The requirement of zinc and calcium ions for functional MMP activity in demineralized dentin matrices

The progressive degradation of resin-dentin bonds is due, in part, to the slow degradation of collagen fibrils in the hybrid layer by endogenous matrix metalloproteinases (MMPs) of the dentin matrix. In in vitro durability studies, the storage medium composition might be important because the optimum activity of MMPs requires both zinc and calcium. Objective. This study evaluated the effect of different storage media on changes in matrix stiffness, loss of dry weight or solubilization of collagen from demineralized dentin beams incubated in vitro for up to 60 days. Methods. Dentin beams (1 mm x 2 mm x 6 mm) were completely demineralized in 10% phosphoric acid. After baseline measurements of dry mass and elastic modulus (E) (3-point bending, 15% strain) the beams were divided into 5 groups (n = 11/group) and incubated at 37 degrees C in either media containing both zinc and calcium designated as complete medium (CM), calcium-free medium, zinc-free medium, a doubled-zinc medium or water. Beams were retested at 3, 7, 14, 30, and 60 days of incubation. The incubation media was hydrolyzed with HCl for the quantitation of hydroxyproline (HOP) as an index of solubilization of collagen by MMPs. Data were analyzed using repeated measures of ANOVA. Results. Both the storage medium and the storage time showed significant effects on E, mass loss and HOP release (p < 0.05). The incubation in CM resulted in relatively rapid and significant (p < 0.05) decreases in stiffness, and increasing amounts of mass loss. The HOP content of the experimental media also increased with incubation time but was significantly lower (p < 0.05) than in the control CM medium, the recommended storage medium. Conclusions. The storage solutions used to age resin-dentin bonds should be buffered solutions that contain both calcium and zinc. The common use of water as an aging medium may underestimate the hydrolytic activity of endogenous dentin MMPs. (c) 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Influence of occlusal access on demineralized dentin removal in the Atraumatic Restorative Treatment (ART) approach

Purpose: To verify the influence of cavity access diameter on demineralized dentin removal in the ART approach. Methods: 40 non-carious human premolars were randomly divided into four groups. The occlusal surface was ground flat and the teeth were sectioned mesio-distally. The hemi-sections were reassembled and occlusal access preparations were carried out using ball-shaped diamonds. The resulting size of the occlusal opening was 1.0 mm, 1.4 mm, 1.6 mm and 1.8 mm for Groups A, B, C, and D, respectively. Standardized artificial carious lesions were created and demineralized dentin was excavated. After excavation, the cavities were analyzed using: (a) the tactile method, (b) caries-detection dye to stain demineralized dentin, as proposed by Smales & Fang, and (c) Demineralized Tissue Removal index, as proposed in this study. Statistical analysis was performed using Fisher, Spearman correlation coefficient, kappa, Kruskal-Wallis and Miller tests (P < 0.05). Results: The three methods of evaluation showed no significant difference between Groups A vs. B, and C vs. D, while statistically significant differences were observed between Groups A vs. C, A vs. D, B vs. C and B vs. D. Based on the results of this study, the size of occlusal access significantly affected the efficacy of demineralized tissue removal.

Clinical versus laboratory adhesive performance to wet and dry demineralized primary dentin

Purpose: To evaluate the influence of dentin moisture on bond strengths of an etch-and-rinse bonding agent to primary dentin clinically and in the laboratory. Methods: The sample consisted of two groups of 20 caries-free primary second molars: molars in exfoliation period (clinical group) and extracted molars (laboratory group). Class I cavities were prepared in all specimens leaving a flat dentin surface on the pulpal floor. A two-step etch-and-rinse adhesive was vigorously rubbed on either dry (n= 5) or wet demineralized dentin (n= 5) under clinical or laboratory conditions. After restorative procedures, the teeth from the clinical group were extracted after 20 minutes. All samples were processed and underwent microtensile bond strength test and silver nitrate uptake evaluation under scanning electron microscopy. Results: Statistically higher bond strength values were observed when the bonding was performed under laboratory conditions and on a wet demineralized dentin. Most of the failures were adhesive and mixed irrespective of the experimental condition. Silver nitrate uptake occurred in all groups irrespective of the experimental condition. Resin-dentin bond strengths produced in the laboratory in primary teeth may overestimate those produced under clinical circumstances. (Am J Dent 2011;24:221-225).

