Effect of power densities and irradiation times on the degree of conversion and temperature increase of a microhybrid dental composite resin

The different parameters used for the photoactivation process provide changes in the degree of conversion (DC%) and temperature rise (TR) of the composite resins. Thus, the purpose of this study was to evaluate the DC (%) and TR of the microhybrid composite resin photoactivated by a new generation LED. For the KBr pellet technique, the composite resin was placed into a metallic mould (1-mm thickness and 4-mm diameter) and photoactivated as follows: continuous LED LCU with different power density values (50-1000 mW/cm(2)). The measurements for the DC (%) were made in a FTIR Spectrometer Bomen (model MB-102, Quebec-Canada). The spectroscopy (FTIR) spectra for both uncured and cured samples were analyzed using an accessory for the diffuse reflectance. The measurements were recorded in the absorbance operating under the following conditions: 32 scans, 4-cm(-1) resolution, and a 300 to 4000-cm(-1) wavelength. The percentage of unreacted carbon-carbon double bonds (% C=C) was determined from the ratio of the absorbance intensities of aliphatic C=C (peak at 1638 cm(-1)) against an internal standard before and after the curing of the specimen: aromatic C-C (peak at 1608 cm-1). For the TR, the samples were made in a metallic mould (2-mm thickness and 4-mm diameter) and photoactivated during 5, 10, and 20 s. The thermocouple was attached to the multimeter to allow the temperature readings. The DC (%) and TR were calculated by the standard technique and submitted to ANOVA and Tukey`s test (p < 0.05). The degree of conversion values varied from 35.0 (+/- 1.3) to 45.0 (+/- 2.4) for 5 s, 45.0 (+/- 1.3) to 55.0 (+/- 2.4) for 10 s, and 47.0 (+/- 1.3) to 52.0 (+/- 2.4) for 20 s. For the TR, the values ranged from 0.3 (+/- 0.01) to 5.4 (+/- 0.11)degrees C for 5 s, from 0.5 (+/- 0.02) to 9.3 (+/- 0.28)degrees C for 10 s, and from 1.0 (+/- 0.06) to 15.0 (+/- 0.95)degrees C for 20 s. The power densities and irradiation times showed a significant effect on the degree of conversion and temperature rise.

Electronic synergism in [RuCl(2)(PPh(3))(2)(amine)] complexes differing the reactivity for ROMP of norbornene and norbornadiene

The reactivity of the new complex [RuCl(2)(PPh(3))(2)(3,5-Me(2)piperidine)], complex 1, was investigated for ring opening metathesis polymerization (ROMP) of norbornene (NBE) and norbornadiene (NBD) in the presence of ethyl diazoacetate (EDA) in CHCl(3). The aim is to observe the combination of PPh(3) and an amine as ancillary ligands concerning the steric hindrance and the electronic perturbation in the properties of the N-bound site when replacing the amines. Thus, the results with 1 were compared to the results obtained when the amine is piperidine (complex 2). Reaction with 1 provides 70% yield of isolated polyNBE (M(n) =8.3 x 10(4) g/mol; PDI = 2.03), whereas 2 provides quantitative reaction (M(n) = 1.2 x 10(5) g/mol; PDI = 1.90) with [NBE]/[Ru] = 5000, [EDA]/[Ru] = 48 and 1.1 mu mol of Ru for 5 min at 25 degrees C. The resulting polymers showed c.a. 62% of trans-polyNBE, determined by (1)H NMR, and T(g) = 32 degrees C, determined by DSC and DMTA. For ROMP of NBD, 1 showed quantitative yield with PDI =2.62 when [NBD]/[Ru] = 5000 for 20 min at 25 degrees C, whereas the reaction with 2 reached 55% with PDI = 2.16 in the same conditions. It is concluded that the presence of the two methyl groups in the piperidine ring provides an increase in the induction period to produce the Ru-carbene species justifying better polyNBE results with 2, and a greater amine(sigma)-> Ru(pi)-> monomer synergism which contributed to the best activation of less tensioned olefin as NBD. (C) 2010 Elsevier B.V. All rights reserved.