Microleakage in conservative cavities varying the preparation method and surface treatment

OBJECTIVE: To assess microleakage in conservative class V cavities prepared with aluminum-oxide air abrasion or turbine and restored with self-etching or etch-and-rinse adhesive systems. Materials and Methods: Forty premolars were randomly assigned to 4 groups (I and II: air abrasion; III and IV: turbine) and class V cavities were prepared on the buccal surfaces. Conditioning approaches were: groups I/III - 37% phosphoric acid; groups II/IV - self-priming etchant (Tyrian-SPE). Cavities were restored with One Step Plus/Filtek Z250. After finishing, specimens were thermocycled, immersed in 50% silver nitrate, and serially sectioned. Microleakage at the occlusal and cervical interfaces was measured in mm and calculated by a software. Data were subjected to ANOVA and Tukey's test (α=0.05). RESULTS: Marginal seal provided by air abrasion was similar to high-speed handpiece, except for group I. There was SIGNIFICANT difference between enamel and dentin/cementum margins for to group I and II: air abrasion. The etch-and-rinse adhesive system promoted a better marginal seal. At enamel and dentin/cementum margins, the highest microleakage values were found in cavities treated with the self-etching adhesive system. At dentin/cementum margins, high-speed handpiece preparations associated with etch-and-rinse system provided the least dye penetration. CONCLUSION: Marginal seal of cavities prepared with aluminum-oxide air abrasion was different from that of conventionally prepared cavities, and the etch-and-rinse system promoted higher marginal seal at both enamel and dentin margins.

Influence of Aluminum Oxide Sandblasting Associated with Nd:YAG or Er:YAG Lasers on Shear Bond Strength of a Feldspathic Ceramic to Resin Cements

Objective: This in vitro study evaluated the influence of the surface pretreatment of a feldspathic ceramic on the shear bond strength of two different resin cements. Background Data: Although several conventional surface treatments have been used on feldspathic ceramic, few studies have investigated the effects of an alternative surface treatment, the association of aluminum oxide sandblasting with Nd:YAG and Er:YAG lasers. Methods: Sixty samples made of a feldspathic ceramic were divided into three groups (n = 20) and treated with (1) controlled-air abrasion with Al(2)O(3) + 10% hydrofluoric acid (HF), (2) Al(2)O(3) + Er:YAG laser, and (3) Al(2)O(3) + Nd:YAG laser. Afterward, silane (Dentsply) was applied on each treated surface. Each of the three main groups was divided into two subgroups (n = 10), where a different resin cement was employed for each subgroup. It was built a cylinder with resin cement (RelyX Arc) in subgroup (A) and with self-adhesive cement (RelyX U100) in subgroup (B). After 24 h at 37 degrees C, the prepared specimens were submitted to shear bond strength test and stereoscopic evaluation to determine the type of failure. Results: Bond strength mean values were not statistically significant for the surface treatment methods or resin cements. Conclusion: The null surface treatment proposed with aluminum oxide sandblasting associated with the Er:YAG or Nd:YAG laser and using cementation with self-adhesive cement can be an alternative bonding technique for feldspathic ceramic, since it was as effective as the conventional treatment with aluminum oxide sandblasting and hydrofluoric acid using the conventional resin cement.

Effect of Different Fluoride Concentrations of Experimental Dentifrices on Enamel Erosion and Abrasion

It has been suggested that fluoride products are able to reduce erosive tooth wear. Thus, the purpose of this in vitro study was to evaluate the effect of dentifrices with different fluoride concentrations as well as of a low-fluoridated dentifrice supplemented with trimetaphosphate (TMP) on enamel erosion and abrasion. One hundred twenty bovine enamel blocks were assigned to the following experimental dentifrices: placebo, 1,100 mu g F/g, 500 mu g F/g plus 3% TMP and 5,000 mu g F/g. The groups of enamel blocks were additionally subdivided into conditions of erosion (ERO) and of erosion plus abrasion (ERO + ABR). For 7 days, the blocks were subjected to erosive challenges (immersion in Sprite (R) 4 times a day for 5 min each time) followed by a remineralizing period (immersion in artificial saliva between erosive challenges for 2 h). After each erosive challenge, the blocks were exposed to slurries of the dentifrices (10 ml/sample for 15 s). Sixty of the blocks were additionally abraded by brushing using an electric toothbrush (15 s). The alterations of the enamel were quantified using the Knoop hardness test and profilometry (measurements in micrometers). The data were analyzed using a 2-way ANOVA test followed by a Bonferroni correction (p < 0.05). In in vitro conditions, the 5,000 mu g F/g and 500 mu g F/g plus 3% TMP dentifrices had a greater protective effect when compared with the 1,100 mu g F/g dentifrice, under both ERO and ERO + ABR conditions. The results suggest that dentifrices alone are not capable of completely inhibiting tooth wear. Copyright (C) 2010 S. Karger AG, Basel