Application of hydrophobic resin adhesives to acid-etched dentin with an alternative wet bonding technique

Hydrophilic dentin adhesives are prone to water sorption that adversely affects the durability of resin-dentin bonds. This study examined the feasibility of bonding to dentin with hydrophobic resins via the adaptation of electron microscopy tissue processing techniques. Hydrophobic primers were prepared by diluting 2,2-bis[4(2-hydroxy-3-methacryloyloxy-propyloxy)-phenyl] propane/triethyleneglycol dimethacrylate resins with known ethanol concentrations. They were applied to acid-etched moist dentin using an ethanol wet bonding technique that involved: (1) stepwise replacement of water with a series of increasing ethanol concentrations to prevent the demineralized collagen matrix from collapsing; (2) stepwise replacement of the ethanol with different concentrations of hydrophobic primers and subsequently with neat hydrophobic resin. Using the ethanol wet bonding technique, the experimental primer versions with 40, 50, and 75% resin exhibited tensile strengths which were not significantly different from commercially available hydrophilic three-step adhesives that were bonded with water wet bonding technique. The concept of ethanol wet bonding may be explained in terms of solubility parameter theory. This technique is sensitive to water contamination, as depicted by the lower tensile strength results from partial dehydration protocols. The technique has to be further improved by incorporating elements of dentin permeability reduction to avoid water from dentinal tubules contaminating water-free resin blends during bonding. (c) 2007 Wiley Periodicals, Inc. J Biomed Mater Res 84A: 19-29, 2008.

Influence of Er:YAG Laser Frequency on Dentin Caries Removal Capacity

The purposes of this study were to evaluate in vitro the influence of different frequencies of Er:YAG laser on the human dentin caries removal capacity. Thirty fragments obtained from third molars were randomly assigned into three groups (n = 10) according to the laser frequency used: 4, 6, and 10 Hz. The caries lesion (+/-1 mm deep) was induced before the irradiation by S. mutans cultures for 6 weeks. The specimens of all groups were irradiated with 200 mJ of energy in noncontact and focused mode under constant refrigeration (water flow: 2.5 mL/min). Quantitative analysis of the caries removal was performed by DIAGNOdent (TM) and the Axion Vision (TM) software. Qualitative analysis was performed by Scanning electron microscope (SEM) and light microscope (LM). Data were analyzed by ANOVA and Fishers` tests. The DIAGNOdent (TM) revealed that the caries removal was similar with 4 and 6 Hz and was superior with 10 Hz (P < 0.05). The analysis with Axion Vision (TM) software revealed that the caries removal was similar with 6 and 10 Hz and the 4 Hz group promoted the lowest caries removal. Through SEM morphologic analysis, some specimens irradiated with 4 Hz presented, under the demineralized dentin, a disorganized collagenous matrix. The LM images revealed that all frequencies used promoted irregular caries removal, being observed over preparations with 6 and 10 Hz. It can be concluded that the increase of Er:YAG laser frequency provided a higher dentin caries removal without selectivity to the disorganized dentin. Microsc. Res. Tech. 74:281-286, 2011. (C) 2010 Wiley-Liss, Inc.

