Comparative analysis of the fit of 3-unit implant-supported frameworks cast in nickel-chromium and cobalt-chromium alloys and commercially pure titanium after casting, laser welding, and simulated porcelain firings

This study compared the vertical misfit of 3-unit implant-supported nickel-chromium (Ni-Cr) and cobalt-chromium (Co-Cr) alloy and commercially pure titanium (cpTi) frameworks after casting as 1 piece, after sectioning and laser welding, and after simulated porcelain firings. The results on the tightened side showed no statistically significant differences. On the opposite side, statistically significant differences were found for Co-Cr alloy (118.64 mu m [SD: 91.48] to 39.90 mu m [SD: 27.13]) and cpTi (118.56 mu m [51.35] to 27.87 mu m [12.71]) when comparing 1-piece to laser-welded frameworks. With both sides tightened, only Co-Cr alloy showed statistically significant differences after laser welding. Ni-Cr alloy showed the lowest misfit values, though the differences were not statistically significantly different. Simulated porcelain firings revealed no significant differences.

Effects of Cobalt Chloride in Junctional Epithelium and Reduced Enamel Epithelium of the Rat Maxillary First Molar

Cobalt is one of the main components of cast metal alloys broadly used in dentistry. It is the constituent of 45 to 70% of numerous prosthetic works. There are evidences that metal elements cause systemic and local toxicity. The purpose of the present study was to evaluate the effects of cobalt on the junctional epithelium and reduced enamel epithelium of the first superior molar in rats, during lactation. To do this, 1-day old rats were used, whose mothers received 300mg of cobalt chloride per liter of distilled water in the drinker, during lactation. After 21 days, the rat pups were killed with an anesthetic overdose. The heads were separated, fixed in ""alfac"", decalcified and embedded in paraffin. Frontal sections stained with hematoxylin and eosin were employed. Karyometric methods allowed to estimate the following parameters: biggest, smallest and mean diameters, D/d ratio, perimeter, area, volume, volume/area ratio, eccentricity, form coefficient and contour index. Stereologic methods allow to evaluate: cytoplasm/nucleus ratio, cell and cytoplasm volume, cell number density, external surface/basal membrane ratio, thickness of the epithelial layers and surface density. All the collected data were subjected to statistic analysis by the non-parametric Wilcoxon-Mann-Whitney test. The nuclei of the studied tissues showed smaller values after karyometry for: diameters; perimeter, area, volume and volume/area ratio. Stereologically, it was observed, in the junctional epithelium and in the reduced enamel epithelium, smaller cells with scarce cytoplasm, reflected in the greater number of cells per mm3 of tissue. In this study, cobalt caused epithelial atrophy, indicating a direct action on the junctional and enamel epithelium.

Cobalt-related impurity centers in diamond: electronic properties and hyperfine parameters

Cobalt-related impurity centers in diamond have been studied using first principles calculations. We computed the symmetry, formation and transition energies, and hyperfine parameters of cobalt impurities in isolated configurations and in complexes involving vacancies and nitrogen atoms. We found that the Co impurity in a divacant site is energetically favorable and segregates nitrogen atoms in its neighborhood. Our results are discussed in the context of the recently observed Co-related electrically active centers in synthetic diamond.

Synthesis and Characterization of Homoleptic and Heteroleptic Cobalt, Nickel, Copper, Zinc and Cadmium Compounds with the 2-(Tosylamino)-N-[2-(tosylamino)benzylidene]aniline Ligand