In Vitro Evaluation of Enamel Erosion After Nd:YAG Laser Irradiation and Fluoride Application

Objective: Previous investigations have demonstrated improved enamel demineralization resistance after laser irradiation. Due to the possibility of a synergistic effect between laser and fluoride, this study investigated the effect of fluoridated agents and Nd:YAG irradiation separately and in combination on enamel resistance to erosion. Methods: One hundred bovine enamel blocks were randomly divided into 10 groups: G1, untreated (control); G2, acidic phosphate fluoride (APF) (1.23% F) for 4 min; G3, fluoride varnish for 6 h (NaF, 2.26%); G4, 0.5 W Nd: YAG laser (250 mm pulse width, 10 Hz, 35 J/cm(2), with uniform velocity for 30 sec in each application); G5, 0.75 W Nd:YAG laser (52.5 J/cm(2)); G6, 1.0 W Nd:YAG laser (70 J/cm(2)); G7, APF + 0.75 W Nd:YAG laser; G8, 0.75 W Nd:YAG laser + APF; G9, fluoride varnish + 0.75 W Nd:YAG laser; and G10, 0.75 W Nd:YAG laser + fluoride varnish. During 10 d the erosive cycle was conducted by immersion of the blocks in Sprite light for 1 min, followed by immersion in artificial saliva for 59 min. This procedure was consecutively repeated four times per day. In each day, during the remaining 20 h, the blocks were maintained in artificial saliva. The wear was evaluated by profilometry (days 5 and 10). Data were tested by two-way ANOVA and Bonferroni's tests (p < 0.05). Results: The mean wear at days 5 and 10 was, respectively: G1, 1.83 and 2.67 mu m; G2, 1.04 and 2.60 mu m; G3, 1.03 and 2.48 mu m; G4, 1.13 and 2.47 mu m; G5, 1.07 and 2.44 mu m; G6, 1.0 and 2.35 mu m; G7, 0.75 and 2.27 mu m; G8, 0.80 and 2.12 mu m; G9, 0.76 and 2.47 mu m; and G10, 1.09 and 2.46 mu m. At day 5, all the experimental groups presented significant lesser wear when compared to control group. However, at 10 d, only G7 and G8 were still different from control. Conclusions: The association between APF application and laser irradiation seems to be an alternative preventive measure against dental erosion.

Effect of different surface treatments on the repair bond strength of indirect composites

Purpose: To evaluate the tensile bond strength of indirect composites repaired with different surface treatments and direct composites. Methods: 180 specimens were prepared with Targis, belleGlass HP and Sculpture indirect composites, light-activated and post-cured according to the manufacturers` recommendations. The specimens were stored in distilled water for 24 hours at 37 degrees C. The bonding surfaces were prepared with air abrasion, hydrofluoric acid or hydrofluoric acid followed by a neutralizing solution. All the treated surfaces were subject to the application of a silane and a bonding agent before the repair procedures with Tetric Ceram and Tetric Flow for the Targis specimens, Herculite XRV and Revolution for the belleGlass HP specimens and Sculp-It and Flow-It for Sculpture specimens. The tensile bond strength tests were carried out using a universal testing machine at cross-head speed of 0.5 mm/minute. The type of fracture was observed under a light microscope at x40 magnification. Data were analyzed by a two-way ANOVA and Tukey`s post-hoc tests (P<0.05). Results: Targis showed a statistically higher repair bond strength than belleGlass HP and Sculpture, which were not significantly different from each other. Air abrasion increased the repair bond strength of belleGlass HP and Sculpture. For Targis, all the surface treatments resulted in similar repair bond strength. The different viscosity of repair composites did not affect the repair of indirect composites. Fractured surfaces showed mostly adhesive failures, mainly with hydrofluoric acid treatment.

