High Solids Content, Soap-Free, Film-Forming Latexes Stabilized by Laponite Clay Platelets

High solids content film-forming poly[styrene-co-(n-butyl acrylate)] [poly(Sty-co-BuA)] latexes armored with Laponite clay platelets have been synthesized by soap-free emulsion copolymerization of styrene and n-butyl acrylate. The polymerizations were performed in batch in the presence of Laponite and a methyl ether acrylateterminated poly(ethylene glycol) macromonomer in order to promote polymer/clay association. The overall polymerization kinetics showed a pronounced effect of clay on nucleation and stabilization of the latex particles. Cryo-transmission electron microscopy observation confirmed the armored morphology and indicated that the majority of Laponite platelets were located at the particle surface. The resulting nanostructured films displayed enhanced mechanical properties.

Influence of Granulometry and Organic Treatment of a Brazilian Montmorillonite on the Properties of Poly(styrene-co-n-butyl acrylate)/Layered Silicate Nanocomposites Prepared by Miniemulsion Polymerization

The influence of granulometry and organic treatment of a Brazilian montmorillonite (MMT) clay on the synthesis and properties of poly(styrene-co-n-butyl acrylate)/layered silicate nanocomposites was studied. Hybrid latexes of poly(styrene-co-butyl acrylate)/MMT were synthesized via miniemulsion polymerization using either sodium or organically modified MMT. Five clay granulometries ranging from clay particles smaller than 75 mu m to colloidal size were selected. The size of the clay particles was evaluated by Specific surface area measurements (BET). Cetyl trimethyl ammonium chloride was used as an organic modifier to enhance the clay compatibility with the monomer phase before polymerization and to improve the clav distribution and dispersion within the polymeric matrix after polymerization. The sodium and organically modified natural clays as well as the composites were characterized by X-ray diffraction analysis. The latexes were characterized by dynamic light scattering. The mechanical, thermal, and rheological properties of the composites obtained were characterized by dynamical-mechanical analysis, thermogravimetry, and small amplitude oscillatory, shear tests, respectively. The results showed that smaller the size of the organically modified MMT, the higher the degree of exfoliation of nanoplatelets. Hybrid latexes in presence of Na-MMT resulted in materials with intercalated structures. (C) 2009 Wiley, Periodicals, Inc. J Appl Polym Sci 112: 1949-1958, 2009

Preparation and characterization of colloidal Ni(OH)(2)/bentonite composites

A conductive and electrochemically active composite material has been prepared by the combination of bentonite and nickel hydroxide precursor sol. This material exhibits the characteristic intercalation properties of the clay component and the electrochemical and optical properties of nickel hydroxide. The clay particles seem to induce the aggregation of nickel hydroxide, leading to the formation of a layer of alpha-Ni(OH)(2) exhibiting needle like morphology. The composite forms stable films and has been conveniently used for the preparation of modified electrodes exhibiting intercalation and electrochemical properties, thus providing an interesting material for the development of amperometric sensors. (C) 2008 Elsevier Ltd. All rights reserved.

Nanostructured thin films obtained by electrodeposition over a colloidal crystal template: applications in electrochemical devices

Colloidal particles have been used to template the electrosynthesis of several materials, such as semiconductors, metals and alloys. The method allows good control over the thickness of the resulting material by choosing the appropriate charge applied to the system, and it is able to produce high density deposited materials without shrinkage. These materials are a true model of the template structure and, due to the high surface areas obtained, are very promising for use in electrochemical applications. In the present work, the assembly of monodisperse polystyrene templates was conduced over gold, platinum and glassy carbon substrates in order to show the electrodeposition of an oxide, a conducting polymer and a hybrid inorganic-organic material with applications in the supercapacitor and sensor fields. The performances of the resulting nanostructured films have been compared with the analogue bulk material and the results achieved are depicted in this paper.

