Effects of calcining conditions on the microstructure of sugar cane waste ashes (SCWA): Influence in the pozzolanic activation

in this paper a study of calcining conditions on the microstructural features of sugar cane waste ash (SCWA) is carried out. For this purpose, some microparticles (< 90 mu m) of sugar cane straw ash and sugar cane bagasse ash of samples calcined at 800 degrees C and 1000 are studied by combining the bright field and the dark field images with the electron diffraction patterns in the transmission electron microscopy (TEM). It is appreciated that the morphology and texture of these microparticles change when silicon or calcium are present. Furthermore, it is observed that iron oxide (magnetite Fe(3)O(4)) is located in the calcium-rich particles. The microstructural information is correlated with the results of a kinetic-diffusive model that allows the computing of the kinetic parameters of the pozzolanic reaction (mainly the reaction rate constant). The results show that the sugar cane wastes ash calcined at 800 and 1000 degrees C have properties indicative of high pozzolanic activity. The X-ray diffraction patterns, the TEM images and the pozzolanic activity tests show the influence of different factors on the activation of these ashes. (c) 2008 Elsevier Ltd. All rights reserved.

Study of the pozzolanic reaction kinetics in sugar cane bagasse-clay ash/calcium hydroxide system: kinetic parameters and pozzolanic activity

This paper presents a study of the pozzolanic reaction kinetics between calcium hydroxide and a mixture of sugar cane bagasse with 20 and 30% of clay, burned at 800 and 1000 degrees C (SCBCA) by electrical conductivity measurements. A kinetic-diffusive model produced in previous studies by some of the authors was used. The model was fitted to the experimental data, which allowed the computation of the kinetic parameters of the pozzolanic reaction (reaction rate constant and free energy of activation) that rigorously characterised the pozzolanic activity of the materials. The results show that SCBCA demonstrated reactivity and good pozzolanic qualities in the range 800-1000 degrees C.

Fast or slow melting of the Marinoan snowball Earth? The cap dolostone record

The end of the Neoproterozoic era is punctuated by two global glacial events marked by the presence of glacial deposits overlaid by cap carbonates. Duration of glacial intervals is now consistently constrained to 3-12 million years but the duration of the post-glacial transition is more controversial due to the uncertainty in cap dolostone sedimentation rates. Indeed, the presence of several stratabound magnetic reversals in Brazilian cap dolostones recently questioned the short sedimentation duration (a few thousand years at most) that was initially suggested for these rocks. Here, we present new detailed magnetostratigraphic data of the Mirassol d`Oeste cap dolostones (Mato Grosso, Brazil) and ""bomb-spike"" calibrated AMS (14)C data of microbial mats from the Lagoa Vermelha (Rio de Janeiro, Brazil). We also compile sedimentary, isotopic and microbiological data from post-Marinoan outcrops and/or recent depositional analogues in order to discuss the deposition rate of Marinoan cap dolostones and to infer an estimation of the deglaciation duration in the snowball Earth aftermath. Taken together, the various data point to a sedimentation duration in the range of a few 10(5) years. (C) 2010 Elsevier B.V. All rights reserved.

Retention at room temperature of the tetragonal t ``-form in Sc(2)O(3)-doped ZrO(2) nanopowders

Synchrotron X-ray powder diffraction was applied to the study of the effect of crystallite size on the crystal structure of ZrO(2)-10 mol% Sc(2)O(3) nanopowders synthesized by a nitrate-lysine gel-combustion route Nanopowders with different average crystallite sizes were obtained by calcination at several temperatures, ranging from 650 to 1200 degrees C The metastable t""-form of the tetragonal phase, exhibiting a cubic unit cell and tetragonal P4(2)/nmc spatial symmetry, was retained at room temperature in fine nanocrystalline powders, completely avoiding the presence of the stable rhombohedral beta phase. Differently, this phase was identified in samples calcined at high temperatures and its content increased with increasing crystallite size The critical maximum crystallite size for the retention of the mestastable t""-form resulted of about 35 nm (C) 2009 Elsevier B.V All rights reserved

Photoluminescence behavior of Eu(3+) ion doped into gamma- and alpha-alumina systems prepared by combustion, ceramic and Pechini methods