Preventive effect of iron gel with or without fluoride on bovine enamel erosion in vitro

Background: The aim of this study was to evaluate the preventive effect in vitro of experimental gel containing iron and/or fluoride on the erosion of bovine enamel. Methods: To standardize the blocks (n = 80), specimens (4 x 4 mm) were previously selected to measure the initial microhardness. The blocks were randomly allocated into four groups of 20 samples each: C (control, placebo gel); F (fluoride gel, 1.23% NaF); Fe (iron gel, 10 mmol/L FeSO(4)) and F + Fe (fluoride + iron gel). The gels were applied and removed after 1 minute. The blocks were then submitted to six alternating remineralization and demineralization cycles. The beverage Coca-Cola (R) (10 minutes, 30 mL) was used for demineralization, and artificial saliva (1 hour) for remineralization. The effect of erosion was measured by wear analysis (profilometry). Data were analysed by ANOVA and the Tukey test for individual comparisons (p <0.05). Results: The mean wear (+/- SD, mu m) was C: 0.94 +/- 0.22; F: 0.55 +/- 0.12; Fe: 0.49 +/- 0.11 and F + Fe: 0.55 +/- 0.13. When the experimental gels were used, there was statistically significant reduction in enamel wear in comparison with the control (p <0.001). However, the experimental gels did not differ significantly among them. Conclusions: The gels containing iron with or without fluoride are capable of interfering with the dissolution dental enamel in the presence of erosive challenge.

Insights into preventive measures for dental erosion

Dental erosion is defined as the loss of tooth substance by acid exposure not involving bacteria. The etiology of erosion is related to different behavioral, biological and chemical factors. Based on an overview of the current literature, this paper presents a summary of the preventive strategies relevant for patients suffering from dental erosion. Behavioral factors, such as special drinking habits, unhealthy lifestyle factors or occupational acid exposure, might modify the extent of dental erosion. Thus, preventive strategies have to include measures to reduce the frequency and duration of acid exposure as well as adequate oral hygiene measures, as it is known that eroded surfaces are more susceptible to abrasion. Biological factors, such as saliva or acquired pellicle, act protectively against erosive demineralization. Therefore, the production of saliva should be enhanced, especially in patients with hyposalivation or xerostomia. With regard to chemical factors, the modification of acidic solutions with ions, especially calcium, was shown to reduce the demineralization, but the efficacy depends on the other chemical factors, such as the type of acid. To enhance the remineralization of eroded surfaces and to prevent further progression of dental wear, high-concentrated fluoride applications are recommended. Currently, little information is available about the efficacy of other preventive strategies, such as calcium and laser application, as well as the use of matrix metalloproteinase inhibitors. Further studies considering these factors are required. In conclusion, preventive strategies for patients suffering from erosion are mainly obtained from in vitro and in situ studies and include dietary counseling, stimulation of salivary flow, optimization of fluoride regimens, modification of erosive beverages and adequate oral hygiene measures.

Scanning electron microscopic study of the in situ effect of salivary stimulation on erosion and abrasion in human and bovine enamel

This in situ study investigated, using scanning electron microscopy, the effect of stimulated saliva on the enamel surface of bovine and human substrates submitted to erosion followed by brushing abrasion immediately or after one hour. During 2 experimental 7-day crossover phases, 9 previously selected volunteers wore intraoral palatal devices, with 12 enamel specimens (6 human and 6 bovine). In the first phase, the volunteers immersed the device for 5 minutes in 150 ml of a cola drink, 4 times a day (8h00, 12h00, 16h00 and 20h00). Immediately after the immersions, no treatment was performed in 4 specimens (ERO), 4 other specimens were immediately brushed (0 min) using a fluoride dentifrice and the device was replaced into the mouth. After 60 min, the other 4 specimens were brushed. In the second phase, the procedures were repeated but, after the immersions, the volunteers stimulated the salivary flow rate by chewing a sugar-free gum for 30 min. Enamel superficial alterations of all specimens were then evaluated using a scanning electron microscope. Enamel prism core dissolution was seen on the surfaces submitted to erosion, while on those submitted to erosion and to abrasion (both at 0 and 60 min) a more homogeneous enamel surface was observed, probably due to the removal of the altered superficial prism layer. For all the other variables - enamel substrate and salivary stimulation -, the microscopic pattern of the enamel specimens was similar.

Assessment in vitro of brushing on dental surface roughness alteration by laser interferometry