Mechanism of point-defect diffusion in a two-dimensional colloidal crystal

The dynamics and mechanism of migration of a vacancy point defect in a two-dimensional (2D) colloidal crystal are studied using numerical simulations. We find that the migration of a vacancy is always realized by topology switching between its different configurations. From the temperature dependence of the topology switch frequencies, we obtain the activation energies for possible topology transitions associated with the vacancy diffusion in the 2D crystal. (C) 2011 American Institute of Physics. [doi:10.1063/1.3615287]

Properties of Y-TZP/Al(2)O(3) ceramic nanocomposites obtained by high-energy ball milling

In this work, the synthesis of Y(2)O(3) stabilized tetragonal zirconia polycrystals (Y-TZP)-alumina (Al(2)O(3)) powder mixture was performed by high-energy ball milling and the sintering behavior of this composite was investigated. In order to understand the phase transformations occurring during ball milling, samples were collected after different milling times, from 1 to 60 h. The milled powders were compacted by cold uniaxial pressing and sintered at 1400 and 1600 degrees C. Both powders and sintered samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometry analysis (EDS) and mechanical properties. Fully dense samples were obtained after sintering at 1600 degrees C, while the samples sintered at 1400 degrees C presented a full density for powder mixtures milled for 30 and 60 h. Fracture toughness and Vickers hardnessvalues of the Y-T-ZP/Al(2)O(3) nanocomposite were improved due to dispersed Al(2)O(3) grains and reduced ZrO(2) grain size. Samples sintered at 1400 degrees C, based on powders milled for 60 h, presented high K(IC) and hardness values near to 8.0 Mpan(1/2) and 15 GPa, respectively (C) 2008 Elsevier B.V. All rights reserved

Influence of the Type of Quaternary Ammonium Salt Used in the Organic Treatment of Montmorillonite on the Properties of Poly(Styrene-co-Butyl Acrylate)/Layered Silicate Nanocomposites Prepared by In Situ Miniemulsion Polymerization

Hybrid latices of poly(styrene-co-butyl acrylate) were synthesized via in situ miniemulsion polymerization in the presence of 3 and 6 wt % organically modified montmorillonite (OMMT). Three different ammonium salts: cetyl trimethyl ammonium chloride (CTAC), alkyl dimethyl benzyl ammonium chloride (Dodigen), and distearyl dimethyl ammonium chloride (Praepagen), were investigated as organic modifiers. Increased affinity for organic liquids was observed after organic modification of the MMT. Stable hybrid latices were obtained even though miniemulsion stability was disturbed to some extent by the presence of the OMMTs during the synthesis. Highly intercalated and exfoliated polymer-MMT nanocomposites films were produced with good MMT dispersion throughout the polymeric matrix. Materials containing MMT modified with the 16 carbons alkyl chain salt (CTAC) resulted in the largest increments of storage modulus, indicating that single chain quaternary salts provide higher increments on mechanical properties. Films presenting exfoliated structure resulted in the largest increments in the onset temperature of decomposition. For the range of OMMT loading studied, the nanocomposite structure influenced more significantly the thermal stability properties of the hybrid material than did the OMMT loading. The film containing 3 wt % MMT modified with the two 18 carbons alkyl chains salt (Praepagen) provided the highest increment of onset temperature of decomposition. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 119: 3658-3669, 2011

Quantification of Clay Dispersion in Nanocomposites of Styrenic Polymers

Polymer-clay nanocomposites are materials with many interesting structures, properties, and potential applications. Microstructural evaluation of a nanocomposite is not an easy task, as clay may form hierarchical structures which may look different when observed at various magnifications under a microscope, and also as the concepts of ""intercalation"" and ""exfoliation"" are not self-sufficient to describe its morphology. In this work polymer-clay nanocomposites of polystyrene and two styrene-containing block copolymers (styrene-butadiene-styrene and styrene-ethylene/butylene-styrene) were prepared using three different techniques. Clay dispersion was evaluated by a recently developed microscopy image analysis procedure, combining the analysis of optical and transmission electron micrographs, and the characterization was complemented by X-ray diffraction and rheological measurements. The results showed better clay dispersion for both block copolymers nanocomposites, mainly due to their molecular architectures. Moreover, the techniques which showed the best results involved mixing the materials in a solvent medium. POLYM. ENG. SCI., 50:257-267, 2010. (C) 2009 Society of Plastics Engineers