The electrochemical oxidation of anodic metal (cobalt, nickel, copper, zinc and cadmium) in an acetonitrile solution of the Schiff-base ligand 2-(tosylamino)-N-[2-(tosylamino)-benzylidene] aniline (H(2)L) afforded the homoleptic compounds [ML]. The addition of 1,1-diphenylphosphanylmethane (dppm), 2,2`-bipyridine (bipy) or 1,10-phenanthroline (phen) to the electrolytic phase gave the heteroleptic complexes [NiL(dppm)], [ML(bipy)] and [ML(phen)]. The crystal structures of H(2)L (1), [NiL] (2), [CuL] (3), [NiL(dppm)] (4), [CoL(phen)] (5), [CuL(bipy)] (6) and [Zn(Lphen)] (7) were determined by X-ray diffraction. The homoleptic compounds [NiL] and [CuL] are mononuclear with a distorted square planar [MN(3)O] geometry with the Schiff base acting as a dianionic (N(amide)N(amide)N(imine)O(tosyl)) tetradentate ligand. Both compounds exhibit an unusual pi-pi stacking interaction be-tween a six-membered chelate ring containing the metal and a phenylic ring of the ligand. In the heteroleptic complex [NiL(dppm)], the nickel atom is in a distorted tetrahedral [NiN(3)P] environment defined by the imine, two amide nitrogen atoms of the L(2-) dianionic tridentate ligand and one of the phosphorus atoms of the dppm molecule. In the other heteroleptic complexes, [CoL(phen)], [CuL(bipy)] and [ZnL(phen)], the metal atom is in a five-coordinate environment defined by the imine, two amide nitrogen atoms of the dianionic tridentate ligand and the two bipyridine or phenanthroline nitrogen atoms. The compounds were characterized by microanalysis, IR and UV/Vis (Co, Ni and Cu complexes) spectroscopy, FAB mass spectrometry and (1)H NMR ([NiL] and Zn and Cd complexes) and EPR spectroscopy (Cu complexes).

Identification of species formed after pyridine adsorption on iron, cobalt, nickel and silver electrodes by SERS and theoretical calculations

The adsorption of pyridine (py) on Fe, Co, Ni and Ag electrodes was studied using surface-enhanced Raman scattering (SERS) to gain insight into the nature of the adsorbed species. The wavenumber values and relative intensities of the SERS bands were compared to the normal Raman spectrum of the chemically prepared transition metal complexes. Raman spectra of model clusters M(4)(py) (four metal atoms bonded to one py moiety) and M(4)(alpha-pyridil) where M = Ag, Fe, Co or Ni were calculated by density functional theory (DFT) and used to interpret the experimental SERS results. The similarity of the calculated M(4)(py) spectra with the experimental SERS spectra confirm the molecular adsorption of py on the surface of the metallic electrodes. All these results exclude the formation of adsorbed alpha-pyridil species, as suggested previously. Copyright (C) 2009 John Wiley & Sons, Ltd.

Electrocatalytic oxidation of urea by nanostructured nickel/cobalt hydroxide electrodes

The present paper describes the catalytic oxidation of urea performed by nickel hydroxide and nickel/cobalt hydroxide modified electrodes by using both electrodeposited films and nanoparticles. The incorporation of Co foreign atoms leads to a slight increase in sensitivity besides the shift in redox process, avoiding the oxygen reaction. Nanostructured Ni80Co20(OH)(2) was synthesized by sonochemical route producing 5 nm diameter particles characterized by high-resolution transmission electron microscopy (HRTEM) being immobilized onto electrode by using the electrostatic Layer-by-layer technique, yielding attractive modified electrodes for sensor development. (C) 2007 Elsevier Ltd. All rights reserved.

Selective Allylic oxidation of Cyclohexene by a Magnetically Recoverable Cobalt Oxide Catalyst

In this work, we prepared a new magnetically recoverable CoO catalyst through the deposition of the catalytic active metal nanoparticles of 2-3 nm on silica-coated magnetite nanoparticles to facilitate the solid separation from liquid media. The catalyst was fully characterized and presented interesting properties in the oxidation of cyclohexene, as for example, selectivity to the allylic oxidation product. It was also observed that CoO is the most active species when compared to Co(2+), Co(3)O(4) and Fe(3)O(4) in the catalytic conditions studied.