Noncarious cervical lesions (NCCLs) are considered to be of multifactorial origin, normally associated with inadequate brushing. This study assessed the influence in vitro of simulated brushing on NCCL formation. Fifteen human premolars were submitted to brushing in the cementoenamel junction region, using hard-, medium- and soft-bristled brushes associated with a toothpaste of medium abrasiveness under a 200 g load, at a speed of 356 rpm for 100 minutes. The surface topography of the region was analyzed before and after brushing, by means of a laser interferometer, using "cut-off" values of 0.25 and considering roughness values in mm. The initial roughness (mm) results for dentin (D / bristle consistency: 1 - soft, 2 - medium and 3 - hard) were as follows: (D1) 1.25 ± 0.45; (D2) 1.12 ± 0.44; (D3) 1.05 ± 0.41. For enamel (E / bristle consistency: 1 - soft, 2 - medium and 3 - hard), the initial results were: (E1) 1.18 ± 0.35; (E2) 1.32 ± 0.25; (E3) 1.50 ± 0.38. After brushing, the following were the values for dentin: (D1) 2.32 ± 1.99; (D2) 3.30 ± 0.96; (D3) Over 500. For enamel, the values after brushing were: (E1) 1.37 ± 0.31; (E2) 2.15 ± 0.90; (E3) 1.22 ± 0.47. Based on the results of the ANOVA and Tukey statistical analyses (a = .05) it was concluded that soft, medium and hard brushes are not capable of abrading enamel, whereas dentin showed changes in surface roughness by the action of medium- and hard-bristled brushes.

Effect of Nd:YAG Laser and Acidulated Phosphate Fluoride on Bovine and Human Enamel Submitted to Erosion/Abrasion or Erosion Only: An in Vitro Preliminary Study

Objective: The aim of the present in vitro study was to evaluate, using two different methodologies, the effectiveness of pulsed Nd:YAG laser irradiation associated with topical acidulated phosphate fluoride (APF) for preventing enamel erosion and structure loss under regimes of erosion and abrasion or erosion only. Background Data: An increased incidence of noncarious lesions (erosion and abrasion) has been observed, consequently new preventative therapies have been proposed. Materials and Methods: Two different methodologies were performed. For the first, 100 bovine crowns were submitted to four different treatments (n = 25): no treatment (control), 4 min application of APF, Nd:YAG laser irradiation (1 W, 100 mJ, 10 Hz, 141.5 J/cm(2)), and Nd:YAG laser irradiation+4 min of APF. After the specimens were exposed to citric acid (2% w/v; 30 min), they were submitted to 5000 brushing cycles. Specimen mass was measured before and after the treatments. For the second methodology, 20 human crowns were embedded in acrylic resin and cut surfaces were exposed and polished. The specimens were divided into four groups (n = 10): no treatment (control), APF for 4 min, Nd:YAG laser irradiation (1 W, 100 mJ, 10 Hz, 125 J/cm(2)), and Nd:YAG laser irradiation+APF. The samples were then immersed in citric acid (2% w/v; 90 min). Vickers hardness was obtained before and after the treatments. Results: The Nd:YAG laser irradiation+APF (bovine and human enamel) was more effective and yielded statistically significant results for surface microhardness and enamel wear. Conclusion: Nd:YAG laser irradiation associated with APF reduced bovine enamel wear and human enamel softening when samples were submitted to a regime of erosion and abrasion or erosion only in vitro.

Oral Myiasis in a Captive Hippopotamus

Causes of dental infections can be related to failed dental eruption, malocclusion, abrasion, fractures with or without exposure of the dental pulp, and periodontal disease. Reports of oral myiasis in megavertebrates in captivity air infrequent, perhaps due to the difficulty in observing the oral cavity in such species. This report describes a case of oral myiasis in an adult male hippopotamus in the gingival area and alveolar mucosa of the left mandibular canine tooth. J Vet Dent 26 (3); 168 170,2009

Prevention of toothbrushing abrasion of acid-softened enamel by CO(2) laser irradiation

Objective: The aim of the present study was to evaluate the effect of CO(2) laser irradiation (10.6 mu m) at 0.3 J/cm(2) (0.5 mu s; 226 Hz) on the resistance of softened enamel to toothbrushing abrasion, in vitro. Methods: Sixty human enamel samples were obtained, polished with silicon carbide papers and randomly divided into five groups (n = 12), receiving 5 different surface treatments: laser irradiation (L), fluoride (AmF/NaF gel) application (F), laser prior to fluoride (LF), fluoride prior to laser (FL), non-treated control (C). After surface treatment they were submitted to a 25-day erosive-abrasive cycle in 100 ml sprite light (90 s) and brushed twice daily with an electric toothbrush. Between the demineralization periods samples were immersed in supersaturated mineral solution. At the end of the experiments enamel surface loss was determined using a contact profilometer and morphological analysis was performed using scanning electron microscopy (SEM). For SEM analysis of demineralization pattern, cross-sectional cuts of cycled samples were prepared. The data were statistically analysed by one-way ANOVA model with subsequent pairwise comparison of treatments. Results: Abrasive surface loss was significantly lower in all laser groups compared to both control and fluoride groups (p < 0.0001 in all cases). Amongst the laser groups no significant difference was observed. Softened enamel layer underneath lesions was less pronounced in laser-irradiated samples. Conclusion: Irradiation of dental enamel with a CO(2) laser at 0.3 J/cm(2) (5 mu s, 226 Hz) either alone or in combination with amine fluoride gel significantly decreases toothbrushing abrasion of softened-enamel, in vitro. (C) 2011 Elsevier Ltd. All rights reserved.