Long-term stability of dentin matrix following treatment with various natural collagen cross-linkers

Objectives: Collagen disorganization is one of the main degradation patterns found in unsuccessful adhesive restorations. The hypothesis of this study was that pretreatment using natural collagen cross-linking agents rich in proanthocyanidin (PA) would improve mechanical properties and stability over time of the dentin collagen and, thus, confer a more resistant and lasting substrate for adhesive restorations. Methods: PA-based extracts, from grape seed (GSE), cocoa seed (CSE), cranberry (CRE), cinnamon (CNE) and acai berry (ACE) were applied over the demineralized dentin. The apparent elastic modulus (E) of the treated dentin collagen was analyzed over a 12 month period. Specimens were immersed in the respective solution and E values were obtained by a micro-flexural test at baseline, 10, 30, 60, 120 and 240 min. Samples were stored in artificial saliva and re-tested after 3, 6 and 12 months. Data was analyzed using ANOVA and Tukey test. Results: GSE and CSE extracts showed a time-dependent effect and were able to improve [240 min (MPa): GSE = 108.96 +/- 56.08: CSE = 59.21 +/- 24.87] and stabilize the E of the organic matrix [12 months (MPa): GSE = 40.91 +/- 19.69; CSE = 42.11 +/- 13.46]. CRE and CNE extracts were able to maintain the E of collagen matrices constant over 12 months [CRE = 11.17 +/- 7.22; CNE = 9.96 +/- 6.11; MPa]. ACE (2.64 +/- 1.22 MPa) and control groups immersed in neat distilled water (1.37 +/- 0.69 MPa) and ethanol-water (0.95 +/- 0.33 MPa) showed no effect over dentin organic matrix and enable their degradation and reduction of mechanical properties. Significance: Some PA-based extracts were capable of improving and stabilizing collagen matrices through exogenous cross-links induction. (C) 2011 Elsevier Ltd. All rights reserved.

Effects of adhesive temperature on the early and 6-month dentin bonding

Objectives: The aim of this study was to test the effect of adhesive temperature on the bond strength to dentin (mu TBS) and silver nitrate uptake (SNU) of an ethanol/water (Adper Single Bond 2 [SB]) and an acetone-based (Prime&Bond 2.1 [PB]) etch-and-rinse adhesive system. Methods: The bottles of each adhesive were kept in various temperatures (5 degrees C, 20 degrees C, 37 degrees C and 50 degrees C) for 1 h previously to its application in the occlusal demineralized dentin of 40 molars. Bonded sticks (0.8 mm(2)) were tested in tension (0.5 mm/min) immediately (IM) or after 6 months (6 M) of water storage. Two bonded sticks from each hemi-tooth were immersed in silver nitrate and analyzed by SEM. Data were analyzed by two-way repeated measures ANOVA and Tukey`s test (alpha = 0.05). Results: No significant difference in mu TBS was detected for both adhesives at 5 degrees C and 20 degrees C. The highest bond strength for PB was observed in the 37 degrees C group while for SB it was in the 50 degrees C. Significant reductions of bond strengths were observed for PB at 37 degrees C and SB at 50 degrees C after 6 M of water storage. Silver nitrate deposition was seen in all hybrid layers, irrespective of the group. Lower silver nitrate deposition (water trees) in the adhesive layer was seen for PB and SB at higher temperatures. Conclusions: The heating or refrigeration of the adhesives did not improve their resin-dentin bond resistance to water degradation over time. (C) 2009 Elsevier Ltd. All rights reserved.