Quantification of N-acetylcysteine in pharmaceuticals using cobalt phthalocyanine modified graphite electrodes

Flow injection analysis (FIA) with amperometric detection was employed for the quantification of N-acetylcysteine (NAC) in pharmaceutical formulations, utilizing an ordinary pyrolytic graphite (OPG) electrode modified with cobalt phthalocyanine (CoPc). Cyclic voltammetry was used in preliminary studies to establish the best conditions for NAC analysis. In FIA-amperometric experiments the OPG-CoPc electrode exhibited sharp and reproducible current peaks over a wide linear working range (5.0 x 10(-5)-1.0 x 10(-3) mol L(-1)) in 0.1 mol L(-1) NaOH solution. High sensitivity (130 mA mol(-1) cm(2)) and a low detection limit (9.0 x 10(-7) mol L(-1)) were achieved using the sensor. The repeatability (R.S.D.%) for 13 successive flow injections of a solution containing 5.0 x 10(-4) mol L(-1) NAC was 1.1%. The new procedure was applied in analyses of commercial pharmaceutical products and the results were in excellent agreement with those obtained using the official titrimetric method. The proposed amperometric method is highly suitable for quality control analyses of NAC in pharmaceuticals since it is rapid, precise and requires much less work than the recommended titrimetric method. (C) 2010 Elsevier B.V. All rights reserved.

Ethanol steam reforming for production of hydrogen on magnesium aluminate-supported cobalt catalysts promoted by noble metals

The performance of noble metal (Pt, Ru, Ir)-promoted Co/MgAl(2)O(4) catalysts for the steam reforming of ethanol was investigated. The catalysts were characterized by energy-dispersive X-ray spectroscopy, Xray diffraction, UV-vis diffuse reflectance spectroscopy, temperature-programmed reduction, temperature-programmed oxidation and X-ray absorption near edge structure (XANES). The results showed that the formation of inactive cobalt aluminate was suppressed by the presence of a MgAl(2)O(4) spinel phase. The effects of the noble metals included a marked lowering of the reduction temperatures of the cobalt surface species interacting with the support. It was seen that the addition of noble metal stabilized the Co sites in the reduced state throughout the reaction. Catalytic performance was enhanced in the promoted catalysts, particularly CoRu/MgAl(2)O(4), which showed the highest selectivity for H(2) production. (C) 2009 Elsevier B.V. All rights reserved.

Cobalt catalysts promoted with cerium and lanthanum applied to partial oxidation of methane reactions

Catalysts of Co/Mg/Al promoted with Ce and La were tested in the catalytic partial oxidation of methane (POM) reaction. The addition of promoters was made by anion-exchange. X-ray diffraction (XRD) confirmed the formation of hydrotalcite phase for precursors. The mixed oxides were characterized as a mixture of Co3O4, periclase (Co, Al)MgO and/or spinel structure (Mg, Co)Al2O4. In the catalytic POM reaction over the promoted catalysts, a reduction in the carbon formation rate was found. (c) 2008 Elsevier B.V. All rights reserved.

Electrocatalytic behavior of glassy carbon electrodes modified with multiwalled carbon nanotubes and cobalt phthalocyanine for selective analysis of dopamine in presence of ascorbic acid

This work describes the development, electrochemical characterization and utilization of a cobalt phthalocyanine modified carbon nanotube electrode for the quantitative determination of dopamine in 0.2 mol L-1 phosphate buffer contaminated with high concentration of ascorbic acid. The electrode surface was analyzed by cyclic voltammetry and electrochemical impedance spectroscopy which showed a modified surface presenting a charge transfer resistance of 500 Omega, against the 16.46 k Omega value found for the bare glassy carbon surface. A pseudo rate constant value of 5.4 x 10(-4) cm s(-1) for dopamine oxidation was calculated. Voltammetric experiments showed a shift of the peak potential of DA oxidation to less positive value at 390 mV as compared with that of a bare GC electrode at 570 mV. The electrochemical determination of dopamine, in presence of ascorbic acid in concentrations up to 0.1 mol L-1 by differential pulse voltarnmetry, yielded a detection limit as low as 2.56 x 10(-7) mol L-1.