Colloidal Processing of Glass-Ceramics for Laminated Object Manufacturing

Green tapes of Li(2)O-ZrO(2)-SiO(2)-Al(2)O(3) (LZSA) parent glass were produced by aqueous tape casting as the starting material for the laminated object manufacturing (LOM) process. The rheological behavior of the powder suspensions in aqueous media, as well as the mechanical properties of the cast tapes, was evaluated. According to xi potential measurements, the LZSA glass powder particles showed acid surface characteristics and an IEP of around 4 when in aqueous media. The critical volume fraction of solids was about 72 wt% (27 vol%), which hindered the processability of more concentrated slurries. The glass particles also showed an anisometric profile, which contributed to an increase in the interactions between particles during flow. Therefore, the suspensions could not be processed at high solids loadings. Aqueous-based glass suspensions were also characterized by shear thickening after the addition of dispersants. Three slurry compositions were formulated, suitable green tapes were cast, and tapes were successfully laminated by LOM to a gear wheel geometry. A higher tensile strength of the green tapes corresponded to a higher tensile strength of the laminates. Thermal treatment was then applied to the laminates: pyrolysis at 525 degrees C, sintering at 700 degrees C for 1 h, and crystallization at 850 degrees C for 30 min. A 20% volumetric shrinkage was observed, but no surface flaws or inhomogeneous areas were detected. The sintered part maintained the curved edges and internal profile after heat treatment.

Photooxidative behavior of polystyrene-montmorillonite nanocomposites

The weathering behavior of polystyrene and polystyrene-montmorillonite composites containing 2.5, 5.0, and 7.5 wt% of montmorillonite (MMT) was investigated. Samples were exposed to UV radiation for periods of up to similar to 12 weeks and their molecular weight, chemical changes, and mechanical properties were monitored as a function of time. The addition of MMT was shown to improve the photostability of all composites investigated, probably because of a screen effect against UV radiation and barrier effect against diffusion of oxygen promoted by the silicate layers of MMT. Scanning electron microscopy of fracture surfaces of degraded samples showed that there is a degraded layer near the surface that provided a recovery of tensile strength of the samples.

Linear viscoelasticity of styrenic block copolymers-clay nanocomposites

In this work, the rheological behavior of block copolymers with different morphologies (lamellar, cylindrical, spherical, and disordered) and their clay-containing nanocomposites was studied using small amplitude oscillatory shear. The copolymers studied were one asymmetric starblock styrene-butadiene-styrene copolymer and four styrene-ethylene/butylenes-styrene copolymers with different molecular architectures, one of them being modified with maleic anhydride. The nanocomposites of those copolymers were prepared by adding organophilic clay using three different preparation techniques: melt mixing, solution casting, and a hybrid melt mixing-solution technique. The nanocomposites were characterized by X-ray diffraction and transmission electron microscopy, and their viscoelastic properties were evaluated and compared to the ones of the pure copolymers. The influence of copolymer morphology and presence of clay on the storage modulus (G`) curves was studied by the evaluation of the changes in the low frequency slope of log G` x log omega (omega: frequency) curves upon variation of temperature and clay addition. This slope may be related to the degree of liquid- or solid-like behavior of a material. It was observed that at temperatures corresponding to the ordered state, the rheological behavior of the nanocomposites depended mainly on the viscoelasticity of each type of ordered phase and the variation of the slope due to the addition of clay was small. For temperatures corresponding to the disordered state, however, the rheological behavior of the copolymer nanocomposites was dictated mostly by the degree of clay dispersion: When the clay was well dispersed, a strong solid-like behavior corresponding to large G` slope variations was observed.

Morphology of cobalt ferrite nanoparticle-polyelectrolyte multilayered nanocomposites

Novel magnetic nanocomposite films with controlled morphology were produced via the electrostatic layer-by-layer assembly of cationic CoFe(2)O(4) nanoparticles and anionic poly(3,4-ethylenedioxy thiophene)/poly(styrene sulfonic acid) (PEDOT:PSS) complex. The electrostatic interaction between nanoparticle and the polyelectrolyte complex ensured a stepwise growth of the nanocomposite film with virtually identical amounts of materials being adsorbed at each deposition cycle as observed by UV-vis spectroscopy. AFM images acquired under the tapping mode revealed a globular morphology with dense and continuous layers of nanoparticles with voids being filled with polymeric material. (C) 2010 Elsevier B.V. All rights reserved.