Long-term effect of carbodiimide on dentin matrix and resin-dentin bonds

Objectives: To characterize the interaction of 1-Ethyl-3-[3-dimethylaminopropyl] carbodiimide Hydrochloride (EDC) with dentin matrix and its effect on the resin-dentin bond. Methods: Changes to the stiffness of demineralized dentin fragments treated with EDC/N-hydroxysuccinimide (NHS) in different solutions were evaluated at different time points. The resistance against enzymatic degradation was indirectly evaluated by ultimate tensile strength (UTS) test of demineralized dentin treated or not with EDC/NHS and subjected to collagenase digestion. Short- and long-term evaluations of the strength of resin-dentin interfaces treated with EDC/NHS for 1 h were performed using microtensile bond strength (mu TBS) test. All data (MPa) were individually analyzed using ANOVA and Tukey HSD tests (alpha = 0.05). Results: The different exposure times significantly increased the stiffness of dentin (p < 0.0001, control-5.15 and EDC/NHS-29.50), while no differences were observed among the different solutions of EDC/NHS (p = 0.063). Collagenase challenge did not affect the UTS values of EDC/NHS group (6.08) (p > 0.05), while complete degradation was observed for the control group (p = 0.0008, control-20.84 and EDC/NHS-43.15). EDC/NHS treatment did not significantly increase resin-dentin mu TBS, but the values remained stable after 12 months water storage (p < 0.05). Conclusions: Biomimetic use of EDC/NHS to induce exogenous collagen cross-links resulted in increased mechanical properties and stability of dentin matrix and dentin-resin interfaces. (C) 2010 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 94B: 250-255, 2010.

Solubility study of phytochemical cross-linking agents on dentin stiffness

Objectives: The effects of interactions between cross-linking proanthocyanidins (PA) in polar solvents and type-I collagen of demineralized dentin were investigated. Methods: Three PA-rich extracts, two from grape seed (GSEP and GSES) and one from cocoa (COE), were dissolved (water, ethanol:water and acetone:water) and analyzed for their ability to increase the modulus of elasticity of demineralized dentin. Sound dentin beams (0.5 mm x 1.7 mm x 7 mm) were fully demineralized and divided into 12 groups according to the type of cross-linking agent and solvents used. Specimens were immersed in the respective solutions and tested at baseline, 10, 30, 60, 120 and 240 min. Results: The elastic modulus (EM) of dentin was significantly increased by the PA treatment regardless of time (p < 0.05 for all times). The extracts showed different solubility in different solvents. GSEP showed the highest increase in EM when diluted in distilled water and acetone at all exposure times. Both GSEs showed superior results when diluted in distilled water and after 4 h of treatment, while COE produced strongest enhancement when dissolved in ethanol:water. Conclusions: The results indicates that herbal extraction process and other pharmacognostic parameters have an important influence on extract solubility as well as constitution and, consequently, on the PA-dentin matrix interaction. (C) 2010 Elsevier Ltd. All rights reserved.

Adhesive Temperature: Effects on Adhesive Properties and Resin-Dentin Bond Strength

Objectives: To evaluate the effect of adhesive temperature on the resin-dentin bond strength (mu TBS), nanoleakage (NL), adhesive layer thickness (AL), and degree of conversion (DC) of ethanol/water- (SB) and acetone-based (PB) etch-and-rinse adhesive systems. Methods: The bottles of the two adhesives were kept at each temperature (5 degrees C, 20 degrees C, 37 degrees C, and 50 degrees C) for 2 hours before application to demineralized dentin surfaces of 40 molars. Specimens were prepared for mu TBS testing. Bonded sticks (0.8 mm(2)) were tested under tension (0.5 mm/min). Three bonded sticks from each tooth were immersed in silver nitrate and analyzed by scanning electron microscopy. The DC of the adhesives was evaluated by Fourier transformed infrared spectroscopy. Results: Lower mu TBS was observed for PB at 50 degrees C. For SB, the mu TBS values were similar for all temperatures. DC was higher at 50 degrees C for PB. Higher NL and thicker AL were observed for both adhesives in the 5 degrees C and 20 degrees C groups compared to the 37 degrees C and 50 degrees C groups. The higher temperatures (37 degrees C or 50 degrees C) reduced the number of pores within the adhesive layer of both adhesive systems. Conclusions: It could be useful to use an ethanol/water-based adhesive at 37 degrees C or 50 degrees C and an acetone-based adhesive at 37 degrees C to improve adhesive performance.