Cobalt catalysts derived from hydrotalcite-type precursors applied to steam reforming of ethanol

Catalysts derived from Co/Mg/Al hydrotalcite-type precursors modified with La and Ce were characterized by XANES and tested in ethanol steam reforming. The reaction data showed that, with a molar ratio of water: ethanol = 3:1 in the feed, addition of Ce and La favored acetaldehyde production. Increasing the water content (water:ethanol = 5:1) decreased the acetaldehyde formation by favoring the adsorption of water molecules on these samples, enhancing the acetaldehyde conversion. (C) 2011 Elsevier B.V. All rights reserved.

Determination of epinephrine in urine using multi-walled carbon nanotube modified with cobalt phthalocyanine in a paraffin composite electrode

This paper describes the development, electrochemical characterization and utilization of a cobalt phthalocyanine (CoPc), modified multi-walled carbon nanotube (MWCNT), and paraffin composite electrode for the quantitative determination of epinephrine (EP) in human urine samples. The electrochemical profile of the proposed composite electrode was analyzed by differential pulse voltammetry (DPV) that showed a shift of the oxidation peak potential of EP at 175 mV to less positive value, compared with a paraffin/graphite composite electrode without CoPc. DPV experiments in PBS at pH 6.0 were performed to determine EP without any previous step of extraction, clean-up, and derivatization, in the range from 1.33 to 5.50 mu mol L(-1), with a detection limit of 15.6 nmol L(-1) (2.86) of EP in electrolyte prepared with purified water. The lifetime of the proposed sensors was at least over 1000 determinations with 1.7 and 3.1 repeatability and reproducibility relative standard deviations, respectively. Human urine samples without any purification step were successfully analyzed under the standard addition method using paraffin/MWCNT/CoPc composite electrode. (C) 2010 Elsevier B.V. All rights reserved.

Degradation of alachlor herbicide by gamma radiation from cobalt-60 in aqueous and alcohol solution

Alachlor has been widely used in agriculture all over the world. It is suggested that it may be a carcinogen and an environmental estrogen. The aim of this work was to verify the degradation the alachlor by gamma radiation. Gamma radiation from (60)Co was used to degrade the alachlor herbicide in water and methanol solution. The alachlor in water and alcohol solution in the concentration of 100 mgL(-1) was irradiated with doses of 0.25-50 kGy, at dose rate 5-6 and 2.7 kGyh(-1). High performance liquid chromatography was used as an analytical technique to determine the degradation rate of herbicide studied.

Correlation between vertical misfits and stresses transmitted to implants from metal frameworks

An inappropriate prosthetic fit could cause stress over the interface implant/bone. The objective of this study was to compare stresses transmitted to implants from frameworks cast using different materials and to investigate a possible correlation between vertical misfits and these stresses. Fifteen one-piece cast frameworks simulating bars for fixed prosthesis in a model with five implants were fabricated and arranged into three different groups according to the material used for casting: CP Ti (commercially pure titanium), Co-Cr (cobalt-chromium) or Ni-Cr-Ti (nickel-chromium-titanium) alloys. Each framework was installed over the metal model with all screws tightened to a 10 N cm torque and then, vertical misfits were measured using an optical microscope. The stresses transmitted to implants were measured using quantitative photoelastic analysis in values of maximum shear stress (T), when each framework was tightened to the photoelastic model to a 10 N cm standardized torque. Stress data were statistically analyzed using one-way ANOVA and Tukey`s test and correlation tests were performed using Pearson`s rank correlation (alpha = 0.05). Mean and standard deviation values of vertical misfit are presented for CP Ti (22.40 +/- 9.05 mu m), Co-Cr (66.41 +/- 35.47 mu m) and Ni-Cr-Ti (32.20 +/- 24.47 mu m). Stresses generated by Co-Cr alloy (tau = 7.70 +/- 2.16 kPa) were significantly higher than those generated by CP Ti (tau = 5.86 +/- 1.55 kPa, p = 0.018) and Ni-Cr-Ti alloy (tau =5.74 +/- 3.05 kPa, p = 0.011), which were similar (p = 0.982). Correlations between vertical misfits and stresses around the implants were not significant as for any evaluated materials. (C) 2011 Elsevier Ltd. All rights reserved.