Bacterial Adhesion on Smooth and Rough Titanium Surfaces After Treatment With Different Instruments

Background: Newly formed biofilm after implant debridement may challenge the long-term stability of peri-implant therapy. This in vitro study aimed to assess the roughness and adherence of Streptococcus sanguinis after treatment of smooth and rough titanium surfaces with an erbium-doped: yttrium, aluminum, and garnet (Er:YAG) laser, metal and plastic curets, and an air-powder abrasive system. Methods: Forty titanium disks with smooth-machined surfaces and 40 with sand-blasted and acid-etched surfaces were divided into the following treatment groups: Er:YAG laser; plastic curet; metal curet, and air-powder abrasive system. The surface roughness (roughness average [Raj) before and after treatments was determined using a profilometer. S. sanguinis (American Type Culture Collection 10556) was grown on treated and untreated specimens, and the amounts of retained bacteria on the surfaces were measured by the culture method. Rough and smooth surfaces with and without a suspension of S. sanguinis were also analyzed using scanning electron microscopy (SEM). Results: For smooth surfaces, the roughest surfaces were produced by metal curets (repeated - measures analysis of variance [ANOVA] and Tukey test; P<0.05). The rough-surface profile was not altered by any of the treatments (repeated-measures ANOVA; P>0.05). Rough surfaces treated with metal curets and air-powder abrasion showed the lowest level of bacteria] adhesion (two-way ANOVA and Tukey test; P<0.05). SEM analysis revealed distinct surface profiles produced by all devices. Conclusions: Metal curets are not recommended for smooth titanium surface debridement due to severe texture alteration. Rough surfaces treated with a metal curet and the air-powder abrasive system were less susceptible to bacterial adhesion, probably due to texture modification and the presence of abrasive deposits. J Periodontol 2009;80: 1824-1832.

Influence of leucite content on slow crack growth of dental porcelains

Objectives. To determine the stress corrosion susceptibility coefficient, n, of seven dental porcelains (A: Ceramco I; B: Ceramco-II; C: Ceramco-III; D: d.Sign; E: Cerabien; F: Vitadur-Alpha; and G: Ultropaline) after aging in air or artificial saliva, and correlate results with leucite content (LC). Methods. Bars were fired according to manufacturers` instructions and polished before induction of cracks by a Vickers indenter (19.6 N, 20 s). Four specimens were stored in air/room temperature, and three in saliva/37 degrees C. Five indentations were made per specimen and crack lengths measured at the following times: similar to 0; 1; 3; 10; 30; 100; 300; 1000 and 3000 h. The stress corrosion coefficient n was calculated by linear regression analysis after plotting crack length as a function of time, considering that the slope of the curve was (2/(3n + 2)]. Microstructural analysis was performed to determine LC. Results. LC of the porcelains were 22% (A and B); 6% (C); 15% (D); 0% (E and F); and 13% (G). Except for porcelains A and D, all materials showed a decrease in their n values when stored in artificial saliva. However, the decrease was more pronounced for porcelains B, F, and G. Ranking of materials varied according to storage media (in air, porcelain G showed higher n compared to A, while in saliva both showed similar coefficients). No correlation was found between n values and LC in air or saliva. Significance. Storage media influenced the n value obtained for most of the materials. LC did not affect resistance to slow crack growth regardless of the test environment. (c) 2008 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Stress intensity factor threshold in dental porcelains

The stress intensity factor threshold (K(IO)) is related to the stress level at which cracks start to grow stably, causing the weakening of porcelain prostheses during their use. The values of K(IO) of seven dental porcelains (with and without reinforcing leucite crystal, KAlSi(2)O(6)) stored in air (22 degrees C, 60% relative humidity) and artificial saliva (37 degrees C) were determined by measuring the crack growth velocity of radial cracks generated at the corner of Vickers indentations. The results of K(IO) were correlated with the leucite content, fracture toughness (K(Ic)), and chemical composition of the porcelains. It was observed that K(IO) increased with the increase of leucite content (only for the leucite-based porcelains) and with the increase of K(Ic). The increase in Al(2)O(3) content or the decrease in the alkali oxide (K(2)O and Na(2)O) content of the material`s glassy matrix tended to increase the K(IO) values. Storage media (air and saliva) did not significantly affect the K(IO) of porcelains tested, indicating that the control parameter of K(IO) value was not the water content of the storage media.