Effect of oxalate desensitizers and dentin moisture during total-etch bonding

Purpose: To evaluate the effect of oxalate during total-etch bonding, under different dentin moisture conditions, over time. The null hypothesis tested was that microtensile bond strength (mu TBS) was not affected by oxalate treatment and dentin moisture during two evaluation periods. Methods: Extracted human third molars had their mid-coronal dentin exposed flat and polished with 600-grit SiC paper. The surfaces were etched with 35% phosphoric acid for 15 seconds, washed and blot dried. After etching, a 3% potassium oxalate gel was applied for 120 seconds, except for the control group (no desensitizer). The surface was then washed and left moist (Wet bonding) or air-dried for 30 seconds (Dry bonding). The surfaces were bonded with: (I) two 2-step etch-and-rinse adhesives: Single Bond (SB); Prime & Bond NT (PBNT) and (2) one 3-step etch-and-rinse adhesive: Scotchbond Multi Purpose (SBMP). Composite buildups were constructed incrementally with Tetric Ceram resin composite. Each increment was cured for 40 seconds. After storage in water for 24 hours or 1 year at 37 C, the specimens were prepared for mu TBS testing with a cross-sectional area of approximately 1 mm(2). They were then tested in tension in an Instron machine at 0.5 mm/minute. Data were analyzed by ANOVA and Student-Newman-Keuls at alpha = 0.05. Results: Application of potassium oxalate had no significant effect on the bond strengths of SBMP and PBNT, regardless of the surface moisture condition (P > 0.05). Conversely, reduced bond strengths were observed after oxalate treatment for SB in both moisture conditions, that being significantly lower when using a dry-bonding procedure (P < 0.05). Lower bond strength was obtained for PBNT when a dry-bonding technique was used, regardless of the oxalate treatment (P < 0.05). After aging the specimens for 1 year, bond strengths decreased. Smaller reductions were observed for SBMP, regardless of moisture conditions. For the WB technique, smaller reductions after 1 year were observed without oxalate treatment for SB and after oxalate treatment for PBNT. (Am J Dent 2010;23:137-141).

Mechanical characterization of proanthocyanidindentin matrix interaction

Objectives To characterize the properties of dentin matrix treated with two proanthocyanidin rich cross-linking agents and their effect on dentin bonded interfaces. Methods Sound human molars were cut into 0.5mm thick dentin slabs, demineralized and either treated with one of two cross-linking agents (grape seedGSE and cocoa seedCOE extracts) or left untreated. The modulus of elasticity of demineralized dentin was assessed after 10 or 60min and the swelling ratio after 60min treatment. Bacterial collagenase was also used to assess resistance to enzymatic degradation of samples subjected to ultimate tensile strength. The effect of GSE or COE on the resindentin bond strength was evaluated after 10 or 60min of exposure time. Data were statistically analyzed at a 95% confidence interval. Results Both cross-linkers increased the elastic modulus of demineralized dentin as exposure time increased. Swelling ratio was lower for treated samples when compared to control groups. No statistically significant changes to the UTS indicate that collagenase had no effect on dentin matrix treated with either GSE or COE. Resindentin bonds significantly increased following treatment with GSE regardless of the application time or adhesive system used. Significance Increased mechanical properties and stability of dentin matrix can be achieved by the use of PA-rich collagen cross-linkers most likely due to the formation of a PAcollagen complex. The short term resindentin bonds can be improved after 10min dentin treatment.(C) 2010 Academy of Denta lMaterials. Published by Elsevier Ltd. All rights reserved.