Al(2)O(3):Eu(3+)(1%) samples were prepared by combustion, ceramic, and Pechini methods annealed from 400 to 1400 degrees C. XRD patterns indicate that samples heated up to 1000 degrees C present disordered character of activated alumina (gamma-Al(2)O(3)). However, alpha-Al(2)O(3) phase showed high crystallinity and thermostability at 1200-1400 degrees C. The sample characterizations were also carried out by means of infrared spectroscopy (IR), scanning electron microscopy (SEM) and specific surface areas analysis (BET method). Excitation spectra of Al(2)O(3):Eu(3+) samples present broaden bands attributed to defects of Al(2)O(3) matrices and to LMCT state of O -> Eu(3+), however, the narrow bands are assigned to (7)F(0) -> (5)D(J),(5)H(J) and (5)L(J) transitions of Eu(3+) ion. Emission spectra of samples calcined up to 1000 degrees C show broaden bands for (5)D(0) -> (7)F(J) transitions of Eu(3+) ion suggesting that the rare earth ion is in different symmetry sites showed by inhomogeneous line broadening of bands, confirming the predominance of the gamma-alumina phase. For all samples heated from 1200 to 1400 degrees C the spectra exhibit narrow (5)D(0) -> (7)F(J) transitions of Eu(3+) ion indicating the conversion of gamma to alpha-Al(2)O(3) phases, a high intensity narrow peak around 695 nm assigned to R lines of Cr(3+) ion is shown. Al(2)O(3):Eu(3+) heated up to 1100 degrees C presents an increase in the Omega(2) intensity parameter with the increase of temperatures enhancing the covalent character of metal-donor interaction. The disordered structural systems present the highest values of emission quantum efficiencies (eta). CIE coordinates of Al(2)O(3):Eu(3+) are also discussed. (C) 2007 Elsevier Inc. All rights reserved.

Influence of calcination temperature on the morphology and magnetic properties of Ni-Zn ferrite applied as an electromagnetic energy absorber

An evaluation was made of the influence of calcination temperatures on the structure, morphology and eletromagnetic properties of Ni-Zn ferrite powders. To this end, Ni(0.5)Zn(0.5)Fe(2)O(4) ferrite powders were prepared by combustion reaction and calcined at temperatures of 800, 1000 and 1200 degrees C/2 h. The resulting powders were characterized by XRD, SEM and reflectivity measurements in the frequency bands of 8-12 GHz. The results demonstrated that raising the calcination temperature increased the particle sizes of the powders of all the systems in question, improving the reflectivity of the materials. (C) 2008 Elsevier B.V. All rights reserved.

Oxide surface modification: Synthesis and characterization of zirconia-coated alumina

Four aluminas were used as Supports for impregnation with a zirconium oxide with the aim to achieve a coating, without phase separation, between Support and modifier. The Supports were impregnated with different concentrations Of zirconium aqueous resin, obtained through the polymeric precursor method. After impregnation the samples were calcined and then characterized by XRD, which led to identification of crystalline zirconia in different concentrations from each support used. Using a simple geometric model the maximum amount Of Surface modifier Oxide required for the complete coating of a support with a layer of unit cells was estimated. According to this estimate, only the support should be identified below the limit proposed and crystalline zirconium oxide Should be identified above this limit when a complete coating is reached. The results obtained From XRD agree with the estimated values and to confirm the coating, the samples were also characterized by EDS/STEM, HRTEM, XPS, and XAS. The results showed that the zirconium oxide oil the Surface of alumina Support reached the coating in the limit of 15 Zr nm(-2), without the formation of the ZrO(2) phase. (c) 2009 Elsevier Inc. All rights reserved.

Electrophoretic deposition of Ba0.77Ca0.23TiO3 nanopowders

Ba0.77Ca0.23TiO3 (BCT23) nanometric powders, synthesized by the modified Pechini method, were used as precursor to produce thick films (50-130 mu m) employing the electrophoretic deposition (EPD) technique. The BCT23 powder presented a single crystalline phase with an average particle size and a crystallite size of similar to 60 nm and similar to 20 nm, respectively, when calcined at 800 degrees C/2h. BCT23 thick films were deposited on platinum substrates starting from different suspensions prepared by dispersion of the powder into: isopropyl alcohol (IPA) or a mixture of acetylacetone (Acac) and ethanol (EtOH) (1:1, volumetric ratio). A milling process was used to deagglomerate the powders in order to increase the suspension stability and improving the deposition. Dense and crack free thick films with uniform microstructure were obtained after sintering at 1300 degrees C/2 h from Acac+EtOH solution. (C) 2007 Elsevier B.V. All rights reserved.

Menezesite, the first natural heteropolyniobate, from Cajati, Sao Paulo, Brazil: Description and crystal structure

