING AFTER REPEATED FIRINGS

Statement of problem. Color stability is an important factor to ensure the long-term clinical success of ceramic restorations. There is a lack of information on how color is affected by fabrication procedures, such as the number of firings. Purpose. The purpose of this study was to evaluate the effects that the number of firings and type of substrate have on the color stability of dental ceramic submitted to artificial accelerated aging. Material and methods. Sixty specimens were fabricated: 30 metal ceramic (Verabond II + IPS d.SIGN) and 30 all-ceramic (IPS d.SIGN). Specimens were divided into 3 groups (n=10), and submitted to 2, 3, or 4 firings (+/- 900 degrees C), respectively, according to the manufacturer`s instructions. Color readings were obtained with a spectro photometer before and after artificial accelerated aging, and L*, a*, and b* coordinates and total color variation (Delta E) were analyzed (2-way ANOVA, Bonferroni, (alpha=05). Results. For metal ceramic specimens, differences for the L* coordinates were significant (P<.05) only for the group submitted to 3 firings. With respect to the all-ceramic specimens, smaller L* coordinates were obtained for greater a* and b* coordinates, indicating that the greater the number of firings, the darker and more reddish/yellowish the specimen. All Delta E values, for all groups, were below 1.0. All-ceramic specimens submitted to 3 and 4 firings presented Delta E means differing statistically (P<.05) from those of the metal ceramic group. Conclusions. The type of substrate and number of firings affected the color stability of the ceramic material tested. Artificial accelerated aging did not produce perceptible color stability changes (Delta E<1.0). (J Prosthet Dent 2009-101:13-18)

Equicrestal and Subcrestal Dental Implants: A Histologic and Histomorphometric Evaluation of Nine Retrieved Human Implants

Background: Stability of pen-implant crestal bone plays a relevant role relative to the presence or absence of interdental papilla. Several factors can contribute to the crestal bone resorption observed around two-piece implants, such as the presence of a microgap at the level of the implant abutment junction, the type of connection between implant and prosthetic components, the implant positioning relative to the alveolar crest, and the interimplant distance. Subcrestal positioning of dental implants has been proposed to decrease the risk of exposure of the metal of the top of the implant or of the abutment margin, and to get enough space in a vertical dimension to create a harmoniously esthetic emergence profile. Methods: The present retrospective histologic study was performed to evaluate dental implants retrieved from human jaws that had been inserted in an equicrestal or subcrestal position. A total of nine implants were evaluated: five of these had been inserted in an equicrestal position, whereas the other four had been positioned subcrestally (1 to 3 mm). Results: In all subcrestally placed implants, preexisting and newly formed bone was found over the implant shoulder. In the equicrestal implants, crestal bone resorption (0.5 to 1.5 mm) was present around all implants. Conclusion: The subcrestal position of the implants resulted in bone located above the implant shoulder. J Periodontol 2011;82:708-715.

Chemical and Morphological Features of Dental Composite Resin: Influence of Light Curing Units and Immersion Media

Aims: The study evaluated the influence of light curing units and immersion media on superficial morphology and chemistry of the nanofilled composite resin Supreme XT (3M) through the EDX analysis and SEM evaluation. Light curing units with different power densities and mode of application used were XL 3000 (480 mW/cm(2)), Jet Lite 4000 Plus (1230mW/cm(2)), and Ultralume Led 5 (790 mW/cm(2)) and immersion media were artificial saliva, Coke(R), tea and coffee, totaling 12 experimental groups. Specimens (10 mm X 2 mm) were immersed in each respective Solution for 5 min, three times a day, during 60 days and stored in artificial saliva at 37 degrees C +/- 1 degrees C between immersion periods. Topography and chemical analysis was qualitative. Findings: Groups immersed in artificial saliva, showed homogeneous degradation of matrix and deposition of calcium at the material surface. Regarding coffee, there was a reasonable chemical degradation with loss of load particles and deposition of ions. For tea, superficial degradation occurred in specific areas with deposition of calcium, carbon. potassium and phosphorus. For Coke(R), excessive matrix degradation and loss of load particles with deposition of calcium, sodium, and potassium. Conclusion: Light curing units did not influence the superficial morphology of composite resin tested, but the immersion beverages did. Coke(R) affected material`s surface more than did the other tested drinks. Microsc. Res. Tech. 73:176-181, 2010. (c) 2009 Wiley-Liss Inc.

Bond Strength of Dental Adhesive Systems Irradiated with Ionizing Radiation

Purpose: The aim of the present paper was to determine the effect of different types of ionizing radiation on the bond strength of three different dentin adhesive systems. Materials and Methods: One hundred twenty specimens of 60 human teeth (protocol number: 032/2007) sectioned mesiodistally were divided into 3 groups according to the adhesives systems used: SB (Adper Single Bond Plus), CB (Clearfil SE Bond) and AP (Adper Prompt Self-Etch). The adhesives were applied on dentin and photo-activated using LED (Lec 1000, MMoptics, 1000 mW/cm(2)). Customized elastomer molds (0.5 mm thickness) with three orifices of 1.2 mm diameter were placed onto the bonding areas and filled with composite resin (Filtek Z-250), which was photo-activated for 20 s. Each group was subdivided into 4 Subgroups for application of the different types of ionizing radiation: ultraviolet radiation (UV), diagnostic x-ray radiation (DX), therapeutic x-ray radiation (TX) and without irradiation (control group, CG). Microshear tests were carried out (Instron, model 4411), and afterwards the modes of failure were evaluated by optical and scanning electron microscope and classified using 5 scores: adhesive failure, mixed failures with 3 significance levels, and cohesive failure. The results of the shear bond strength test were submitted to ANOVA with Tukey`s test and Dunnett`s test, and the data from the failure pattern evaluation were analyzed with the Mann Whitney test (p = 0.05). Results: No change in bond strength of CB and AP was observed after application of the different radiation types, only SB showed increase in bond strength after UV (p = 0.0267) irradiation. The UV also changed the failure patterns of SB (p = 0.0001). Conclusion: The radio-induced changes did not cause degradation of the restorations, which means that they can be exposed to these types of ionizing radiation without weakening the bond strength.

Thermal analysis and structural investigation of different dental composite resins

The structural and thermal properties of three different dental composite resins, Filtek (TM) Supreme XT, Filtek (TM) Z-250 and TPHA (R)(3) were investigated in this study. The internal structures of uncured and cured resins with blue light-emitting diodes (LEDs) were examined by Micro-Raman spectroscopy. Thermal analysis techniques as DSC, TG and DTG methods were used to investigate the temperature characteristics, as glass transition (T (g) ), degradation, and the thermal stability of the resins. The results showed that the TPHA (R)(3) and Filtek (TM) Supreme XT presented very similar T (g) values, 48 and 50A degrees C, respectively, while the Filtek (TM) Z-250 composite resin presented a higher one, 58A degrees C. AFM microscope was utilized in order to analyze the sample morphologies, which possess different fillers. The composed resin Filtek (TM) Z-250 has a well interconnected more homogeneous morphology, suggesting a better degree of conversion correlated to the glass phase transition temperature. The modes of vibration of interest in the resin were investigated using Raman spectroscopy. It was possible to observe the bands representative for the C=C (1630 cm(-1)) and C=O(1700 cm(-1)) vibrations were studied with respect to their compositions and polymerization. It was observed that the Filtek (TM) Z -250 resin presents the best result related to the thermal properties and polymerization after light curing among the other resins.