Montmorillonite/carbon nanocomposites prepared from sucrose for catalytic applications

Sucrose was used to prepare montmorillonite/carbon nanocomposites by calcination in a reduced atmosphere. The aim was to investigate the changes derived from varying the clay and sucrose content in the resulting material and to change the adsorption properties to evaluate its potential to be used in catalytic applications. X-ray diffraction patterns revealed the formation of an intercalated nanostructure composed of carbon-filled clay mineral layers, which was confirmed by the Fourier transform infrared spectra and thermogravimetry curves. Differences in composition and texture surface were detected by scanning electron microscopy images and were supported by viscosity measurements. These measurements were helpful in understanding why the sample prepared with the highest sucrose content presented the lowest gasoline and methylene blue adsorption results and why the highest adsorption properties were attributed to the sample with the highest clay content. Moreover, BET and BJH studies allowed understanding oleic acid catalytic conversion. Finally, a water flux simulation test was performed to determine the mechanical resistance in comparison to an activated carbon. It was found that the nanocomposites were more resistant, supporting their use in catalytic applications for a longer period of time. (C) 2011 Elsevier B.V. All rights reserved.

THE ROLE OF COLLOIDAL SILICON DIOXIDE IN THE ENHANCEMENT OF THE DRYING OF HERBAL PREPARATIONS IN SUSPENDED STATE

Recently, some research groups have been developing studies aiming to apply spouted beds of inert particles for production of dried herbal extracts. However, mainly due to their complex composition, several problems arise during the spouted bed drying of herbal extracts such as bed instability, product accumulation, particle agglomeration, and bed collapse. The addition of drying carriers, like colloidal silicon dioxide, to the extractive solution can minimize these unwanted effects. The aim of this work was to study the influence of the addition of colloidal silicon dioxide on enhancement of the performance of the drying of hydroalcoholic extract of Bauhinia forficata Link on a spouted bed of inert particles. The physical properties of the herbal extract and of its mixture with colloidal silicon dioxide at several concentrations (20% to 80% related to solids content) were quantified by determination of the surface tension, rheological properties, density, pH, and contact angles with the inert surfaces. Drying performance was evaluated through determination of the elutriation ratio, product recovery ratio, and product accumulation. The product was characterized through determination of the thermal degradation of bioactive compounds and product moisture content. The results indicated that the rheological properties of the extracts and their preparations, the contact angle with inert material, and the work of adhesion play important roles in the spouted bed drying of herbal extracts. Higher concentration of the drying carrier significantly improved the spouted bed drying performance.

Visible and near-infrared luminescent Eu(3+) or Er(3+) doped laponite-derived xerogels and thick films: Structural and spectroscopic properties

Laponite-derived materials represent promising materials for optical applications. In this work, Eu(3+)- or Er(3+)-doped laponite xerogels and films were prepared from colloidal dispersion. Homogeneous, crack-free and transparent single layers were deposited on soda-lime substrates with a thickness of 10 mu m. Structural and spectroscopic properties were analyzed by thermal analyses, X-ray diffractometry, transmission electron microscopy, infrared spectroscopy, and luminescence spectroscopy. The addition of a rare earth ion to the laponite does not promote any changes in thermal stability or phase transition. Laponite clay was identified after annealing up to 500 degrees C, with a decrease in basal spacing when the annealing temperature is changed from 100 degrees C to 500 degrees C. Enstatite polymorphs and amorphous silicate phases were observed after heat treatment at 700 degrees C and 900 degrees C. Stationary and time-dependent luminescence spectra in the visible region for Eu(3+), and (5)D(0) lifetime are discussed in terms of thermal treatment and structural evolution. In the layered host, the Eu(3+) ions are distributed in many different local environments. However, Eu(3+) ions were found to occupy at least two symmetry sites, and the ions are preferentially incorporated into the crystalline enstatite for the materials annealed at 700 degrees C and 900 degrees C. A (5)D(0) lifetime of 1.3 ms and 3.1 ms was obtained for Eu(3+) ions in an amorphous silicate and crystalline MgSiO(3) local environment, respectively. Strong Er(3+) emission at the 1550 nm region was observed for the materials annealed at 900 degrees C, with a bandwidth of 44 nm. (C) 2008 Elsevier B.V. All rights reserved.