The synthesis and study of the chemiluminescence parameters and thermal stability of 1,2-dioxetanes containing a spirofenchyl substituent are reported. Three fenchyl-substituted 1,2-dioxetanes were synthesized by photooxygenation of the corresponding alkenes, obtained by Barton-Kellogg olefination of the readily available (-)-fenchone. The fenchyl-substituted 1,2-dioxetanes showed thermal stabilities similar to those of the corresponding spiroadamantyl-substituted derivatives, although being slightly more labile with respect to unimolecular decomposition than the latter derivatives, which are widely utilized as labels in a great variety of chemiluminescent immunoassays. Fluoride induced decomposition of one triggerable fenchyl 1,2-dioxetane derivative showed kinetic parameters similar to those of the corresponding adamantyl-substituted derivative. The chemiluminescence quantum yields in the one percent range are also similar to that of other widely utilized chemiluminescence systems as the luminol reaction. These results indicate that fenchyl-substituted 1,2-dioxetanes can potentially be utilized as a cheaper alternative to substitute the corresponding spiroadamantyl derivatives in bioanalytical applications. (C) 2010 Elsevier B.V. All rights reserved.

Study of Water-Gas-Shift Reaction over La((1-y))Sr(y)Ni(x)Co((1-x))O(3) Perovskite as Precursors

The performance of La((1-y))Sr(y)Ni(x)Co((1-x))O(3) perovskites for the water gas shift reaction (WGSR) was investigated. The samples were prepared by the co- precipitation method and were performed by the BET method, XRD, TPR, and XPS. The catalytic tests were performed at 300 and 400 A degrees C and H(2)O(v)/CO = 2.3/1 (molar ratio). The sample with the highest surface area is La(0.70)Sr(0.30)NiO(3). The XRD results showed the formation of perovskite structure for all samples, and the La(0.70)Sr(0.30)NiO(3) sample also presented peaks corresponding to La(2)NiO(4) and NiO, indicating that the solubility limit of Sr in the perovskite lattice was surpassed. The replacement of Co by Ni favored the reduction of the species at lower temperatures, and the sample containing Sr presented the highest amount of reducible species, as identified by TPR results. All samples were active, the Sr containing perovskite appearing the most active due to the highest surface area, presence of the La(2)NiO(4) phase, and higher content of Cu in the surface, as detected by XPS. Among the samples containing Co, the most active one was that with x = 0.70 (60% of CO conversion).