Influence of glutaraldehyde priming on bond strength of an experimental adhesive system applied to wet and dry dentine

Objectives: This study tested the following null hypotheses: (1) there is no difference in resin-dentine bond strength when an experimental glutaraldehyde primer solution is added prior to bonding procedures and (2) there is no difference in resin-dentine bond strength when experimental glutaraldehyde/adhesive system is applied under dry or wet demineralized dentine conditions. Methods: Extracted human maxillary third molars were selected. Flat, mid-coronal dentine was exposed for bonding and four groups were formed. Two groups were designated for the dry and two for the wet dentine technique: DRY: (1) Group GD: acid etching + glutaraldehyde primer (primer A) + HEMA/ethanol primer (primer B)-under dried dentine + unfilled resin; (2) Group D: the same as GD, except for primer A application; WET: (3) Group GW: the same as GD, but primer B was applied under wet dentine condition; (4) Group W: the same as GW, except for primer A application. The bonding resin was light-cured and a resin core was built up on the adhesive layer. Teeth were then prepared for microtensile bond testing to evaluate bond strength. The data obtained were submitted to ANOVA and Tukey`s test (alpha = 0.05). Results: Glutaraldehyde primer application significantly improved resin-dentine bond strength. No significant difference was observed when the same experimental adhesive system was applied under either dry or wet dentine conditions. These results allow the first null hypothesis to be rejected and the second to be accepted. Conclusion: Glutaraldehyde may affect demineralized dentine properties leading to improved resin bonding to wet and dry substrates. (C) 2008 Elsevier Ltd. All rights reserved.

Mechanical stability of adhesives under water storage

Objectives. To evaluate the effects of storage condition (wet or dry) and storage time (24 h and 3 months) on the ultimate tensile strength (UTS) of Single Bond (SB), 3M-ESPE; Opti Bond Solo Plus (OB), Kerr; One Step (OS), Bisco, and Prime & Bond NT (PB), Dentsply adhesive resins. Methods. Hourglass-shaped specimens were obtained from a metallic matrix. Each adhesive was dispensed to fill the molds completely and left undisturbed in a dark chamber for 4 min at 37 degrees C for solvent evaporation. They were individually light-cured for 80 s at 500 mW/cm(2) and randomly divided into three groups: 24 h of water storage; 3 months of water storage; 3 months of dry storage. The specimens were tested in tension at 0.5 mm/min using the microtensile method and data were analyzed by two-way ANOVA and SNK tests for each material. Results. Water storage for 3 months did not cause significant changes in the UTS of any of the adhesives (p-value). Values for water storage ranged from 25.9 MPa for Single Bond at 24 h to 32.7 MPa for Prime & Bond NT after 3 months. Dry storage for 3 months yielded significantly higher UTS for most adhesives, which ranged from approximately 20% for Opti Bond to 160% higher values for Single Bond compared to their 3 months wet storage values. Conclusion. The effects of storage condition and time on the UTS of adhesives were material-dependent. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Stability of wet versus dry bonding with different solvent-based adhesives

Objective. To evaluate the effects of surface moisture (wet or dry) and storage (24h or 3 months) on the microtensile bond strength (BS) of resin/dentin bonds mediated by two water/ethanol based adhesives Single Bond, 3M-ESPE, (SB) and Opti Bond Solo Plus, Kerr, (OB), and two acetone-based adhesives, One Step, Bisco, (OS) and Prime&Bond NT, Caulk/Dentsply, (PB). Materials and methods. Flat dentin surfaces were polished with 600-grit SiC paper, etched with 35% phosphoric acid for 15 s and rinsed for 20 s. Half the surface was maintained moist and the other half was air-dried for 30 s. Each adhesive was applied simultaneously to both halves, left undisturbed for 30 s and light-cured. Four-mm resin build-ups were constructed incrementally. After storage in water at 37 degrees C for 24h, slabs were produced by transversal sectioning and trimmed to an hourglass shape (0.8 mm 2). Half of the specimens were tested in tension at 0.6 mm/min immediately after trimming and the other half after 3 months of water storage. Data were analyzed by two-way ANOVA and SNK for each material. Results. Both moisture and storage affected BS to dentin, and was material- dependent. Dry, bonding affected mostly the acetone-based adhesives. Larger reductions in bond strength were associated with dry bonding after 3 months of water storage. Significance. Wet bonding resulted in more stable bonds over 3 months of water storage for most of the materials tested. (C) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.