Menezesite, ideally Ba2MgZr4(BaNb12O42)center dot 12H(2)O, occurs as a vug mineral in the contact zone between dolomite carbonatite and ""jacupirangite"" (=a pyroxenite) at the Jacupiranga mine, in Cajati county, Sao Paulo state, Brazil, associated with dolomite, calcite, magnetite, clinohumite, phlogopite, ancylite-(Ce), strontianite, pyrite, and tochilinite. This is also the type locality for quintinite-2H. The mineral forms rhombododecahedra up to I mm, isolated or in aggregates. Menezesite is transparent and displays a vitreous luster; it is reddish brown with a white streak. It is non-fluorescent. Mohs hardness is about 4. Calculated density derived from the empirical formula is 4.181 g/cm(3). It is isotropic, 1.93(1) (white light); n(calc) = 2.034. Menezesite exhibits weak anomalous birefringence. The empirical formula is (Ba1.47K0.53Ca0.3,Ce0.17Nd0.10Na0.06La0.02)(Sigma 2.66)(Mg0.94Mn0.23Fe0.23Al0.03)(Sigma 1.43)(Zr2.75Ti0.96Th0.29)(Sigma 4.00)[(Ba0.72Th0.26U0.02)(Sigma 1.00)(Nb9.23Ti2.29Ta0.36Si0.12)Sigma O-12.00(42)]center dot 12H(2)O. The mineral is cubic, space group 10 (204), a = 13.017(1) angstrom, V = 2206(1) angstrom(3), Z = 2. Menezesite is isostructural with the synthetic compound Mg-7[MgW12O42](OH)(4)center dot 8H(2)O. The mineral was named in honor of Luiz Alberto Dias Menezes Filho (born 1950), mining engineer, mineral collector and merchant. Both the description and the name were approved by the CNMMN-IMA (Nomenclature Proposal 2005-023). Menezesite is the first natural heteropolyniobate. Heteropolyanions have been employed in a range of applications that include virus-binding inorganic drugs (including the AIDs virus), homogeneous and heterogeneous catalysts, electro-optic and electrochromic materials, metal and protein binding, and as building blocks for nanostructuring of materials.

Mineralogy and trace-element geochemistry of the high-grade iron ores of the Aguas Claras Mine and comparison with the Capao Xavier and Tamandua iron ore deposits, Quadrilahero Ferrifero, Brazil

Several major iron deposits occur in the Quadrilatero Ferrifero (QF), southeastern region of Brazil, where metamorphosed and heterogeneously deformed banded iron formation (BIF) of the Caue Formation, regionally called itabirite, was transformed into high- (Fe >64%) and lowgrade (30%dolomite, sericite, chlorite, and apatite in the hard and soft ores, and Mn-oxides and ferrihydrite in the soft ore where they are concentrated within porous bands. Chemical analyses show that hard and soft ores consist almost entirely of Fe(2)O(3), with a higher amount of detrimental impurities, especially MnO, in the soft ore. Both hard and soft ores are depleted in trace elements. The high-grade ores at the Aguas Claras Mine have at least a dual origin, involving hypogene and supergene processes. The occurrence of the hard, massive high-grade ore within ""fresh"" dolomitic itabirite is evidence of its hypogene origin. Despite the contention about the origin of the dolomitic itabirite (if this rock is a carbonate-rich facies of the Caue Formation or a hematite-carbonate precursor of the soft high-grade ore), mineralogical and geochemical features of the soft high-grade ore indicate that it was formed by leaching of dolomite from the dolomitic itabirite by meteoric water. The comparison of the Aguas Claras, Capao Xavier and Tamandua orebodies shows that the original composition of the itabiritic protore plays a major role in the genesis of high- and low-grade soft ores in the QF. Under the same weathering and structural conditions, the dolomitic itabirite is the more favorable to form high-grade deposits than siliceous itabirite. Field relations at the Aguas Claras and Capao Xavier deposits suggest that it is not possible to form huge soft high-grade supergene deposits from siliceous itabirite, unless another control, such as impermeable barriers, had played an important role. The occurrence in the Tamandua Mine of a large, soft, high-grade orebody formed from siliceous itabirite and closely associated with hypogene hard ore suggests that large, soft, high-grade orebodies of the Quadrilatero Ferrifero, which occur within siliceous itabirite, have a hypogene contribution in their formation.

La(2-x)Ce(x)Cu(1-y)Zn(y)O(4) perovskites for high temperature water-gas shift reaction

The performance of La(2-x)Ce(x)Cu(1-y)Zn(y)O(4) perovskites as catalysts for the high temperature water-gas shift reaction (H T-W G S R) was investigated. The catalysts were characterized by EDS, XRD, BET surface area, TPR, and XANES. The results showed that all the perovskites exhibited the La(2)CuO(4) orthorhombic structure, so the Pechini method is suitable for the preparation of pure perovskite. However, the La(1.90)Ce(0.10)CuO(4) perovskite alone, when calcined at 350/700 degrees C, also showed a (La(0.935)Ce(0.065))(2)CuO(4) perovskite with tetragonal structure, which produced a surface area higher than the other perovskites. The perovskites that exhibited the best catalytic performance were those calcined at 350/700 degrees C and, among these, La(1.90)Ce(0.10)CuO(4) was outstanding, probably because of the high surface area associated with the presence of the (La(0.935)Ce(0.065))(2)CuO(4) perovskite with tetragonal structure and orthorhombic La(2)CuO(4) phase.