Surface modification and crystallization of the BaO-B2O3-SiO2 glassy system using CO2 laser irradiation

The surface modification and crystallization process of BaO-B2O3-SiO2 glass compositions when exposed to CO2 laser irradiation was evaluated as a function of the laser power, irradiation time and surface condition. The glass surface was modified by the application of laser power exceeding 0.40 W and an irradiation time of more than 300 s. Micro-Raman and X-ray diffraction measurements revealed at high laser power the formation of beta-BaB2O4 (beta-BBO) crystalline phase. The crystallization of the irradiated region was enhanced when beta-BBO micrometer sized particles were dispersed on the surface of the glass sample. The intensity of the second harmonic generation observed in the crystallized region was found to depend mainly on the condition of the glassy surface prior to glass irradiation. (C) 2007 Elsevier B.V. All rights reserved.

Thermal and structural investigation of Er:YAl(3)(BO(3))(4) nanocrystalline powders

Pure Er:YAB (Er:YAl(3)(BO(3))(4)) nanometer-sized crystalline powder was produced from low cost chemical route, the polymeric precursor method. The initial homogeneous solutions were heat treated from 200 to 700A degrees C under oxygen atmosphere and the unique crystalline phase was synthesized at around 1150A degrees C. The thermal treatments and the initial stoichiometry play a very important role on the Er:YAB preparation. The thermal events of amorphous precursor resins and the crystallization process up to phase formation were investigated.

Synthesis and characterization of a new mebendazole salt: Mebendazole hydrochloride

Mebendazole hydrochloride [(5-benzoyl-1H-benzimidazole-2-yl)-carbamic acid methyl ester hydrochloride, MBZ.HCl], a new stable salt of mebendazole (MBZ), has been synthesized and characterized. It can easily be obtained from recrystallization of forms A, B, or C of MBZ in diverse solvents with the addition of hydrochloric acid solution. Crystallographic data reveals that the particular conformation adopted by the carbamic group contributes to the stability of the network. The crystal packing is stabilized by the presence of three N-H...Cl intermolecular interactions that form chains along the b axis. The XRD analyses of the three crystalline habits found in the crystallization process (square-based pyramids, pseudohexagonal plates, and prismatic) show equivalent diffraction patterns. The vibrational behavior is consistent with crystal structure. The most important functional groups show shifts to lower or higher frequencies in relation to the MBZ polymorphs. The thermal study on MBZ center dot HCI indicates that the compound is stable up to 160 degrees C approximately. Decomposition occurs in four steps. In the first step the HCl group is eliminated, and after that the remaining MBZ polymorph A decomposes in three steps, as happens with polymorphs B and C. (C) 2007 Wiley-Liss, Inc. and the American Pharmacists Association J Pharm Sci 97:542-552, 2008.

Elaboration and optimization of (Y,Er)Al(3)(BO(3))(4) glassy planar waveguides through the sol-gel process

In this work, a sol-gel route was used to prepare Y(0.9)Er(0.1)Al(3)(BO(3))(4) glassy thin films by spin-coating technique looking for the preparation and optimization of planar waveguides for integrated optics. The films were deposited on silica and silicon substrates using stable sols synthesized by the sol-gel process. Deposits with thicknesses ranging between 520 and 720 nm were prepared by a multi-layer process involving heat treatments at different temperatures from glass transition to the film crystallization and using heating rates of 2 degrees C/min. The structural characterization of the layers was performed by using grazing incidence X-ray diffraction and Raman spectroscopy as a function of the heat treatment. Microstructural evolution in terms of annealing temperatures was followed by high resolution scanning electron microscopy and atomic force microscopy. Optical transmission spectra were used to determine the refractive index and the film thicknesses through the envelope method. The optical and guiding properties of the films were studied by m-line spectroscopy. The best films were monomode with 620 nm thickness and a refractive index around 1.664 at 980 nm wavelength. They showed good waveguiding properties with high light-coupling efficiency and low propagation loss at 632.8 and 1550 nm of about 0.88 dB/cm. (C) 2009 Elsevier B.V. All rights reserved.

Is the electrochemically-induced crystallization in lead oxifluoroborate glasses indeed an electrode- or/and an electric field-promoted phenomenon?

While evidence of ion reduction at the cathode has been given, proof of anode activity, in order to account completely for the redox-type electrochemical mechanism so far postulated to originate the electric field-induced non-spontaneous crystallization observed in glasses, is still lacking. This study demonstrates that direct contact of both cathode and anode electrodes with the material is mandatory to promote crystal nucleation. The electrochemical process of concern is established here to involve a solid-state process, electrolytic in nature. (C) 2008 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.